METHOD OF PRODUCING PORTLAND CEMENT
FIELD: chemistry.SUBSTANCE: invention relates to production of hydraulic binder materials based on mineral base, particularly, to production of portland cements. Method involves burning Portland cement raw meal in a reducing atmosphere and subsequent grinding Portland cement clinker to a specific surface Sss= 2800–3000 cm2/g with the addition of gypsum, is not greater than 3.5 % SO3. To form reducing medium inside clinker capsules during firing raw mixture coke additives are introduced into it in range of 3.5–4 wt. % over the weight of the crude mixture based on coke contained in the ash-slag wastes, which are an integral part of the components of the crude mixture of portland cement. Reduction gas medium formation during clinker annealing is controlled by air excess ratio of 1.05–1.10, annealing is carried out at temperature of 1450 °C for 30 minutes, rapid cooling of cement clinker is carried out in an aerated air-water medium.EFFECT: higher activity of cement, reduced consumption of process fuel and electric power, improved grinding capacity of cement clinker, increased service life of lining.1 cl, 1 tbl
Изобретение относится к технологии получения гидравлических вяжущих материалов на минеральной основе, в частности к технологии получения портландцементов. Способ включает обжиг портландцементной сырьевой смеси в восстановительной среде и дальнейший помол портландцементного клинкера до удельной поверхности Sуд=2800-3000 см2/г с добавлением гипса, не превышающим 3,5% по SO3. Для образования восстановительной среды внутри капсул клинкера при обжиге сырьевой смеси в нее вводят добавки кокса в пределах 3,5-4 мас. % сверх массы сырьевой смеси с учетом кокса, содержащегося в золошлаковых отходах, являющихся составной частью компонентов сырьевой смеси портландцемента. Образование восстановительной газовой среды при обжиге клинкера регулируется коэффициентом избытка воздуха 1,05-1,10, обжиг осуществляется при температуре 1450°С в течение 30 минут, быстрое охлаждение цементного клинкера производят в аэрированной воздушно-водной среде. Повышается активность цемента, снижается расход технологического топлива и электроэнергии, улучшается размалываемость цементного клинкера, увеличивается срок службы футеровки. 1 табл.
METHOD OF PRODUCING PORTLAND CEMENT
FIELD: chemistry.SUBSTANCE: invention relates to production of hydraulic binder materials based on mineral base, particularly, to production of portland cements. Method involves burning Portland cement raw meal in a reducing atmosphere and subsequent grinding Portland cement clinker to a specific surface Sss= 2800–3000 cm2/g with the addition of gypsum, is not greater than 3.5 % SO3. To form reducing medium inside clinker capsules during firing raw mixture coke additives are introduced into it in range of 3.5–4 wt. % over the weight of the crude mixture based on coke contained in the ash-slag wastes, which are an integral part of the components of the crude mixture of portland cement. Reduction gas medium formation during clinker annealing is controlled by air excess ratio of 1.05–1.10, annealing is carried out at temperature of 1450 °C for 30 minutes, rapid cooling of cement clinker is carried out in an aerated air-water medium.EFFECT: higher activity of cement, reduced consumption of process fuel and electric power, improved grinding capacity of cement clinker, increased service life of lining.1 cl, 1 tbl
Изобретение относится к технологии получения гидравлических вяжущих материалов на минеральной основе, в частности к технологии получения портландцементов. Способ включает обжиг портландцементной сырьевой смеси в восстановительной среде и дальнейший помол портландцементного клинкера до удельной поверхности Sуд=2800-3000 см2/г с добавлением гипса, не превышающим 3,5% по SO3. Для образования восстановительной среды внутри капсул клинкера при обжиге сырьевой смеси в нее вводят добавки кокса в пределах 3,5-4 мас. % сверх массы сырьевой смеси с учетом кокса, содержащегося в золошлаковых отходах, являющихся составной частью компонентов сырьевой смеси портландцемента. Образование восстановительной газовой среды при обжиге клинкера регулируется коэффициентом избытка воздуха 1,05-1,10, обжиг осуществляется при температуре 1450°С в течение 30 минут, быстрое охлаждение цементного клинкера производят в аэрированной воздушно-водной среде. Повышается активность цемента, снижается расход технологического топлива и электроэнергии, улучшается размалываемость цементного клинкера, увеличивается срок службы футеровки. 1 табл.
METHOD OF PRODUCING PORTLAND CEMENT
Способ получения портландцемента
AVAKYAN ARSEN GAJKOVICH (author) / PROTSENKO KIRILL DENISOVICH (author) / KAPLIEV MAKSIM EVGENEVICH (author)
2021-02-05
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME
PORTLAND CEMENT CLINKER, CEMENT COMPOSITION AND METHOD FOR PRODUCING PORTLAND CEMENT CLINKER
| European Patent Office | 2025
PORTLAND CEMENT CLINKER, CEMENT COMPOSITION, AND METHOD FOR PRODUCING PORTLAND CEMENT CLINKER
| European Patent Office | 2025
PORTLAND CEMENT CLINKER, CEMENT COMPOSITION, AND METHOD FOR PRODUCING PORTLAND CEMENT CLINKER
| European Patent Office | 2024
PORTLAND CEMENT CLINKER, CEMENT COMPOSITION AND METHOD FOR PRODUCING PORTLAND CEMENT CLINKER
| European Patent Office | 2024