METHOD FOR PREPARING γ-TYPE DICALCIUM SILICATE AND HIGH-STRENGTH CARBONIZED MATERIAL COMPOSED OF γ-TYPE DICALCIUM SILICATE AS MAIN PHASE
The present invention belongs to the field of building materials, and particularly relates to a method for preparing a γ-type dicalcium silicate and a high-strength carbonized material composed of the γ-type dicalcium silicate as the main phase. The method for preparing a γ-type dicalcium silicate of the present invention comprises the following steps: (1) mixing a calcareous raw material with a siliceous raw material in a molar ratio of calcium to silicon of 2 : 1 until uniform, then adding deionized water and intensively mixing same until uniform to obtain a mixture, pressing the mixture with a tablet press into tablets, and drying same in a vacuum drying oven, so as to obtain sample tablets; and (2) putting the sample tablets into a microwave sintering furnace, heating same to a first temperature, maintaining the temperature for 30 min, then heating same to a second temperature, maintaining the temperature, and cooling same to obtain a γ-type dicalcium silicate. According to the method of the present invention, a reaction is carried out at a temperature lower than that of a traditional sintering method, a high-quality product, γ-C2S, is obtained, the production energy consumption is reduced, and the method has an important industrial application value.
La présente invention appartient au domaine des matériaux de construction, et concerne en particulier un procédé de préparation d'un silicate dicalcique de type γ et d'un matériau carbonisé de haute résistance composé du silicate dicalcique de type γ en tant que phase principale. Le procédé de préparation d'un silicate dicalcique de type γ selon la présente invention comprend les étapes suivantes consistant à : (1) mélanger une matière première calcaire avec une matière première siliceuse dans un rapport molaire calcium sur silicium de 2 : 1 jusqu'à uniformité, puis ajouter de l'eau désionisée et mélanger de manière intense jusqu'à uniformité pour obtenir un mélange, presser le mélange avec une presse à comprimés en comprimés, et sécher les comprimés dans un four de séchage sous vide, de façon à obtenir des comprimés d'échantillon; et (2) mettre les comprimés d'échantillon dans un four de frittage par micro-ondes, les chauffer à une première température, maintenir la température pendant 30 min, puis les chauffer à une seconde température, maintenir la température, et refroidir les comprimés pour obtenir un silicate dicalcique de type γ. Selon le procédé de la présente invention, une réaction est effectuée à une température inférieure à celle d'un procédé de frittage classique, un produit de haute qualité, γ-C2S, est obtenu, la consommation d'énergie de production est réduite, et le procédé a une valeur d'application industrielle importante.
本发明属于建筑材料领域，特别涉及一种γ型硅酸二钙的制备方法及一种以γ型硅酸二钙为主要物相组成的高强碳化材料。本发明的γ型硅酸二钙的制备方法，包括以下步骤：（1）将钙质原料与硅质原料按钙与硅的摩尔比为2：1混合均匀，然后加去离子水充分混合均匀，得混合料，使用压片机将混合料压制成片，于真空干燥箱中干燥，得到样片；（2）将样片置于微波烧结炉中，加热至第一温度，保温30min，然后再加热至第二温度，保温，冷却，即得γ型硅酸二钙。本发明的方法实现反应在较传统烧结法低的温度下进行，获得高质量的产物γ-C 2S，降低生产能耗，具有重要的工业应用价值。
METHOD FOR PREPARING γ-TYPE DICALCIUM SILICATE AND HIGH-STRENGTH CARBONIZED MATERIAL COMPOSED OF γ-TYPE DICALCIUM SILICATE AS MAIN PHASE
The present invention belongs to the field of building materials, and particularly relates to a method for preparing a γ-type dicalcium silicate and a high-strength carbonized material composed of the γ-type dicalcium silicate as the main phase. The method for preparing a γ-type dicalcium silicate of the present invention comprises the following steps: (1) mixing a calcareous raw material with a siliceous raw material in a molar ratio of calcium to silicon of 2 : 1 until uniform, then adding deionized water and intensively mixing same until uniform to obtain a mixture, pressing the mixture with a tablet press into tablets, and drying same in a vacuum drying oven, so as to obtain sample tablets; and (2) putting the sample tablets into a microwave sintering furnace, heating same to a first temperature, maintaining the temperature for 30 min, then heating same to a second temperature, maintaining the temperature, and cooling same to obtain a γ-type dicalcium silicate. According to the method of the present invention, a reaction is carried out at a temperature lower than that of a traditional sintering method, a high-quality product, γ-C2S, is obtained, the production energy consumption is reduced, and the method has an important industrial application value.
La présente invention appartient au domaine des matériaux de construction, et concerne en particulier un procédé de préparation d'un silicate dicalcique de type γ et d'un matériau carbonisé de haute résistance composé du silicate dicalcique de type γ en tant que phase principale. Le procédé de préparation d'un silicate dicalcique de type γ selon la présente invention comprend les étapes suivantes consistant à : (1) mélanger une matière première calcaire avec une matière première siliceuse dans un rapport molaire calcium sur silicium de 2 : 1 jusqu'à uniformité, puis ajouter de l'eau désionisée et mélanger de manière intense jusqu'à uniformité pour obtenir un mélange, presser le mélange avec une presse à comprimés en comprimés, et sécher les comprimés dans un four de séchage sous vide, de façon à obtenir des comprimés d'échantillon; et (2) mettre les comprimés d'échantillon dans un four de frittage par micro-ondes, les chauffer à une première température, maintenir la température pendant 30 min, puis les chauffer à une seconde température, maintenir la température, et refroidir les comprimés pour obtenir un silicate dicalcique de type γ. Selon le procédé de la présente invention, une réaction est effectuée à une température inférieure à celle d'un procédé de frittage classique, un produit de haute qualité, γ-C2S, est obtenu, la consommation d'énergie de production est réduite, et le procédé a une valeur d'application industrielle importante.
本发明属于建筑材料领域，特别涉及一种γ型硅酸二钙的制备方法及一种以γ型硅酸二钙为主要物相组成的高强碳化材料。本发明的γ型硅酸二钙的制备方法，包括以下步骤：（1）将钙质原料与硅质原料按钙与硅的摩尔比为2：1混合均匀，然后加去离子水充分混合均匀，得混合料，使用压片机将混合料压制成片，于真空干燥箱中干燥，得到样片；（2）将样片置于微波烧结炉中，加热至第一温度，保温30min，然后再加热至第二温度，保温，冷却，即得γ型硅酸二钙。本发明的方法实现反应在较传统烧结法低的温度下进行，获得高质量的产物γ-C 2S，降低生产能耗，具有重要的工业应用价值。
METHOD FOR PREPARING γ-TYPE DICALCIUM SILICATE AND HIGH-STRENGTH CARBONIZED MATERIAL COMPOSED OF γ-TYPE DICALCIUM SILICATE AS MAIN PHASE
PROCÉDÉ DE PRÉPARATION D'UN SILICATE DICALCIQUE DE TYPE γ ET D'UN MATÉRIAU CARBONISÉ DE HAUTE RÉSISTANCE COMPOSÉ DE SILICATE DICALCIQUE DE TYPE γ EN TANT QUE PHASE PRINCIPALE
一种γ型硅酸二钙的制备方法及以γ型硅酸二钙为主要物相组成的高强碳化材料
LUO SHUQIONG (author) / ZHAO MINGHUI (author) / LIU SONGHUI (author) / JIANG ZHUANGZHUANG (author) / YANG LEI (author) / PAN CHONGGEN (author) / MAO YUXIANG (author) / ZHANG HAIBO (author) / WANG YULI (author) / GUAN XUEMAO (author)
2022-01-27
Patent
Electronic Resource
Chinese
| European Patent Office | 2022
Dicalcium silicate doped with sulfur
| Online Contents | 2012
The system dicalcium silicate-calcium fluoride
| TIBKAT | 1966
Method for preparing amorphous nano dicalcium silicate by hydrothermal method
| European Patent Office | 2021