METHOD FOR PREPARING CLINKERLESS BINDER ALKALINE ACTIVATION
FIELD: construction.SUBSTANCE: invention relates to the industry of construction materials and can be used in making concrete and solutions based on binder alkaline activation. Invention contains a method for obtaining clinkerless binder alkaline activation. Method involves separate grinding of siliceous marl and volcanic tuff with further combined stirring in the presence of alkaline activators. Siliceous marl ground to a specific surface of 1,150 m/kg, followed by heat treatment in a muffle furnace at 700 °C. Then it is mixed for 2 minutes with volcanic tuff. Volcanic tuff is preliminarily milled to specific surface area of 905 m/kg. Next, activated for 2–3 minutes with an alkaline solution based on sodium hydroxide, sodium liquid glass with silicate module 2.8, density of 1.24 g/cm, and hydrophobization liquid GKZh-11. Weight ratio of components, wt%: thermally activated marl – 33.6–66.2; volcanic tuff – 21.4–51.2; liquid glass NaSiO– 11.0–13.0; sodium hydroxide NaOH – 0.6–1.0; GKZh-11 – 0.8–1.2.EFFECT: improved physical and mechanical properties of the end product.1 cl, 3 dwg, 4 tbl
Изобретение относится к промышленности строительных материалов и может быть использовано при изготовлении бетонов и растворов на основе вяжущих щелочной активации. Изобретение содержит способ получения бесклинкерного вяжущего щелочной активации. Способ включает раздельный помол окремненного мергеля и вулканического туфа с последующим совместным перемешиванием в присутствии щелочных активаторов. Окремненный мергель измельчают до удельной поверхности 1150 м/кг с последующей термообработкой в муфельной печи при температуре 700°С. Затем смешивают в течение 2 минут с вулканическим туфом. Вулканический туф предварительно измельчают до удельной поверхности 905 м/кг. Далее активируют в течение 2-3 минут щелочным раствором на основе гидроксида натрия, жидкого стекла натриевого с силикатным модулем 2,8, плотностью 1,24 г/см, и гидрофобизирующей жидкостью ГКЖ-11. Массовое соотношение компонентов, мас. %: термоактивированный мергель – 33,6-66,2; вулканический туф – 21,4-51,2; жидкое стекло NaSiO– 11,0-13,0; гидроксид натрия NaOH – 0,6-1,0; ГКЖ-11 – 0,8-1,2. Технический результат – улучшение физико-механических свойств конечного продукта. 3 ил., 4 табл.
METHOD FOR PREPARING CLINKERLESS BINDER ALKALINE ACTIVATION
FIELD: construction.SUBSTANCE: invention relates to the industry of construction materials and can be used in making concrete and solutions based on binder alkaline activation. Invention contains a method for obtaining clinkerless binder alkaline activation. Method involves separate grinding of siliceous marl and volcanic tuff with further combined stirring in the presence of alkaline activators. Siliceous marl ground to a specific surface of 1,150 m/kg, followed by heat treatment in a muffle furnace at 700 °C. Then it is mixed for 2 minutes with volcanic tuff. Volcanic tuff is preliminarily milled to specific surface area of 905 m/kg. Next, activated for 2–3 minutes with an alkaline solution based on sodium hydroxide, sodium liquid glass with silicate module 2.8, density of 1.24 g/cm, and hydrophobization liquid GKZh-11. Weight ratio of components, wt%: thermally activated marl – 33.6–66.2; volcanic tuff – 21.4–51.2; liquid glass NaSiO– 11.0–13.0; sodium hydroxide NaOH – 0.6–1.0; GKZh-11 – 0.8–1.2.EFFECT: improved physical and mechanical properties of the end product.1 cl, 3 dwg, 4 tbl
Изобретение относится к промышленности строительных материалов и может быть использовано при изготовлении бетонов и растворов на основе вяжущих щелочной активации. Изобретение содержит способ получения бесклинкерного вяжущего щелочной активации. Способ включает раздельный помол окремненного мергеля и вулканического туфа с последующим совместным перемешиванием в присутствии щелочных активаторов. Окремненный мергель измельчают до удельной поверхности 1150 м/кг с последующей термообработкой в муфельной печи при температуре 700°С. Затем смешивают в течение 2 минут с вулканическим туфом. Вулканический туф предварительно измельчают до удельной поверхности 905 м/кг. Далее активируют в течение 2-3 минут щелочным раствором на основе гидроксида натрия, жидкого стекла натриевого с силикатным модулем 2,8, плотностью 1,24 г/см, и гидрофобизирующей жидкостью ГКЖ-11. Массовое соотношение компонентов, мас. %: термоактивированный мергель – 33,6-66,2; вулканический туф – 21,4-51,2; жидкое стекло NaSiO– 11,0-13,0; гидроксид натрия NaOH – 0,6-1,0; ГКЖ-11 – 0,8-1,2. Технический результат – улучшение физико-механических свойств конечного продукта. 3 ил., 4 табл.
METHOD FOR PREPARING CLINKERLESS BINDER ALKALINE ACTIVATION
СПОСОБ ПОЛУЧЕНИЯ БЕСКЛИНКЕРНОГО ВЯЖУЩЕГО ЩЕЛОЧНОЙ АКТИВАЦИИ
MURTAZAEV SAJD-ALVI YUSUPOVICH (author) / SALAMANOVA MADINA SHAKHIDOVNA (author) / NAKHAEV MAGOMED RAMZANOVICH (author) / SAJDUMOV MAGOMED SALAMUVICH (author) / ALIEV SALAMBEK ALIMBEKOVICH (author) / MURTAZAEVA TAMARA SAID-ALVIEVNA (author)
2020-09-24
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME
Method for preparing calcium carbonate binder through CO2 activation
| European Patent Office | 2023
Alkaline Activation of Volcanic Ash as Binder for Soil Improvement
| Springer Verlag | 2023