HIGH-STRENGTH CONCRETE AND PREPARATION METHOD THEREFOR
Provided are high-strength concrete and a preparation method therefor. The concrete comprises lignin, regenerated micropowder, cement, water, sand, gravel, and a water reducing agent. The regenerated micropowder is regenerated micropowder of waste concrete, and the preparation method comprises: separating solid construction waste, then performing impurity removal and crushing processing, and using a ball mill to grind the solid construction waste into dust having a particle size of less than 0.16 mm. The lignin is waste wood lignin, and the extraction method comprises: crushing wood, using a sodium hydroxide aqueous solution having a mass concentration of 5% to stir and extract at 80°C for 1-2 hours to obtain a black lignin alkaline solution, adding a hydrochloric acid solution having a mass concentration of 30% into the alkaline solution for stirring to reduce the pH to 7.0, and standing for layering to obtain the lignin. The strength grade of the concrete is remarkably improved, and the recycling of the construction waste is also achieved.
L'invention concerne un béton hautement résistant et un procédé de fabrication associé. Le béton comprend de la lignine, une micropoudre régénérée, du ciment, de l'eau, du sable, du gravier et un agent de réduction de l'eau. La micropoudre régénérée est une micropoudre régénérée de béton usagé et le procédé de préparation consiste à : séparer les déchets de construction solides, puis réaliser une élimination d'impuretés et un traitement de broyage et utiliser un broyeur à boulets pour broyer les déchets de construction solides en une poussière présentant une grosseur de particule inférieure à 0,16 mm. La lignine est la lignine de bois de rebut et le procédé d'extraction consiste à : broyer le bois, utiliser une solution aqueuse d'hydroxyde de sodium présentant une concentration massique de 5 % pour agiter et extraire à 80 °C pendant 1 à 2 heures pour obtenir une solution alcaline de lignine noire, ajouter une solution d'acide chlorhydrique présentant une concentration massique de 30 % dans la solution alcaline pour une agitation en vue de réduire le pH à 7,0, et laisser au repos pour la stratification pour obtenir la lignine. Le grade de résistance du béton est remarquablement amélioré et le recyclage des déchets de construction est également obtenu.
提供一种高强度混凝土及其制备方法。该混凝土包括木质素、再生微粉、水泥、水、沙子、碎石和减水剂；其中，再生微粉为废弃混凝土的再生微粉，制备方法为：将废弃建筑固体垃圾分离后进行除杂、破碎加工、再经过球磨机研磨为粒径小于0.16mm的粉尘；木质素为废弃木材木质素，提取方法为：将木材粉碎，用质量浓度为5％的氢氧化钠水溶液，在80℃下搅拌提取1-2小时，得到黑色的木质素碱溶液，向碱溶液中加入质量浓度为30％的盐酸溶液并搅拌，使pH降低到7.0，静置分层后获得。该混凝土不仅强度等级显著提高，还实现了建筑垃圾的循环再利用。
HIGH-STRENGTH CONCRETE AND PREPARATION METHOD THEREFOR
Provided are high-strength concrete and a preparation method therefor. The concrete comprises lignin, regenerated micropowder, cement, water, sand, gravel, and a water reducing agent. The regenerated micropowder is regenerated micropowder of waste concrete, and the preparation method comprises: separating solid construction waste, then performing impurity removal and crushing processing, and using a ball mill to grind the solid construction waste into dust having a particle size of less than 0.16 mm. The lignin is waste wood lignin, and the extraction method comprises: crushing wood, using a sodium hydroxide aqueous solution having a mass concentration of 5% to stir and extract at 80°C for 1-2 hours to obtain a black lignin alkaline solution, adding a hydrochloric acid solution having a mass concentration of 30% into the alkaline solution for stirring to reduce the pH to 7.0, and standing for layering to obtain the lignin. The strength grade of the concrete is remarkably improved, and the recycling of the construction waste is also achieved.
L'invention concerne un béton hautement résistant et un procédé de fabrication associé. Le béton comprend de la lignine, une micropoudre régénérée, du ciment, de l'eau, du sable, du gravier et un agent de réduction de l'eau. La micropoudre régénérée est une micropoudre régénérée de béton usagé et le procédé de préparation consiste à : séparer les déchets de construction solides, puis réaliser une élimination d'impuretés et un traitement de broyage et utiliser un broyeur à boulets pour broyer les déchets de construction solides en une poussière présentant une grosseur de particule inférieure à 0,16 mm. La lignine est la lignine de bois de rebut et le procédé d'extraction consiste à : broyer le bois, utiliser une solution aqueuse d'hydroxyde de sodium présentant une concentration massique de 5 % pour agiter et extraire à 80 °C pendant 1 à 2 heures pour obtenir une solution alcaline de lignine noire, ajouter une solution d'acide chlorhydrique présentant une concentration massique de 30 % dans la solution alcaline pour une agitation en vue de réduire le pH à 7,0, et laisser au repos pour la stratification pour obtenir la lignine. Le grade de résistance du béton est remarquablement amélioré et le recyclage des déchets de construction est également obtenu.
提供一种高强度混凝土及其制备方法。该混凝土包括木质素、再生微粉、水泥、水、沙子、碎石和减水剂；其中，再生微粉为废弃混凝土的再生微粉，制备方法为：将废弃建筑固体垃圾分离后进行除杂、破碎加工、再经过球磨机研磨为粒径小于0.16mm的粉尘；木质素为废弃木材木质素，提取方法为：将木材粉碎，用质量浓度为5％的氢氧化钠水溶液，在80℃下搅拌提取1-2小时，得到黑色的木质素碱溶液，向碱溶液中加入质量浓度为30％的盐酸溶液并搅拌，使pH降低到7.0，静置分层后获得。该混凝土不仅强度等级显著提高，还实现了建筑垃圾的循环再利用。
HIGH-STRENGTH CONCRETE AND PREPARATION METHOD THEREFOR
BÉTON HAUTEMENT RÉSISTANT ET PROCÉDÉ DE PRÉPARATION ASSOCIÉ
一种高强度混凝土及其制备方法
WU KE (author) / YANG HONGNA (author) / LI GUODONG (author) / CHEN RONG (author) / ZHAO JIAHUI (author) / HAO DONGXUE (author) / HAN YUCONG (author) / ZHENG YANG (author) / SUN JIE (author)
2022-02-10
Patent
Electronic Resource
Chinese
HIGH-STRENGTH CORAL CONCRETE AND PREPARATION METHOD THEREFOR
| European Patent Office | 2021
Ultra-high strength active powder concrete and preparation method therefor
| European Patent Office | 2015
Early-strength ceramsite aerated concrete block and preparation method therefor
| European Patent Office | 2015
| European Patent Office | 2020