MANGANESE-ZINC FERRITE MATERIAL HAVING SUPER-HIGH SATURATION MAGNETIC FLUX DENSITY AND PREPARATION METHOD THEREFOR
A manganese-zinc ferrite material having super-high saturation magnetic flux density and a preparation method therefor. The main components of soft magnetic ferrite are composed of Fe2O3, ZnO, Co2O3 and MnO; the auxiliary components thereof comprise Nb2O5, CaCO3, NiO, V2O5, SiO2, Ta2O5, and TiO2. The processing steps thereof comprise batching, pre-sintering, sanding, granulating, molding, and sintering. Said sintering employs two-stage heat preservation balancing oxygen partial pressure sintering; the sintering temperature in the first stage is 1200-1240°C, the heat preservation time is 4-8 h, the oxygen content in the first 0-1 h is 3.5-4%, and the oxygen content at a subsequent heat preservation time is 2.0-3.0%; the temperature of a cooling section in the first stage is 1050-1100°C, and the heat preservation time is 30-100 min. The described material has excellent characteristics such as high frequency, wide temperature range, low loss, high saturation magnetic flux density, and so on, thus meeting the high performance requirements of flat transformers, server inductors, and so on for ferrite materials.
L'invention concerne un matériau de ferrite de manganèse-zinc présentant une densité de flux magnétique à saturation très élevée et son procédé de préparation. Les composants principaux de ferrite magnétique souple sont composés de Fe2O3, ZnO, Co2O3 et MnO ; les composants auxiliaires de ceux-ci comprennent Nb2O5, CaCO3, NiO, V2O5, SiO2, Ta2O5, et TiO2. Les étapes de traitement comprennent le dosage, le pré-frittage, le sablage, la granulation, le moulage et le frittage. Ledit frittage utilise une conservation de chaleur en deux étapes équilibrant le frittage sous pression partielle d'oxygène ; la température de frittage dans la première étape est de 1200 à 1240 °C, le temps de conservation de chaleur est de 4 à 8 h, la teneur en oxygène dans la première 0 à 1 h est de 3,5 à 4 %, et la teneur en oxygène à un temps de conservation de chaleur ultérieur est de 2,0 à 3,0 % ; la température d'une section de refroidissement dans la première étape est de 1050 à 1100 °C, et le temps de conservation de la chaleur est de 30 à 100 min. Le matériau décrit présente d'excellentes caractéristiques telles qu'une fréquence élevée, une large gamme de températures, une faible perte, une densité de flux magnétique de saturation élevée, etc., répondant ainsi aux exigences de haute performance des transformateurs plats, des inductances de serveur, etc. pour les matériaux de ferrite.
一种超高饱和磁通密度锰锌铁氧体材料及其制备方法，所述软磁铁氧体主成份由Fe 2O 3、ZnO、Co 2O 3和MnO组成；副成分包括Nb 2O 5、CaCO 3、NiO、V 2O 5、SiO 2、Ta 2O 5、TiO 2。其工艺步骤为配料、预烧、砂磨、造粒、成型、烧结。其中烧结采用二段保温平衡氧分压烧结法，一段烧结温度为1200～1240℃，保温时间为4～8h，前0～1h氧含量为3.5～4％，后面保温时间氧含量为2.0～3.0％；一段在降温段温度为1050～1100℃，保温时间30～100min。该材料具有高频宽温低损耗、高饱和磁通密度等优良特性，以满足平板变压器和服务器电感等对铁氧体材料高性能要求。
MANGANESE-ZINC FERRITE MATERIAL HAVING SUPER-HIGH SATURATION MAGNETIC FLUX DENSITY AND PREPARATION METHOD THEREFOR
A manganese-zinc ferrite material having super-high saturation magnetic flux density and a preparation method therefor. The main components of soft magnetic ferrite are composed of Fe2O3, ZnO, Co2O3 and MnO; the auxiliary components thereof comprise Nb2O5, CaCO3, NiO, V2O5, SiO2, Ta2O5, and TiO2. The processing steps thereof comprise batching, pre-sintering, sanding, granulating, molding, and sintering. Said sintering employs two-stage heat preservation balancing oxygen partial pressure sintering; the sintering temperature in the first stage is 1200-1240°C, the heat preservation time is 4-8 h, the oxygen content in the first 0-1 h is 3.5-4%, and the oxygen content at a subsequent heat preservation time is 2.0-3.0%; the temperature of a cooling section in the first stage is 1050-1100°C, and the heat preservation time is 30-100 min. The described material has excellent characteristics such as high frequency, wide temperature range, low loss, high saturation magnetic flux density, and so on, thus meeting the high performance requirements of flat transformers, server inductors, and so on for ferrite materials.
L'invention concerne un matériau de ferrite de manganèse-zinc présentant une densité de flux magnétique à saturation très élevée et son procédé de préparation. Les composants principaux de ferrite magnétique souple sont composés de Fe2O3, ZnO, Co2O3 et MnO ; les composants auxiliaires de ceux-ci comprennent Nb2O5, CaCO3, NiO, V2O5, SiO2, Ta2O5, et TiO2. Les étapes de traitement comprennent le dosage, le pré-frittage, le sablage, la granulation, le moulage et le frittage. Ledit frittage utilise une conservation de chaleur en deux étapes équilibrant le frittage sous pression partielle d'oxygène ; la température de frittage dans la première étape est de 1200 à 1240 °C, le temps de conservation de chaleur est de 4 à 8 h, la teneur en oxygène dans la première 0 à 1 h est de 3,5 à 4 %, et la teneur en oxygène à un temps de conservation de chaleur ultérieur est de 2,0 à 3,0 % ; la température d'une section de refroidissement dans la première étape est de 1050 à 1100 °C, et le temps de conservation de la chaleur est de 30 à 100 min. Le matériau décrit présente d'excellentes caractéristiques telles qu'une fréquence élevée, une large gamme de températures, une faible perte, une densité de flux magnétique de saturation élevée, etc., répondant ainsi aux exigences de haute performance des transformateurs plats, des inductances de serveur, etc. pour les matériaux de ferrite.
一种超高饱和磁通密度锰锌铁氧体材料及其制备方法，所述软磁铁氧体主成份由Fe 2O 3、ZnO、Co 2O 3和MnO组成；副成分包括Nb 2O 5、CaCO 3、NiO、V 2O 5、SiO 2、Ta 2O 5、TiO 2。其工艺步骤为配料、预烧、砂磨、造粒、成型、烧结。其中烧结采用二段保温平衡氧分压烧结法，一段烧结温度为1200～1240℃，保温时间为4～8h，前0～1h氧含量为3.5～4％，后面保温时间氧含量为2.0～3.0％；一段在降温段温度为1050～1100℃，保温时间30～100min。该材料具有高频宽温低损耗、高饱和磁通密度等优良特性，以满足平板变压器和服务器电感等对铁氧体材料高性能要求。
MANGANESE-ZINC FERRITE MATERIAL HAVING SUPER-HIGH SATURATION MAGNETIC FLUX DENSITY AND PREPARATION METHOD THEREFOR
MATÉRIAU DE FERRITE DE MANGANÈSE-ZINC PRÉSENTANT UNE DENSITÉ DE FLUX MAGNÉTIQUE À SATURATION TRÈS ÉLEVÉE ET SON PROCÉDÉ DE PRÉPARATION
一种超高饱和磁通密度锰锌铁氧体材料及其制备方法
ZHANG QIANGYUAN (author) / XING BINGBING (author) / SONG YANYAN (author) / MIU SIMIN (author) / JIAO SHUAISHUAI (author) / ZHANG ZHIXIN (author) / LI XIAOLONG (author)
2021-07-01
Patent
Electronic Resource
Chinese
| European Patent Office | 2023
Manganese zinc ferrite material with high saturation magnetic flux density and low loss
| European Patent Office | 2022
Ultrahigh saturation flux density manganese-zinc ferrite material and preparation method thereof
| European Patent Office | 2020
Manganese zinc ferrite with high saturation magnetic flux density and preparation method thereof
| European Patent Office | 2015
| European Patent Office | 2021