METHOD OF PRODUCING BORON-CARBON COMPOSITE MATERIAL
FIELD: technological processes.SUBSTANCE: invention relates to powder metallurgy, particularly to a method of producing boron-carbon composite material. Method involves mechanical treatment in a planetary mill of a mixture of amorphous boron powders with particle size of less than 2 mcm and fullerite Cwith particle size of less than 200 mcm, which are taken in ratio from 1:5 to 5:1, with addition of methyl or ethyl alcohol in amount of 1 ml per 1 g of mixture in mode 900–1,200 rpm for 10–30 minutes to obtain a homogeneous state, extraction of mixture from mill, drying mixture in air at temperature 100 °C for 2 hours and exposing the mixture to pressure within 1.5–2.5 GPa and a temperature in range of 900 to 1,100 °C for 60–120 minutes.EFFECT: invention enables to obtain boron-carbon composite material with high elasticity of more than 50 % while maintaining sufficiently high hardness of about 10 GPa on the Vickers scale and density of not less than 95 %.1 cl, 2 dwg, 5 ex
Изобретение относится к области порошковой металлургии, в частности к способу получения композиционного материала бор-углерод. Способ включает механическую обработку в планетарной мельнице смеси порошков аморфного бора с размерами частиц менее 2 мкм и фуллерита Сс размерами частиц менее 200 мкм, которые берут в соотношении от 1:5 до 5:1, с добавлением метилового или этилового спирта в количестве 1 мл на 1 г смеси в режиме 900-1200 оборотов в минуту в течение 10-30 мин с получением гомогенного состояния, извлечение смеси из мельницы, сушку смеси на воздухе при температуре 100°С в течение 2 ч и воздействие на смесь давлением в пределах 1,5-2,5 ГПа и температурой в пределах от 900 до 1100°С в течение 60-120 мин. Изобретение обеспечивает получение композиционного материала бор-углерод с повышенной более 50% эластичностью при сохранении достаточно высокой твердости около 10 ГПа по шкале Виккерса и плотности не менее 95%. 2 ил., 5 пр.
METHOD OF PRODUCING BORON-CARBON COMPOSITE MATERIAL
FIELD: technological processes.SUBSTANCE: invention relates to powder metallurgy, particularly to a method of producing boron-carbon composite material. Method involves mechanical treatment in a planetary mill of a mixture of amorphous boron powders with particle size of less than 2 mcm and fullerite Cwith particle size of less than 200 mcm, which are taken in ratio from 1:5 to 5:1, with addition of methyl or ethyl alcohol in amount of 1 ml per 1 g of mixture in mode 900–1,200 rpm for 10–30 minutes to obtain a homogeneous state, extraction of mixture from mill, drying mixture in air at temperature 100 °C for 2 hours and exposing the mixture to pressure within 1.5–2.5 GPa and a temperature in range of 900 to 1,100 °C for 60–120 minutes.EFFECT: invention enables to obtain boron-carbon composite material with high elasticity of more than 50 % while maintaining sufficiently high hardness of about 10 GPa on the Vickers scale and density of not less than 95 %.1 cl, 2 dwg, 5 ex
Изобретение относится к области порошковой металлургии, в частности к способу получения композиционного материала бор-углерод. Способ включает механическую обработку в планетарной мельнице смеси порошков аморфного бора с размерами частиц менее 2 мкм и фуллерита Сс размерами частиц менее 200 мкм, которые берут в соотношении от 1:5 до 5:1, с добавлением метилового или этилового спирта в количестве 1 мл на 1 г смеси в режиме 900-1200 оборотов в минуту в течение 10-30 мин с получением гомогенного состояния, извлечение смеси из мельницы, сушку смеси на воздухе при температуре 100°С в течение 2 ч и воздействие на смесь давлением в пределах 1,5-2,5 ГПа и температурой в пределах от 900 до 1100°С в течение 60-120 мин. Изобретение обеспечивает получение композиционного материала бор-углерод с повышенной более 50% эластичностью при сохранении достаточно высокой твердости около 10 ГПа по шкале Виккерса и плотности не менее 95%. 2 ил., 5 пр.
METHOD OF PRODUCING BORON-CARBON COMPOSITE MATERIAL
СПОСОБ ПОЛУЧЕНИЯ КОМПОЗИЦИОННОГО МАТЕРИАЛА БОР-УГЛЕРОД
BAGRAMOV RUSTEM KHAMITOVICH (author) / SEREBRYANAYA NADEZHDA RUVIMOVNA (author) / BLANK VLADIMIR DAVYDOVICH (author)
2019-12-23
Patent
Electronic Resource
Russian
IPC:
C01B
NON-METALLIC ELEMENTS
,
Nichtmetallische Elemente
/
B82B
Nanostrukturen, gestaltet durch die Manipulation von einzelnen Atomen, Molekülen, oder einer begrenzten Ansammlung von Atomen oder Molekülen als einzelne Einheiten
,
NANOSTRUCTURES FORMED BY MANIPULATION OF INDIVIDUAL ATOMS, MOLECULES, OR LIMITED COLLECTIONS OF ATOMS OR MOLECULES AS DISCRETE UNITS
/
B82Y
Bestimmter Gebrauch oder bestimmte Anwendung von Nanostrukturen
,
SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES
/
C04B
Kalk
,
LIME
METHOD FOR PREPARING CARBON/BORON CARBIDE COMPOSITE MATERIAL
| European Patent Office | 2022
COMPOSITE CARBON MATERIAL, METHOD FOR PRODUCING THE COMPOSITE CARBON MATERIAL AND BOARD
| European Patent Office | 2016
| European Patent Office | 2016