RARE EARTH TANTALATE CERAMIC RESISTING CORROSION OF LOW MELTING POINT OXIDE AND PREPARATION METHOD THEREFOR
A rare earth tantalate ceramic resisting corrosion of a low melting point oxide. The chemical general formula of the ceramic is RETaO4. A preparation method of the ceramic comprises: taking RE2O3 powder and Ta2O5 powder and adding a solvent for mixing, and performing ball milling on the mixture by using a ball mill to obtain powder A; drying the powder A, and then performing primary sieving to obtain powder B; placing the powder B in a mold for compaction and then pre-sintering same to form a block C, performing grinding by a grinding machine after the block C is cooled to room temperature, and then performing secondary sieving to obtain powder D; and sintering the powder D to obtain the rare earth tantalate ceramic. The rare earth tantalate ceramic obtained by using the technical solution has a high compactness, and a strong capacity of resisting the corrosion of the low melting point oxide.
La présente invention concerne une céramique de tantalate de terre rare résistant à la corrosion d'un oxyde à bas point de fusion. La formule chimique générale de la céramique est RETaO4. Un procédé de préparation de la céramique consiste à : prendre de la poudre de RE2O3 et de la poudre de Ta2O5 et les ajouter à un solvant pour le mélange, et réaliser un broyage à billes sur le mélange à l'aide d'un broyeur à billes pour obtenir de la poudre A ; sécher la poudre A, puis effectuer un tamisage primaire pour obtenir la poudre B ; placer la poudre B dans un moule pour un compactage puis la pré-fritter pour former un bloc C, effectuer un meulage par une machine à meuler après que le bloc C a refroidi à température ambiante, puis effectuer un tamisage secondaire pour obtenir la poudre D ; et fritter la poudre D pour obtenir la céramique de tantalate de terres rares. La céramique de tantalate de terres rares obtenue en utilisant la solution technique a une compacité élevée, et une forte capacité de résistance à la corrosion de l'oxyde à bas point de fusion.
一种抗低熔点氧化物腐蚀的稀土钽酸盐陶瓷，该陶瓷的化学通式为RETaO 4，制备方法为：取RE 2O 3粉末和Ta 2O 5粉末，加入溶剂混合，采用球磨机进行球磨，得到粉末A；将粉末A干燥后进行第一次过筛，得到粉末B；将粉末B放置在模具内压实后进行预烧结，形成块体C，待块体C冷却至室温后采用研磨机进行研磨，后进行第二次过筛，得到粉末D；将粉末D烧结得到稀土钽酸盐陶瓷。采用该技术方案得到的稀土钽酸盐陶瓷致密度高，耐低熔点氧化物腐蚀能力强。
RARE EARTH TANTALATE CERAMIC RESISTING CORROSION OF LOW MELTING POINT OXIDE AND PREPARATION METHOD THEREFOR
A rare earth tantalate ceramic resisting corrosion of a low melting point oxide. The chemical general formula of the ceramic is RETaO4. A preparation method of the ceramic comprises: taking RE2O3 powder and Ta2O5 powder and adding a solvent for mixing, and performing ball milling on the mixture by using a ball mill to obtain powder A; drying the powder A, and then performing primary sieving to obtain powder B; placing the powder B in a mold for compaction and then pre-sintering same to form a block C, performing grinding by a grinding machine after the block C is cooled to room temperature, and then performing secondary sieving to obtain powder D; and sintering the powder D to obtain the rare earth tantalate ceramic. The rare earth tantalate ceramic obtained by using the technical solution has a high compactness, and a strong capacity of resisting the corrosion of the low melting point oxide.
La présente invention concerne une céramique de tantalate de terre rare résistant à la corrosion d'un oxyde à bas point de fusion. La formule chimique générale de la céramique est RETaO4. Un procédé de préparation de la céramique consiste à : prendre de la poudre de RE2O3 et de la poudre de Ta2O5 et les ajouter à un solvant pour le mélange, et réaliser un broyage à billes sur le mélange à l'aide d'un broyeur à billes pour obtenir de la poudre A ; sécher la poudre A, puis effectuer un tamisage primaire pour obtenir la poudre B ; placer la poudre B dans un moule pour un compactage puis la pré-fritter pour former un bloc C, effectuer un meulage par une machine à meuler après que le bloc C a refroidi à température ambiante, puis effectuer un tamisage secondaire pour obtenir la poudre D ; et fritter la poudre D pour obtenir la céramique de tantalate de terres rares. La céramique de tantalate de terres rares obtenue en utilisant la solution technique a une compacité élevée, et une forte capacité de résistance à la corrosion de l'oxyde à bas point de fusion.
一种抗低熔点氧化物腐蚀的稀土钽酸盐陶瓷，该陶瓷的化学通式为RETaO 4，制备方法为：取RE 2O 3粉末和Ta 2O 5粉末，加入溶剂混合，采用球磨机进行球磨，得到粉末A；将粉末A干燥后进行第一次过筛，得到粉末B；将粉末B放置在模具内压实后进行预烧结，形成块体C，待块体C冷却至室温后采用研磨机进行研磨，后进行第二次过筛，得到粉末D；将粉末D烧结得到稀土钽酸盐陶瓷。采用该技术方案得到的稀土钽酸盐陶瓷致密度高，耐低熔点氧化物腐蚀能力强。
RARE EARTH TANTALATE CERAMIC RESISTING CORROSION OF LOW MELTING POINT OXIDE AND PREPARATION METHOD THEREFOR
CÉRAMIQUE DE TANTALATE DE TERRE RARE RÉSISTANT À LA CORROSION D'OXYDE À BAS POINT DE FUSION ET PROCÉDÉ DE PRÉPARATION ASSOCIÉ
一种抗低熔点氧化物腐蚀的稀土钽酸盐陶瓷及其制备方法
FENG JING (author) / CHONG XIAOYU (author)
2020-10-29
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2022
| European Patent Office | 2021
HIGH-ENTROPY RARE EARTH-TOUGHENED TANTALATE CERAMIC AND PREPARATION METHOD THEREFOR
| European Patent Office | 2020
HIGH-ENTROPY RARE EARTH-TOUGHENED TANTALATE CERAMIC AND PREPARATION METHOD THEREFOR
| European Patent Office | 2022
HIGH-ENTROPY RARE EARTH-TOUGHENED TANTALATE CERAMIC AND PREPARATION METHOD THEREFOR
| European Patent Office | 2022