METHOD FOR REDUCING FREE CALCIUM OXIDE IN STEEL SLAG BY USING FERRONICKEL SLAG, AND APPLICATION THEREOF
Disclosed in the present invention are a method for reducing free calcium oxide in steel slag by using ferronickel slag, and an application thereof. In the method, ferronickel slag and steel slag are mixed and reacted in a hot melting condition by means of waste heat after smelting, without the need of external heat, wherein the mass ratio of the ferronickel slag to the steel slag is 1:0.6-4, and at least one of the ferronickel slag and the steel slag is in a molten state. Compared with the prior art, the present invention has the following advantages: (1) the problem of high f-CaO content in converter steel slag is solved, and the f-CaO content in steel slag treated by ferronickel slag can be controlled to be 3% or below, thus achieving the purpose of reducing swelling thereof in contact with water, and making mixed steel slag more stable and durable in the field of building materials or directly applicable to the building materials industry and the field of road and bridge construction; (2) the use thereof can also be expanded to reduce f-CaO in other metallurgical slag, mixed treatment of two or more types of slag is not excluded, other components can also be added in the mixing process in addition to metallurgical slag, and the content of f-CaO in the metallurgical slag is reduced by means of the incompactness and the low calcium property of the ferronickel slag.
Un procédé de réduction d'oxyde de calcium libre dans un laitier d'acier à l'aide de laitier de ferronickel, et une application de associée, sont divulgués dans la présente invention. Dans le procédé, le laitier de ferronickel et le laitier d'acier sont mélangés et mis à réagir dans un état de fusion à chaud au moyen de la chaleur perdue après fusion, sans nécessiter de chaleur externe, le rapport en masse du laitier de ferronickel au laitier d'acier étant de 1:0,6 à 4, et le laitier de ferronickel et/ou le laitier d'acier étant à l'état fondu. Par rapport à l'état de la technique, la présente invention a les avantages suivants : (1) le problème de teneur élevée en f-CaO dans le laitier d'acier de convertisseur est résolu, et la teneur en f-CaO dans le laitier d'acier traité par le laitier de ferronickel peut être régulée à 3 % ou moins, ce qui permet de réduire le gonflement de ce dernier en contact avec l'eau, et la fabrication de laitier d'acier mixte plus stable et durable dans le domaine des matériaux de construction ou directement applicable à l'industrie des matériaux de construction et au domaine de la construction de routes et de ponts ; (2) son utilisation peut également être étendue pour réduire le f-CaO dans un autre laitier métallurgique, un traitement mixte d'au moins deux types de laitiers n'est pas exclu, d'autres constituants peuvent également être ajoutés lors du processus de mélange en plus du laitier métallurgique, et la teneur en f-CaO dans le laitier métallurgique est réduite au moyen de l'incompacité et de la faible propriété calcique du laitier de ferronickel.
本发明公开了利用镍铁渣降低钢渣中游离氧化钙的方法及其应用，所述方法将镍铁渣和钢渣利用冶炼后的余温在热熔条件下混合反应，无需外部热量；其中，镍铁渣和钢渣的质量比为1:0.6-4，且二者至少一种为熔融状态。与现有技术相比，本发明具有以下优点：(1)解决了转炉钢渣中f-CaO含量较高的问题，经过镍铁渣处理的钢渣中f-CaO含量能够控制在3％以下，从而实现其遇水膨胀性减小的目的，使得混合钢渣在建材领域更加稳定耐用，或可直接应用于建材行业和路桥建设领域；(2)其还可衍生到降低其余冶金渣中的f-CaO，不排除两种以上渣混合处理，也不排除在混合过程中除了添加冶金渣，还可添加其它组份，但是其均是利用镍铁渣的松散性和低钙性来降低冶金渣中f-CaO的含量。
METHOD FOR REDUCING FREE CALCIUM OXIDE IN STEEL SLAG BY USING FERRONICKEL SLAG, AND APPLICATION THEREOF
Disclosed in the present invention are a method for reducing free calcium oxide in steel slag by using ferronickel slag, and an application thereof. In the method, ferronickel slag and steel slag are mixed and reacted in a hot melting condition by means of waste heat after smelting, without the need of external heat, wherein the mass ratio of the ferronickel slag to the steel slag is 1:0.6-4, and at least one of the ferronickel slag and the steel slag is in a molten state. Compared with the prior art, the present invention has the following advantages: (1) the problem of high f-CaO content in converter steel slag is solved, and the f-CaO content in steel slag treated by ferronickel slag can be controlled to be 3% or below, thus achieving the purpose of reducing swelling thereof in contact with water, and making mixed steel slag more stable and durable in the field of building materials or directly applicable to the building materials industry and the field of road and bridge construction; (2) the use thereof can also be expanded to reduce f-CaO in other metallurgical slag, mixed treatment of two or more types of slag is not excluded, other components can also be added in the mixing process in addition to metallurgical slag, and the content of f-CaO in the metallurgical slag is reduced by means of the incompactness and the low calcium property of the ferronickel slag.
Un procédé de réduction d'oxyde de calcium libre dans un laitier d'acier à l'aide de laitier de ferronickel, et une application de associée, sont divulgués dans la présente invention. Dans le procédé, le laitier de ferronickel et le laitier d'acier sont mélangés et mis à réagir dans un état de fusion à chaud au moyen de la chaleur perdue après fusion, sans nécessiter de chaleur externe, le rapport en masse du laitier de ferronickel au laitier d'acier étant de 1:0,6 à 4, et le laitier de ferronickel et/ou le laitier d'acier étant à l'état fondu. Par rapport à l'état de la technique, la présente invention a les avantages suivants : (1) le problème de teneur élevée en f-CaO dans le laitier d'acier de convertisseur est résolu, et la teneur en f-CaO dans le laitier d'acier traité par le laitier de ferronickel peut être régulée à 3 % ou moins, ce qui permet de réduire le gonflement de ce dernier en contact avec l'eau, et la fabrication de laitier d'acier mixte plus stable et durable dans le domaine des matériaux de construction ou directement applicable à l'industrie des matériaux de construction et au domaine de la construction de routes et de ponts ; (2) son utilisation peut également être étendue pour réduire le f-CaO dans un autre laitier métallurgique, un traitement mixte d'au moins deux types de laitiers n'est pas exclu, d'autres constituants peuvent également être ajoutés lors du processus de mélange en plus du laitier métallurgique, et la teneur en f-CaO dans le laitier métallurgique est réduite au moyen de l'incompacité et de la faible propriété calcique du laitier de ferronickel.
本发明公开了利用镍铁渣降低钢渣中游离氧化钙的方法及其应用，所述方法将镍铁渣和钢渣利用冶炼后的余温在热熔条件下混合反应，无需外部热量；其中，镍铁渣和钢渣的质量比为1:0.6-4，且二者至少一种为熔融状态。与现有技术相比，本发明具有以下优点：(1)解决了转炉钢渣中f-CaO含量较高的问题，经过镍铁渣处理的钢渣中f-CaO含量能够控制在3％以下，从而实现其遇水膨胀性减小的目的，使得混合钢渣在建材领域更加稳定耐用，或可直接应用于建材行业和路桥建设领域；(2)其还可衍生到降低其余冶金渣中的f-CaO，不排除两种以上渣混合处理，也不排除在混合过程中除了添加冶金渣，还可添加其它组份，但是其均是利用镍铁渣的松散性和低钙性来降低冶金渣中f-CaO的含量。
METHOD FOR REDUCING FREE CALCIUM OXIDE IN STEEL SLAG BY USING FERRONICKEL SLAG, AND APPLICATION THEREOF
PROCÉDÉ DE RÉDUCTION D'OXYDE DE CALCIUM LIBRE DANS UN LAITIER D'ACIER À L'AIDE DE LAITIER DE FERRONICKEL, ET SON APPLICATION
利用镍铁渣降低钢渣中游离氧化钙的方法及其应用
YANG ZHIBIN (author) / CHEN CHONGXUE (author) / JIN HAI (author) / MAO RUI (author) / LEI MING (author) / DU PING (author) / ZHENG CHUANBO (author) / MA HAN (author) / ZOU CHANGDONG (author)
2023-06-01
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2022