COMPOSITION FOR HEAT-RESISTANT COMPOSITES PRODUCTION
FIELD: chemistry.SUBSTANCE: composition for manufacture of heat-resistant composites (concretes), including spent catalyst IM-2201, carbonate rock rubble with an average grain density of 2-2.5 kg/m, fraction of 5-10 mm, HRO, density of at least 1.69 g/cm, and aluminochromous waste of aluminium alloys etching with particle size of 0.1 to 5 m, also comprises ferrosilicon production slag, milled to pass through a 0.14 mm sieve, with oxides content, wt %: SiO- 49.4; AlO- 6.8; FeO- 4.4; CaO - 24.5; MgO - 15.1 at the following ratio, wt %: spent catalyst IM-2201 - 10-15, carbonate rock rubble with an average grain density of 2-2.5 kg/m- 33-40 , HRO- 10-15, aluminochromous waste of aluminum alloys etching - 24-30, ferrosilicon production slag - 10-13. Application of man-made materials for heat-resistant concrete preparation contributes to industrial waste recycling, environmental protection, expansion of the raw material base for building materials.EFFECT: high ultimate compression strength and heat-resistance of the heat-resistant composites.3 tbl
Изобретение относится к области строительных материалов, в частности к производству жаростойких композитов (бетонов) на основе химических связующих. Техническим результатом изобретения является повышение предела прочности при сжатии и термостойкости жаростойких композитов Композиция для изготовления жаростойких композитов (бетонов), включающая отработанный катализатор ИМ-2201, щебень из карбонатных пород со средней плотностью зерен 2-2,5 кг/м, фракции 5-10 мм, НРО, плотностью не менее 1,69 г/сми алюмохромистые отходы травления алюминиевых сплавов с размером частиц от 0,1 до 5 мкм, дополнительно содержит шлак от производства ферросилиция, размолотый до прохода через сито 0,14 мм и с содержанием оксидов, мас.%: SiO- 49,4; AlO- 6,8; FeO- 4,4; СаО - 24,5; MgO - 15,1 при следующем соотношении компонентов, мас.%: отработанный катализатор ИМ-2201 10-15, щебень из карбонатных пород со средней плотностью зерен 2-2,5 кг/м33-40, НРО10-15, алюмохромистые отходы травления алюминиевых сплавов 24-30, шлак от производства ферросилиция 10-13. Использование техногенного сырья при получении жаростойкого бетона способствует утилизации промышленных отходов, охране окружающей среды, расширению сырьевой базы для строительных материалов. 3 табл.
COMPOSITION FOR HEAT-RESISTANT COMPOSITES PRODUCTION
FIELD: chemistry.SUBSTANCE: composition for manufacture of heat-resistant composites (concretes), including spent catalyst IM-2201, carbonate rock rubble with an average grain density of 2-2.5 kg/m, fraction of 5-10 mm, HRO, density of at least 1.69 g/cm, and aluminochromous waste of aluminium alloys etching with particle size of 0.1 to 5 m, also comprises ferrosilicon production slag, milled to pass through a 0.14 mm sieve, with oxides content, wt %: SiO- 49.4; AlO- 6.8; FeO- 4.4; CaO - 24.5; MgO - 15.1 at the following ratio, wt %: spent catalyst IM-2201 - 10-15, carbonate rock rubble with an average grain density of 2-2.5 kg/m- 33-40 , HRO- 10-15, aluminochromous waste of aluminum alloys etching - 24-30, ferrosilicon production slag - 10-13. Application of man-made materials for heat-resistant concrete preparation contributes to industrial waste recycling, environmental protection, expansion of the raw material base for building materials.EFFECT: high ultimate compression strength and heat-resistance of the heat-resistant composites.3 tbl
Изобретение относится к области строительных материалов, в частности к производству жаростойких композитов (бетонов) на основе химических связующих. Техническим результатом изобретения является повышение предела прочности при сжатии и термостойкости жаростойких композитов Композиция для изготовления жаростойких композитов (бетонов), включающая отработанный катализатор ИМ-2201, щебень из карбонатных пород со средней плотностью зерен 2-2,5 кг/м, фракции 5-10 мм, НРО, плотностью не менее 1,69 г/сми алюмохромистые отходы травления алюминиевых сплавов с размером частиц от 0,1 до 5 мкм, дополнительно содержит шлак от производства ферросилиция, размолотый до прохода через сито 0,14 мм и с содержанием оксидов, мас.%: SiO- 49,4; AlO- 6,8; FeO- 4,4; СаО - 24,5; MgO - 15,1 при следующем соотношении компонентов, мас.%: отработанный катализатор ИМ-2201 10-15, щебень из карбонатных пород со средней плотностью зерен 2-2,5 кг/м33-40, НРО10-15, алюмохромистые отходы травления алюминиевых сплавов 24-30, шлак от производства ферросилиция 10-13. Использование техногенного сырья при получении жаростойкого бетона способствует утилизации промышленных отходов, охране окружающей среды, расширению сырьевой базы для строительных материалов. 3 табл.
COMPOSITION FOR HEAT-RESISTANT COMPOSITES PRODUCTION
Композиция для изготовления жаростойких композитов
ABDRAKHIMOVA ELENA SERGEEVNA (author)
2017-04-13
Patent
Electronic Resource
Russian