METHOD FOR PREPARING ARTIFICIAL STONE USING IRON-CONTAINING SLAG OBTAINED FROM PYROMETALLURGY
The present invention relates to the technical field of the energy-saving, environment-friendly and efficient utilization of iron-containing slag obtained from pyrometallurgy, and provides a method for preparing an artificial stone using iron-containing slag obtained from pyrometallurgy. The method comprises: adding a modifier having a mass percentage of 0.1-10% to iron-containing slag obtained from pyrometallurgy, without additional heating, wherein the alkali metal oxide-containing modifier is directly molten using the residual heat of the slag, or slag atmosphere is controlled by means of simultaneous auxiliary gas blowing; preserving the heat of the modified slag for 10-60 min at a temperature higher than 1150°C for shaping, and performing heat treatment to form an artificial stone, wherein the main crystal phase in the artificial stone is magnetite, and the mass percentages of the components of the artificial stone are: 0.5%<8%; and 25%
La présente invention concerne le domaine technique de l'utilisation énergétiquement économe, respectueuse de l'environnement et efficace de scories contenant du fer obtenues à partir de la pyrométallurgie et concerne un procédé de préparation d'une pierre artificielle à l'aide de scories contenant du fer obtenues à partir de la pyrométallurgie. Le procédé consiste à : ajouter un modificateur présentant un pourcentage en masse de 0,1-10 % à des scories contenant du fer obtenu à partir de la pyrométallurgie, sans chauffage supplémentaire, le modificateur contenant de l'oxyde de métal alcalin étant directement fondu à l'aide de la chaleur résiduelle des scories ou l'atmosphère des scories étant régulée au moyen d'un soufflage simultané de gaz auxiliaire ; maintenir la chaleur des scories modifiées pendant 10-60 min à une température supérieure à 1150°C pour la mise en forme et effectuer un traitement thermique pour former une pierre artificielle, la phase cristalline principale dans la pierre artificielle étant la magnétite et les pourcentages en masse des constituants de la pierre artificielle étant : 0,5 % < Na2O+K2O < 8 % ; et 25 % < Fe2O3 < 65 %. La pierre artificielle de la présente invention est une pierre de granit artificiel noire, un produit courant de pierre coulée résistant à l'usure et résistant à la corrosion ou un matériau céramique fonctionnel contenant de la magnétite.
本发明提供一种采用火法冶炼得到的含铁熔渣制备人造石材的方法，属于火法冶炼得到的含铁熔渣节能环保高效利用的技术领域。该方法是在火法冶炼得到的含铁熔渣中添加质量百分含量为0.1～10％的改质剂，不需要额外加热，利用熔渣余热直接熔解含碱金属氧化物的改质剂，或者同时辅助喷吹气体方式来控制熔渣气氛；改质后熔渣在高于1150℃温度下保温10～60min后进行成型，并经过热处理形成人造石材；所述人造石材中的主晶相为磁铁矿，所述人造石材成分的质量百分含量为：0.5％<8％；25％<65％。本发明的人造石材为黑色人造花岗岩石材、普通耐磨耐腐蚀的铸石制品或含磁铁矿的功能性陶瓷材料。
METHOD FOR PREPARING ARTIFICIAL STONE USING IRON-CONTAINING SLAG OBTAINED FROM PYROMETALLURGY
The present invention relates to the technical field of the energy-saving, environment-friendly and efficient utilization of iron-containing slag obtained from pyrometallurgy, and provides a method for preparing an artificial stone using iron-containing slag obtained from pyrometallurgy. The method comprises: adding a modifier having a mass percentage of 0.1-10% to iron-containing slag obtained from pyrometallurgy, without additional heating, wherein the alkali metal oxide-containing modifier is directly molten using the residual heat of the slag, or slag atmosphere is controlled by means of simultaneous auxiliary gas blowing; preserving the heat of the modified slag for 10-60 min at a temperature higher than 1150°C for shaping, and performing heat treatment to form an artificial stone, wherein the main crystal phase in the artificial stone is magnetite, and the mass percentages of the components of the artificial stone are: 0.5%<8%; and 25%
La présente invention concerne le domaine technique de l'utilisation énergétiquement économe, respectueuse de l'environnement et efficace de scories contenant du fer obtenues à partir de la pyrométallurgie et concerne un procédé de préparation d'une pierre artificielle à l'aide de scories contenant du fer obtenues à partir de la pyrométallurgie. Le procédé consiste à : ajouter un modificateur présentant un pourcentage en masse de 0,1-10 % à des scories contenant du fer obtenu à partir de la pyrométallurgie, sans chauffage supplémentaire, le modificateur contenant de l'oxyde de métal alcalin étant directement fondu à l'aide de la chaleur résiduelle des scories ou l'atmosphère des scories étant régulée au moyen d'un soufflage simultané de gaz auxiliaire ; maintenir la chaleur des scories modifiées pendant 10-60 min à une température supérieure à 1150°C pour la mise en forme et effectuer un traitement thermique pour former une pierre artificielle, la phase cristalline principale dans la pierre artificielle étant la magnétite et les pourcentages en masse des constituants de la pierre artificielle étant : 0,5 % < Na2O+K2O < 8 % ; et 25 % < Fe2O3 < 65 %. La pierre artificielle de la présente invention est une pierre de granit artificiel noire, un produit courant de pierre coulée résistant à l'usure et résistant à la corrosion ou un matériau céramique fonctionnel contenant de la magnétite.
本发明提供一种采用火法冶炼得到的含铁熔渣制备人造石材的方法，属于火法冶炼得到的含铁熔渣节能环保高效利用的技术领域。该方法是在火法冶炼得到的含铁熔渣中添加质量百分含量为0.1～10％的改质剂，不需要额外加热，利用熔渣余热直接熔解含碱金属氧化物的改质剂，或者同时辅助喷吹气体方式来控制熔渣气氛；改质后熔渣在高于1150℃温度下保温10～60min后进行成型，并经过热处理形成人造石材；所述人造石材中的主晶相为磁铁矿，所述人造石材成分的质量百分含量为：0.5％<8％；25％<65％。本发明的人造石材为黑色人造花岗岩石材、普通耐磨耐腐蚀的铸石制品或含磁铁矿的功能性陶瓷材料。
METHOD FOR PREPARING ARTIFICIAL STONE USING IRON-CONTAINING SLAG OBTAINED FROM PYROMETALLURGY
PROCÉDÉ DE PRÉPARATION DE PIERRE ARTIFICIELLE À L'AIDE DE SCORIES CONTENANT DU FER OBTENUES À PARTIR DE LA PYROMÉTALLURGIE
一种采用火法冶炼得到的含铁熔渣制备人造石材的方法
LI YU (author) / WANG HONGYU (author) / CHEN KUIYUAN (author) / ZHAO XINYU (author)
2022-04-07
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Method for preparing artificial synthetic stone slab by using nickel smelting slag
| European Patent Office | 2022
Method for preparing artificial decorative stone by using manganese-silicon alloy hot melting slag
| European Patent Office | 2021
Equipment and method for preparing stone from blast furnace slag
| European Patent Office | 2023
Artificial stone manufactured from waste slag and manufacturing method thereof
| European Patent Office | 2023
Method for preparing high-quality raw material from iron-containing smelting slag
| European Patent Office | 2022