CHROMIUM-PERICLASE REFRACTORY MATERIAL
FIELD: metallurgy.SUBSTANCE: refractory material comprises granular fused chromium periclase and dispersed magnesia component at the following ratio of components, wt %: granular fused chromium-periclase-base, dispersed component-15-30. As a dispersed component refractory material contains a mixture of fused chromium-periclase and sintered and/or cauterized periclase, taken in the ratio of (85-98):(2-15). The fused chromium-periclase contains, wt %: SiO0.40-1.50; AlO3-10; CrO15-28; CaO is less than 1.0; MgO 55-65; FeO 5-15. The chromium-periclase refractory material can additionally contain chromium oxide, titanium oxide, silicon oxide, zirconium oxide or their combinations in an amount up to 10% in the composition of dispersed component.EFFECT: increased resistance of the refractory material to structural cracking in contact with molten metal or slag.8 cl, 2 tbl
Изобретение относится к огнеупорной промышленности, а именно к производству хромитопериклазовых материалов, предназначенных для футеровок агрегатов внепечной обработки стали и металлургических агрегатов, работающих в высокотемпературном режиме в контакте с агрессивной средой. Хромитопериклазовый огнеупор включает зернистый плавленый хромитопериклаз и дисперсный магнезиальный компонент при следующем соотношении компонентов, мас.%: зернистый плавленый хромитопериклаз – основа, дисперсный компонент - 15-30. В качестве дисперсного компонента огнеупор содержит смесь плавленого хромитопериклаза и спеченного и/или каустизированного периклаза, взятых в соотношении (85-98):(2-15). Плавленый хромитопериклаз содержит, мас.%: SiO0,40-1,50; AlO3-10; CrO15-28; CaO менее 1,0; MgO 55-65; FeO 5-15. Хромитопериклазовый огнеупор может дополнительно содержать оксид хрома, оксид титана, оксид кремния, оксид циркония или их комбинации в количестве до 10% в составе дисперсного компонента. Технический результат изобретения - увеличение сопротивления огнеупора структурному трещинообразованию в контакте с расплавом металла или шлака. 7 з.п. ф-лы, 2 табл.
CHROMIUM-PERICLASE REFRACTORY MATERIAL
FIELD: metallurgy.SUBSTANCE: refractory material comprises granular fused chromium periclase and dispersed magnesia component at the following ratio of components, wt %: granular fused chromium-periclase-base, dispersed component-15-30. As a dispersed component refractory material contains a mixture of fused chromium-periclase and sintered and/or cauterized periclase, taken in the ratio of (85-98):(2-15). The fused chromium-periclase contains, wt %: SiO0.40-1.50; AlO3-10; CrO15-28; CaO is less than 1.0; MgO 55-65; FeO 5-15. The chromium-periclase refractory material can additionally contain chromium oxide, titanium oxide, silicon oxide, zirconium oxide or their combinations in an amount up to 10% in the composition of dispersed component.EFFECT: increased resistance of the refractory material to structural cracking in contact with molten metal or slag.8 cl, 2 tbl
Изобретение относится к огнеупорной промышленности, а именно к производству хромитопериклазовых материалов, предназначенных для футеровок агрегатов внепечной обработки стали и металлургических агрегатов, работающих в высокотемпературном режиме в контакте с агрессивной средой. Хромитопериклазовый огнеупор включает зернистый плавленый хромитопериклаз и дисперсный магнезиальный компонент при следующем соотношении компонентов, мас.%: зернистый плавленый хромитопериклаз – основа, дисперсный компонент - 15-30. В качестве дисперсного компонента огнеупор содержит смесь плавленого хромитопериклаза и спеченного и/или каустизированного периклаза, взятых в соотношении (85-98):(2-15). Плавленый хромитопериклаз содержит, мас.%: SiO0,40-1,50; AlO3-10; CrO15-28; CaO менее 1,0; MgO 55-65; FeO 5-15. Хромитопериклазовый огнеупор может дополнительно содержать оксид хрома, оксид титана, оксид кремния, оксид циркония или их комбинации в количестве до 10% в составе дисперсного компонента. Технический результат изобретения - увеличение сопротивления огнеупора структурному трещинообразованию в контакте с расплавом металла или шлака. 7 з.п. ф-лы, 2 табл.
CHROMIUM-PERICLASE REFRACTORY MATERIAL
Хромитопериклазовый огнеупор
AKSELROD LEV MOISEEVICH (author) / TURCHIN MAKSIM YUREVICH (author) / EROSHIN MIKHAIL ALEKSANDROVICH (author) / YARUSHINA TATYANA VIKTOROVNA (author) / ZHILTSOVA ANASTASIYA GERMANOVNA (author)
2017-10-24
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME
Preparation method of periclase-forsterite complex-phase refractory raw material
| European Patent Office | 2024
Method for synthesizing periclase-forsterite refractory material at low temperature
| European Patent Office | 2024