FIELD: chemistry.SUBSTANCE: method comprises, in a standard sample and analysed sample of a bitumen-polymer composition, measuring effective viscosity at temperature t=20°C, t=80°C and t=150°C and shear rate D=5.56 s, D=11.1 sand D=16.67 s, ?=5.0 s, ?=15.0 s, ?=30.0 s after the beginning of application thereof; and predetermining confidence intervals of relative deviations of the values of effective viscosity of the standard bitumen-polymer composition and a set of quality parameters, which corresponds to the processing instructions for said standard product; the method of determining confidence intervals of relative deviations of the values of effective viscosity ??, determined by expert evaluation methods, is reduced in a general form to calculation of its relative change based on a given ratio with subsequent formation of a confidence interval of its deviation for the given production conditions. The value ??is calculated based on the obtained experimental values of effective viscosity of the standard bitumen-polymer composition, and control of quality parameters of the analysed bitumen-polymer composition is carried out by comparing values of the obtained relative changes of effective viscosity of the analysed bitumen-polymer composition ??with corresponding confidence intervals of relative deviations of the effective viscosity of the standard bitumen-polymer composition, obtained under the same analysis conditions; based on the comparison results, a conclusion is made on the conformity of the analysed bitumen-polymer composition to properties of the standard bitumen-polymer composition, particularly if the obtained values of the relative change of the values of effective viscosity ??of the analysed bitumen-polymer composition twice successively enter the corresponding different confidence intervals of its relative change for the standard bitumen-polymer composition for partially or completely different conditions of obtaining initial values of effective viscosity, used to calculate ??and form intervals for its confidence deviation for the standard bitumen-polymer composition, the analysed bitumen-polymer composition has a set of physical and mechanical properties which correspond to the process instruction for said product, and is a standard bitumen-polymer composition; if the obtained value of change of effective viscosity ??of the analysed bitumen-polymer composition does not enter the available confidence interval of its change for the standard bitumen-polymer composition, a conclusion is made on the non-conformity of the analysed bitumen-polymer composition to properties of the standard bitumen-polymer composition on the set of physical and mechanical properties.EFFECT: high accuracy, reliability and efficiency, and easy control.4 ex, 11 tbl

Изобретение относится к химической технологии, а именно к технологии производства битум-полимерных композиций, и может быть использовано для контроля и прогнозирования их параметров качества в процессе производства.Способ характеризуется тем, что в кондиционном и исследуемом образцах битум-полимерной композиции измеряют величины эффективной вязкости при температурах t=20°C, t=80°C и t=150°C и градиентах скорости сдвига D=5,56 с, D=11,1 си D=16,67 с, через τ=5,0 сек, τ=15,0 сек, τ=30,0 сек после начала ее приложения, и предварительно определяют доверительные интервалы относительных отклонений величин эффективной вязкости кондиционной битум-полимерной композиции и комплекс параметров качества, который соответствует технологической инструкции на данный кондиционный продукт, методика определения доверительных интервалов относительных отклонений эффективной вязкости Δη, определяемых методами экспертной оценки, сводится в общем виде к расчету относительного ее изменения на основании заданного соотношения с последующим формированием доверительного интервала ее отклонения для данных условий получения, причем значение Δηпредварительно рассчитывают на основе полученных экспериментальных величин эффективной вязкости кондиционной битум-полимерной композиции, а контроль параметров качества исследуемой битум-полимерной композиции проводят, сравнивая значения полученных величин относительных изменений эффективной вязкости исследуемой битум-полимерной композиции Δηс соответствующими доверительными интервалами относительных отклонений величин эффективной вязкости кондиционной битум-полимерной композиции, полученны