CLINKERLESS ALKALINE BINDER
FIELD: chemistry.SUBSTANCE: invention relates to the industry of construction materials and can be used in making concrete and solutions based on binder alkaline activation. Clinkerless cement of alkaline activation includes reaction-active component, mineral powder and alkaline activator. Reaction-active component used is silicified marl. Silicified marl ground to a specific surface of 1150 m/kg, further heat treated in a muffle furnace at 700 °C. Silicified marl is then mixed with mineral powder of volcanic tuff. Volcanic tuff is preliminarily milled to specific surface of 905 m/kg, then it is activated with an alkaline solution. Alkaline solution is prepared based on sodium hydroxide and liquid sodium glass with a silicate modulus of 2.8 and density of 1.24 g/cm. Components are used in the following ratio, wt. %: thermally activated marl - 34.8–67.0; volcanic tuff - 21.4–51.2; liquid glass NaSiO- 11.0–13.0; sodium hydroxide NaOH - 0.6–1.0.EFFECT: technical result is improvement of physical and mechanical properties of end product.1 cl, 3 dwg, 4 tbl
Изобретение относится к промышленности строительных материалов и может быть использовано при изготовлении бетонов и растворов на основе вяжущих щелочной активации. Бесклинкерное вяжущее щелочной активации включает реакционно-активный компонент, минеральный порошок и щелочной активатор. В качестве реакционно-активного компонента используют окремненный мергель. Окремненный мергель измельчают до удельной поверхности 1150 м/кг, далее термообрабатывают в муфельной печи при температуре 700°С. Затем окремненный мергель смешивают с минеральным порошком из вулканического туфа. Вулканический туф предварительно измельчают до удельной поверхности 905 м/кг, далее активируют щелочным раствором. Щелочной раствор приготовлен на основе гидроксида натрия и жидкого стекла натриевого с силикатным модулем 2,8 и плотностью 1,24 г/см. Компоненты используют в следующем соотношении, мас. %: термоактивированный мергель – 34,8-67,0; вулканический туф – 21,4-51,2; жидкое стекло NaSiO– 11,0-13,0; гидроксид натрия NaOH – 0,6-1,0. Технический результат – улучшение физико-механических свойств конечного продукта. 3 ил., 4 табл.
CLINKERLESS ALKALINE BINDER
FIELD: chemistry.SUBSTANCE: invention relates to the industry of construction materials and can be used in making concrete and solutions based on binder alkaline activation. Clinkerless cement of alkaline activation includes reaction-active component, mineral powder and alkaline activator. Reaction-active component used is silicified marl. Silicified marl ground to a specific surface of 1150 m/kg, further heat treated in a muffle furnace at 700 °C. Silicified marl is then mixed with mineral powder of volcanic tuff. Volcanic tuff is preliminarily milled to specific surface of 905 m/kg, then it is activated with an alkaline solution. Alkaline solution is prepared based on sodium hydroxide and liquid sodium glass with a silicate modulus of 2.8 and density of 1.24 g/cm. Components are used in the following ratio, wt. %: thermally activated marl - 34.8–67.0; volcanic tuff - 21.4–51.2; liquid glass NaSiO- 11.0–13.0; sodium hydroxide NaOH - 0.6–1.0.EFFECT: technical result is improvement of physical and mechanical properties of end product.1 cl, 3 dwg, 4 tbl
Изобретение относится к промышленности строительных материалов и может быть использовано при изготовлении бетонов и растворов на основе вяжущих щелочной активации. Бесклинкерное вяжущее щелочной активации включает реакционно-активный компонент, минеральный порошок и щелочной активатор. В качестве реакционно-активного компонента используют окремненный мергель. Окремненный мергель измельчают до удельной поверхности 1150 м/кг, далее термообрабатывают в муфельной печи при температуре 700°С. Затем окремненный мергель смешивают с минеральным порошком из вулканического туфа. Вулканический туф предварительно измельчают до удельной поверхности 905 м/кг, далее активируют щелочным раствором. Щелочной раствор приготовлен на основе гидроксида натрия и жидкого стекла натриевого с силикатным модулем 2,8 и плотностью 1,24 г/см. Компоненты используют в следующем соотношении, мас. %: термоактивированный мергель – 34,8-67,0; вулканический туф – 21,4-51,2; жидкое стекло NaSiO– 11,0-13,0; гидроксид натрия NaOH – 0,6-1,0. Технический результат – улучшение физико-механических свойств конечного продукта. 3 ил., 4 табл.
CLINKERLESS ALKALINE BINDER
БЕСКЛИНКЕРНОЕ ВЯЖУЩЕЕ ЩЕЛОЧНОЙ АКТИВАЦИИ
SALAMANOVA MADINA SHAKHIDOVNA (author) / MURTAZAEV SAJD-ALVI YUSUPOVICH (author) / BATAEV DENA KARIM-SULTANOVICH (author) / NAKHAEV MAGOMED RAMZANOVICH (author) / SAJDUMOV MAGOMED SALAMUVICH (author)
2020-10-07
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME
Alkaline activated binder system
| British Library Online Contents | 1997
METHOD FOR PREPARING CLINKERLESS BINDER ALKALINE ACTIVATION
| European Patent Office | 2020
Hydraulic binder composition comprising steelmaking slag, co-binder and alkaline inorganic salt
| European Patent Office | 2024
Study of a binder based on alkaline activated limestone
| Elsevier | 2021