METHOD OF PRODUCING HIGH-DENSITY AQUEOUS SLURRIES BASED ON LITHIUM-ALUMINOSILICATE GLASS
FIELD: chemistry.SUBSTANCE: invention relates to ceramic industry and can be used in making glass-ceramic articles by water-slurry casting into porous molds. Method of producing a high-density aqueous slurry based on lithium aluminosilicate glass involves loading into a mill a starting material in form of a glass granulate or process wastes for making articles and grinding bodies at ratio of 1:(3–4), introduction in one pass of design amount of water, wet grinding and stabilization of slurry by mechanical stirring with subsequent addition of HCl or NHCl, prior to loading of the initial raw material, a fraction passing through the sieve with the cell side of 1.2 mm, or 1.4 mm, or 1.6 mm is removed from it, and the acid is added in amount of 0.1 ml per 1 l of the stabilized slurry, based on calculation reducing the slurry pH value by 0.1, wherein acid is mixed with same volume of distilled water before introduction into the slurry and uniformly poured on the surface of the slurry.EFFECT: high efficiency when preparing high-density aqueous slurries of lithium aluminosilicate glass in ball mills and low level of process rejection when making ceramic articles from said slurries.1 cl, 1 tbl, 4 ex
Изобретение относится к керамической промышленности и может быть использовано при изготовлении стеклокерамических изделий методом водного шликерного литья в пористые формы. Способ получения высокоплотного водного шликера на основе литийалюмосиликатного стекла включает загрузку в мельницу исходного сырья в виде гранулята стекла либо технологических отходов производства изделий и мелющих тел при соотношении 1:(3-4), введение в один прием расчетного количества воды, мокрый помол и стабилизацию шликера механическим перемешиванием с последующим добавлением HCl или NHCl, перед загрузкой исходного сырья удаляют из него фракцию, прошедшую через сито со стороной ячейки 1,2 мм, или 1,4 мм, или 1,6 мм, а кислоту добавляют в количестве 0,1 мл на 1 л стабилизированного шликера, исходя из расчета снижения значения рН шликера на 0,1, при этом кислоту перед введением в шликер смешивают с таким же объемом дистиллированной воды и равномерно разливают по поверхности шликера. Технический результат – повышение производительности при приготовлении высокоплотных водных шликеров литийалюмосиликатного стекла в шаровых мельницах и снижение уровня технологического брака при изготовлении из данных шликеров керамических изделий. 1 табл., 4 пр.
METHOD OF PRODUCING HIGH-DENSITY AQUEOUS SLURRIES BASED ON LITHIUM-ALUMINOSILICATE GLASS
FIELD: chemistry.SUBSTANCE: invention relates to ceramic industry and can be used in making glass-ceramic articles by water-slurry casting into porous molds. Method of producing a high-density aqueous slurry based on lithium aluminosilicate glass involves loading into a mill a starting material in form of a glass granulate or process wastes for making articles and grinding bodies at ratio of 1:(3–4), introduction in one pass of design amount of water, wet grinding and stabilization of slurry by mechanical stirring with subsequent addition of HCl or NHCl, prior to loading of the initial raw material, a fraction passing through the sieve with the cell side of 1.2 mm, or 1.4 mm, or 1.6 mm is removed from it, and the acid is added in amount of 0.1 ml per 1 l of the stabilized slurry, based on calculation reducing the slurry pH value by 0.1, wherein acid is mixed with same volume of distilled water before introduction into the slurry and uniformly poured on the surface of the slurry.EFFECT: high efficiency when preparing high-density aqueous slurries of lithium aluminosilicate glass in ball mills and low level of process rejection when making ceramic articles from said slurries.1 cl, 1 tbl, 4 ex
Изобретение относится к керамической промышленности и может быть использовано при изготовлении стеклокерамических изделий методом водного шликерного литья в пористые формы. Способ получения высокоплотного водного шликера на основе литийалюмосиликатного стекла включает загрузку в мельницу исходного сырья в виде гранулята стекла либо технологических отходов производства изделий и мелющих тел при соотношении 1:(3-4), введение в один прием расчетного количества воды, мокрый помол и стабилизацию шликера механическим перемешиванием с последующим добавлением HCl или NHCl, перед загрузкой исходного сырья удаляют из него фракцию, прошедшую через сито со стороной ячейки 1,2 мм, или 1,4 мм, или 1,6 мм, а кислоту добавляют в количестве 0,1 мл на 1 л стабилизированного шликера, исходя из расчета снижения значения рН шликера на 0,1, при этом кислоту перед введением в шликер смешивают с таким же объемом дистиллированной воды и равномерно разливают по поверхности шликера. Технический результат – повышение производительности при приготовлении высокоплотных водных шликеров литийалюмосиликатного стекла в шаровых мельницах и снижение уровня технологического брака при изготовлении из данных шликеров керамических изделий. 1 табл., 4 пр.
METHOD OF PRODUCING HIGH-DENSITY AQUEOUS SLURRIES BASED ON LITHIUM-ALUMINOSILICATE GLASS
Способ получения высокоплотных водных шликеров на основе литийалюмосиликатного стекла
KHARITONOV DMITRIJ VIKTOROVICH (author) / ANASHKINA ANTONINA ALEKSANDROVNA (author) / KONKINA RAISA SERGEEVNA (author) / RUSIN MIKHAIL YUREVICH (author) / KHAMITSAEV ANATOLIJ STEPANOVICH (author)
2019-11-29
Patent
Electronic Resource
Russian
METHOD FOR PRODUCING ARTICLES FROM GLASS-CERAMIC MATERIAL OF LITHIUM ALUMINOSILICATE COMPOSITION
| European Patent Office | 2022
| European Patent Office | 2015
METHOD OF MAKING GLASS-CERAMIC ARTICLES OF LITHIUM ALUMINOSILICATE COMPOSITION
| European Patent Office | 2019
Toughening mechanisms for a zirconia-lithium aluminosilicate glass-ceramic
| British Library Online Contents | 1995
Selective laser densification of lithium aluminosilicate glass ceramic tapes
| British Library Online Contents | 2013