Concrete dressed brick and making method of it
Provided is a method of manufacturing a concrete dressed brick using a composite containing 40 to 45 wt% of aggregate, 15 to 20 wt% of stone flour, 25 to 30 wt% of slag, and 10 to 12 wt% of cement. The method of manufacturing a concrete dressed brick comprises: a mixing step (S1) of mixing 35% or less of water, which is compared with the weight ratio of cement, to 40 to 45 wt% of aggregate, 15 to 20 wt% of stone flour, 25 to 30 wt% of slag, and 10 to 12 wt% of cement; a molding step (S2) of putting the mixture made in the mixing step (S1) into a mold and pressurizing the mixture to manufacture a molded brick; a curing step (S3) of hardening and curing the molded brick formed in the molding step (S2) at 500°C or more; and a demolding step (S4) of removing the molded brick cured in the curing step (S3) from the mold and completing a concrete brick. In the molding step (S2), the mold is in a block shape, a cylindrical shape, a round shape, or an oval shape, and the mixture is pressed by a hydraulic vibration press or a pressurizing press. In the curing step (S3), while the molded brick is hardened at 500°C or more, the curing temperature does not exceed 50°C to 65°C, and temperature of a curing chamber is not changed suddenly.
본 발명에 따르면, 콘크리트 치장 벽돌 제조방법에 있어서, 골재 40 ~ 45중량%, 석분 15 ~ 20중량%, 슬래그 25 ~ 30중량%, 시멘트 10 ~ 12중량%를 포함하는 조성물로 제조되는 것으로, 상기 골재 40 ~ 45중량%, 석분 15 ~ 20중량%, 슬래그 25 ~ 30중량% 및 시멘트 10 ~ 12중량%에 시멘트 중량대비 물 35% 이하를 혼합하고 교반하는 혼합단계(S1); 상기 혼합단계(S1)에서 혼합된 혼합물을 성형틀에 넣고 가압하여 벽돌 성형물을 제조하는 성형단계(S2); 상기 성형단계(S2)에서 성형된 벽돌 성형물을 500도시 이상으로 경화시켜 양생하는 양생단계(S3); 상기 양생단계(S3)에서 양생된 벽돌 성형물을 상기 성형틀로부터 탈형하여 콘크리트 벽돌을 완성하는 탈형단계(S4);를 포함하되, 상기 성형단계(S2)에서 상기 성형틀은 블록형, 원통형, 원형, 타원형의 형상을 가진 금형이나 거푸집을 이용하고, 상기 가압을 위해서 진동유압 프레스 또는 가압 프레스 장비를 이용하는 것을 포함하며, 상기 양생단계(S3)에서 상기 성형된 벽돌 성형물을 500도시 이상으로 경화시키는 과정에서 도시는 양생온도(℃)와 양생시간(h)를 서로 곱한 것으로, 상기 양생온도는 50(℃) 이상 65(℃)를 초과하지 않고, 양생실의 온도는 급격한 온도변화가 생기지 않도록 하는 것을 특징으로 하는 벽체와 마감재 겸용 콘크리트 치장벽돌 제조방법이 개시된다.
Concrete dressed brick and making method of it
Provided is a method of manufacturing a concrete dressed brick using a composite containing 40 to 45 wt% of aggregate, 15 to 20 wt% of stone flour, 25 to 30 wt% of slag, and 10 to 12 wt% of cement. The method of manufacturing a concrete dressed brick comprises: a mixing step (S1) of mixing 35% or less of water, which is compared with the weight ratio of cement, to 40 to 45 wt% of aggregate, 15 to 20 wt% of stone flour, 25 to 30 wt% of slag, and 10 to 12 wt% of cement; a molding step (S2) of putting the mixture made in the mixing step (S1) into a mold and pressurizing the mixture to manufacture a molded brick; a curing step (S3) of hardening and curing the molded brick formed in the molding step (S2) at 500°C or more; and a demolding step (S4) of removing the molded brick cured in the curing step (S3) from the mold and completing a concrete brick. In the molding step (S2), the mold is in a block shape, a cylindrical shape, a round shape, or an oval shape, and the mixture is pressed by a hydraulic vibration press or a pressurizing press. In the curing step (S3), while the molded brick is hardened at 500°C or more, the curing temperature does not exceed 50°C to 65°C, and temperature of a curing chamber is not changed suddenly.
본 발명에 따르면, 콘크리트 치장 벽돌 제조방법에 있어서, 골재 40 ~ 45중량%, 석분 15 ~ 20중량%, 슬래그 25 ~ 30중량%, 시멘트 10 ~ 12중량%를 포함하는 조성물로 제조되는 것으로, 상기 골재 40 ~ 45중량%, 석분 15 ~ 20중량%, 슬래그 25 ~ 30중량% 및 시멘트 10 ~ 12중량%에 시멘트 중량대비 물 35% 이하를 혼합하고 교반하는 혼합단계(S1); 상기 혼합단계(S1)에서 혼합된 혼합물을 성형틀에 넣고 가압하여 벽돌 성형물을 제조하는 성형단계(S2); 상기 성형단계(S2)에서 성형된 벽돌 성형물을 500도시 이상으로 경화시켜 양생하는 양생단계(S3); 상기 양생단계(S3)에서 양생된 벽돌 성형물을 상기 성형틀로부터 탈형하여 콘크리트 벽돌을 완성하는 탈형단계(S4);를 포함하되, 상기 성형단계(S2)에서 상기 성형틀은 블록형, 원통형, 원형, 타원형의 형상을 가진 금형이나 거푸집을 이용하고, 상기 가압을 위해서 진동유압 프레스 또는 가압 프레스 장비를 이용하는 것을 포함하며, 상기 양생단계(S3)에서 상기 성형된 벽돌 성형물을 500도시 이상으로 경화시키는 과정에서 도시는 양생온도(℃)와 양생시간(h)를 서로 곱한 것으로, 상기 양생온도는 50(℃) 이상 65(℃)를 초과하지 않고, 양생실의 온도는 급격한 온도변화가 생기지 않도록 하는 것을 특징으로 하는 벽체와 마감재 겸용 콘크리트 치장벽돌 제조방법이 개시된다.
Concrete dressed brick and making method of it
벽체와 마감재 겸용 콘크리트 치장벽돌 및 이의 제조방법
LEE YONG GAB (author) / CHO YONG SOO (author)
2018-07-09
Patent
Electronic Resource
Korean
Dressed in A Delicate Concrete Curtain
British Library Online Contents | 2009
Making concrete brick as quarry by-product
Engineering Index Backfile | 1946
Recycled aggregate brick making equipment and brick making method
| European Patent Office | 2024