SPHERICAL SILICON OXYCARBIDE POWDER AND MANUFACTURING METHOD THEREOF
The present invention relates to spherical silicon oxycarbide microparticles having an average particle diameter of 0.1-100 m and a sphericity of 0.95-1.0 and a method for preparing the same. The spherical silicon oxycarbide microparticles according to the present invention are obtained by the method comprising the steps of: hydrolyzing organo-trialkoxysilane in an aqueous acetic acid solution having a pH of 3-6; continuously adding an aqueous alkaline solution, such as aqueous ammonia having a pH of 6-12 to the resultant hydrolyzate to carry out condensation in an alkaline region, thereby providing spherical polysilsesquioxane particles having no melting point or softening point as spherical silicon oxycarbide precursors; and firing the precursors under inert atmosphere at a firing temperature of 600-1400C to obtain spherical silicon oxycarbide powder.
본 발명은 평균 입경(粒徑)이 0.1∼100 ㎛의 범위이며 또한 진구도(眞球度)가 0.95∼1.0인 구형(球形) 실리콘 옥시카바이드 미립자 및 그 제조 방법을 제공하는 것을 과제로 한다. 상기 과제를 해결하기 위하여, 본 발명은, 오르가노 트리알콕시실란을 pH 3∼6의 아세트산 수용액 중에서 가수분해한 후, 계속하여 상기 가수분해물을 pH 7∼12의 암모니아수 등의 알칼리성 수용액을 첨가하여, 알칼리성 영역에서 축합시킴으로써 생성된 구형 실리콘 옥시카바이드 전구체(前驅體)인, 융점이나 연화점을 가지지 않는 구형 폴리실세스퀴옥산 입상물(粒狀物)을, 불활성 분위기 하에서 600∼1400 ℃의 소성 온도에서 소성함으로써 얻어지는 구형 실리콘 옥시카바이드 분립체(粉粒體) 및 그 제조 방법을 제공한다.
SPHERICAL SILICON OXYCARBIDE POWDER AND MANUFACTURING METHOD THEREOF
The present invention relates to spherical silicon oxycarbide microparticles having an average particle diameter of 0.1-100 m and a sphericity of 0.95-1.0 and a method for preparing the same. The spherical silicon oxycarbide microparticles according to the present invention are obtained by the method comprising the steps of: hydrolyzing organo-trialkoxysilane in an aqueous acetic acid solution having a pH of 3-6; continuously adding an aqueous alkaline solution, such as aqueous ammonia having a pH of 6-12 to the resultant hydrolyzate to carry out condensation in an alkaline region, thereby providing spherical polysilsesquioxane particles having no melting point or softening point as spherical silicon oxycarbide precursors; and firing the precursors under inert atmosphere at a firing temperature of 600-1400C to obtain spherical silicon oxycarbide powder.
본 발명은 평균 입경(粒徑)이 0.1∼100 ㎛의 범위이며 또한 진구도(眞球度)가 0.95∼1.0인 구형(球形) 실리콘 옥시카바이드 미립자 및 그 제조 방법을 제공하는 것을 과제로 한다. 상기 과제를 해결하기 위하여, 본 발명은, 오르가노 트리알콕시실란을 pH 3∼6의 아세트산 수용액 중에서 가수분해한 후, 계속하여 상기 가수분해물을 pH 7∼12의 암모니아수 등의 알칼리성 수용액을 첨가하여, 알칼리성 영역에서 축합시킴으로써 생성된 구형 실리콘 옥시카바이드 전구체(前驅體)인, 융점이나 연화점을 가지지 않는 구형 폴리실세스퀴옥산 입상물(粒狀物)을, 불활성 분위기 하에서 600∼1400 ℃의 소성 온도에서 소성함으로써 얻어지는 구형 실리콘 옥시카바이드 분립체(粉粒體) 및 그 제조 방법을 제공한다.
SPHERICAL SILICON OXYCARBIDE POWDER AND MANUFACTURING METHOD THEREOF
구형 실리콘 옥시카바이드 분립체와 그 제조 방법
KIZAKI TETSURO (author) / IWATANI KEIZO (author)
2016-12-28
Patent
Electronic Resource
Korean
Spherical silicon oxycarbide particle material and manufacturing method thereof