Provided are a composite having improved composite brittleness and having a suitable thermal conductivity, and a method of manufacturing the composite. This aluminum-graphite-carbide composite is manufactured through the following steps. A step of mixing coke powder or a mixed powder of coke powder and graphite powder with any of a carbide powder, an oxide powder and a metal powder; a step of adding tar or pitch to the mixed powder obtained in the previous step to prepare a paste-like substance, extrusion molding the same and then performing primary firing by firing at 1,000 to 1,500°C to obtain a solid material; a step of subjecting the solid material obtained in the previous step repeatedly a plurality of times to impregnation with tar or pitch and to the step of performing primary firing by firing at 1,000°C to 1,500°C to obtain a solid material, and then performing final firing by firing at 2.500°C to 3,000°C to obtain an extrusion molding; and a step of using molten forging to pressure impregnate aluminum or an aluminum alloy into the extrusion molding obtained by the final firing.
Composite ayant une fragilité composite améliorée et ayant une conductibilité thermique appropriée, et procédé de fabrication du composite. Ce composite d'aluminium-graphite-carbure est fabriqué par le biais des étapes suivantes. Une étape de mélange de poudre de coke ou d'une poudre mixte de poudre de coke et de poudre de graphite avec l'une quelconque d'une poudre de carbure, d'une poudre d'oxyde et d'une poudre métallique ; une étape d'ajout de goudron ou de brai à la poudre mixte obtenue à l'étape précédente pour préparer une substance pâteuse, de moulage par extrusion de celle-ci puis de réalisation d'une cuisson primaire par cuisson de 1 000 à 1 500 °C pour obtenir un matériau solide ; une étape de soumission du matériau solide obtenu à l'étape précédente de manière répétée une pluralité de fois à une imprégnation avec du goudron ou du brai et à l'étape de cuisson primaire par cuisson de 1 000 °C à 1 500 °C pour obtenir un matériau solide, puis de réalisation d'une cuisson finale par cuisson de 2 500 °C à 3 000 °C pour obtenir un moulage par extrusion ; et une étape d'utilisation d'un forgeage en fusion pour imprégner par pression de l'aluminium ou un alliage d'aluminium dans le moulage par extrusion obtenu par la cuisson finale.
複合体の脆弱性を改善し、且つ、好適な熱伝導度を有する複合体と、その製造方法を提供する。 次の工程を経て製造されるアルミニウム－黒鉛－炭化物複合体。コークス粉末、又は、コークス粉末と黒鉛粉末との混合粉末と、炭化物粉末、酸化物粉末、金属粉粉末の何れかとを混合する工程、前記工程で得た混合粉にタール又はピッチを加えてペースト状の物質を作り、これを押出成形し、その後１，０００～１，５００℃にて焼成する一次焼成で固形物を得る工程、前記工程で得た固形物に対してタール又はピッチを含浸して１，０００～１，５００℃で焼成する一次焼成により固形物を得る工程を複数回繰り返し、２，５００～３，０００℃で焼成する最終焼成により押出成形体を得る工程、前記最終焼成により得た押出成形体に対して熔湯鍛造法によりアルミニウム又はアルミニウム合金を加圧含浸させる工程。
Provided are a composite having improved composite brittleness and having a suitable thermal conductivity, and a method of manufacturing the composite. This aluminum-graphite-carbide composite is manufactured through the following steps. A step of mixing coke powder or a mixed powder of coke powder and graphite powder with any of a carbide powder, an oxide powder and a metal powder; a step of adding tar or pitch to the mixed powder obtained in the previous step to prepare a paste-like substance, extrusion molding the same and then performing primary firing by firing at 1,000 to 1,500°C to obtain a solid material; a step of subjecting the solid material obtained in the previous step repeatedly a plurality of times to impregnation with tar or pitch and to the step of performing primary firing by firing at 1,000°C to 1,500°C to obtain a solid material, and then performing final firing by firing at 2.500°C to 3,000°C to obtain an extrusion molding; and a step of using molten forging to pressure impregnate aluminum or an aluminum alloy into the extrusion molding obtained by the final firing.
Composite ayant une fragilité composite améliorée et ayant une conductibilité thermique appropriée, et procédé de fabrication du composite. Ce composite d'aluminium-graphite-carbure est fabriqué par le biais des étapes suivantes. Une étape de mélange de poudre de coke ou d'une poudre mixte de poudre de coke et de poudre de graphite avec l'une quelconque d'une poudre de carbure, d'une poudre d'oxyde et d'une poudre métallique ; une étape d'ajout de goudron ou de brai à la poudre mixte obtenue à l'étape précédente pour préparer une substance pâteuse, de moulage par extrusion de celle-ci puis de réalisation d'une cuisson primaire par cuisson de 1 000 à 1 500 °C pour obtenir un matériau solide ; une étape de soumission du matériau solide obtenu à l'étape précédente de manière répétée une pluralité de fois à une imprégnation avec du goudron ou du brai et à l'étape de cuisson primaire par cuisson de 1 000 °C à 1 500 °C pour obtenir un matériau solide, puis de réalisation d'une cuisson finale par cuisson de 2 500 °C à 3 000 °C pour obtenir un moulage par extrusion ; et une étape d'utilisation d'un forgeage en fusion pour imprégner par pression de l'aluminium ou un alliage d'aluminium dans le moulage par extrusion obtenu par la cuisson finale.
複合体の脆弱性を改善し、且つ、好適な熱伝導度を有する複合体と、その製造方法を提供する。 次の工程を経て製造されるアルミニウム－黒鉛－炭化物複合体。コークス粉末、又は、コークス粉末と黒鉛粉末との混合粉末と、炭化物粉末、酸化物粉末、金属粉粉末の何れかとを混合する工程、前記工程で得た混合粉にタール又はピッチを加えてペースト状の物質を作り、これを押出成形し、その後１，０００～１，５００℃にて焼成する一次焼成で固形物を得る工程、前記工程で得た固形物に対してタール又はピッチを含浸して１，０００～１，５００℃で焼成する一次焼成により固形物を得る工程を複数回繰り返し、２，５００～３，０００℃で焼成する最終焼成により押出成形体を得る工程、前記最終焼成により得た押出成形体に対して熔湯鍛造法によりアルミニウム又はアルミニウム合金を加圧含浸させる工程。
ALUMINUM-GRAPHITE-CARBIDE COMPOSITE
COMPOSITE D'ALUMINIUM-GRAPHITE-CARBURE
アルミニウム－黒鉛－炭化物の複合体