MODIFIED ALUMINATE CEMENT, AND PREPARATION METHOD THEREFOR AND USE THEREOF
A modified aluminate cement, and a preparation method therefor and the use thereof. The raw material composition of the modified aluminate cement comprises, in percentages by mass: 90% of an aluminate cement and 10% of fluorgypsum, with KH2PO4 accounting for 0.2% of the total mass of the raw materials, wherein the aluminate cement is a calcium aluminate cement. In the present invention, fluorgypsum and KH2PO4 are used to regulate and control the setting time and compressive strength of the aluminate cement. Results show that 10 wt% of the fluorgypsum promotes the generation of ettringite, and 0.2 wt% of KH2PO4 further optimizes the generation of ettringite; and the incorporation of the two optimizes the hydration product and pore structure of a calcium aluminate cement, in particular KH2PO4 enables the morphology of ettringite to change from needle-shaped to fiber-shaped. The initial setting time and the final setting time are respectively shortened by 39% and 38%; and the 3 d compressive strength and the 28 d compressive strength are respectively increased by 76% and 228.80%. The present invention has a relatively good reference effect on the performance regulation and control of an aluminate cement grouting material.
L'invention concerne un ciment d'aluminate modifié, son procédé de préparation et son utilisation. La composition de matière première du ciment d'aluminate modifié comprend, en pourcentages en masse : 90 % d'un ciment d'aluminate et 10% de fluorogypse, avec le KH2PO4 représentant 0,2% de la masse totale des matières premières, le ciment d'aluminate étant un ciment d'aluminate de calcium. Dans la présente invention, le fluorogypse et le KH2PO4 sont utilisés pour réguler et contrôler le temps de prise et la résistance à la compression du ciment d'aluminate. Les résultats montrent que 10% en poids du fluorogypse active la production d'ettringite, et 0,2% en poids de KH2PO4 active encore davantage la production d'ettringite ; et l'incorporation des deux optimise le produit d'hydratation et la structure poreuse d'un ciment d'aluminate de calcium, en particulier le KH2PO4 permet à la morphologie de l'ettringite de passer de la forme d'aiguille à la forme de fibre. Le temps de prise initiale et le temps de prise finale sont respectivement raccourcis de 39 % et 38 % ; et la résistance à la compression 3 d et la résistance à la compression 28 d sont respectivement augmentées de 76 % et 228,80 %. La présente invention a un effet de référence relativement bon sur la régulation et le contrôle de performance d'un matériau d'injection de ciment d'aluminate.
一种改性铝酸盐水泥及其制备方法和应用。一种改性铝酸盐水泥，按质量百分比计，其原料组成包括铝酸盐水泥90％和氟石膏10％，以及上述原料总质量0.2％的KH2PO4；铝酸盐水泥为铝酸钙水泥。本发明采用氟石膏和KH2PO4对铝酸盐水泥的凝结时间和抗压强度进行了调控。结果表明，10wt％的氟石膏促成了钙矾石的生成，0.2wt％KH2PO4进一步优化了钙矾石的生成，二者的掺入均优化铝酸钙水泥的水化产物和孔结构，尤其是KH2PO4使钙矾石的形貌由针状变为纤维状。其中，初凝时间和终凝时间分别缩短了39％和38％；3d和28d抗压强度分别增大了76％和228.80％。这对铝酸盐水泥注浆材料的性能调控具有较好的参考作用。
MODIFIED ALUMINATE CEMENT, AND PREPARATION METHOD THEREFOR AND USE THEREOF
A modified aluminate cement, and a preparation method therefor and the use thereof. The raw material composition of the modified aluminate cement comprises, in percentages by mass: 90% of an aluminate cement and 10% of fluorgypsum, with KH2PO4 accounting for 0.2% of the total mass of the raw materials, wherein the aluminate cement is a calcium aluminate cement. In the present invention, fluorgypsum and KH2PO4 are used to regulate and control the setting time and compressive strength of the aluminate cement. Results show that 10 wt% of the fluorgypsum promotes the generation of ettringite, and 0.2 wt% of KH2PO4 further optimizes the generation of ettringite; and the incorporation of the two optimizes the hydration product and pore structure of a calcium aluminate cement, in particular KH2PO4 enables the morphology of ettringite to change from needle-shaped to fiber-shaped. The initial setting time and the final setting time are respectively shortened by 39% and 38%; and the 3 d compressive strength and the 28 d compressive strength are respectively increased by 76% and 228.80%. The present invention has a relatively good reference effect on the performance regulation and control of an aluminate cement grouting material.
L'invention concerne un ciment d'aluminate modifié, son procédé de préparation et son utilisation. La composition de matière première du ciment d'aluminate modifié comprend, en pourcentages en masse : 90 % d'un ciment d'aluminate et 10% de fluorogypse, avec le KH2PO4 représentant 0,2% de la masse totale des matières premières, le ciment d'aluminate étant un ciment d'aluminate de calcium. Dans la présente invention, le fluorogypse et le KH2PO4 sont utilisés pour réguler et contrôler le temps de prise et la résistance à la compression du ciment d'aluminate. Les résultats montrent que 10% en poids du fluorogypse active la production d'ettringite, et 0,2% en poids de KH2PO4 active encore davantage la production d'ettringite ; et l'incorporation des deux optimise le produit d'hydratation et la structure poreuse d'un ciment d'aluminate de calcium, en particulier le KH2PO4 permet à la morphologie de l'ettringite de passer de la forme d'aiguille à la forme de fibre. Le temps de prise initiale et le temps de prise finale sont respectivement raccourcis de 39 % et 38 % ; et la résistance à la compression 3 d et la résistance à la compression 28 d sont respectivement augmentées de 76 % et 228,80 %. La présente invention a un effet de référence relativement bon sur la régulation et le contrôle de performance d'un matériau d'injection de ciment d'aluminate.
一种改性铝酸盐水泥及其制备方法和应用。一种改性铝酸盐水泥，按质量百分比计，其原料组成包括铝酸盐水泥90％和氟石膏10％，以及上述原料总质量0.2％的KH2PO4；铝酸盐水泥为铝酸钙水泥。本发明采用氟石膏和KH2PO4对铝酸盐水泥的凝结时间和抗压强度进行了调控。结果表明，10wt％的氟石膏促成了钙矾石的生成，0.2wt％KH2PO4进一步优化了钙矾石的生成，二者的掺入均优化铝酸钙水泥的水化产物和孔结构，尤其是KH2PO4使钙矾石的形貌由针状变为纤维状。其中，初凝时间和终凝时间分别缩短了39％和38％；3d和28d抗压强度分别增大了76％和228.80％。这对铝酸盐水泥注浆材料的性能调控具有较好的参考作用。
MODIFIED ALUMINATE CEMENT, AND PREPARATION METHOD THEREFOR AND USE THEREOF
CIMENT D'ALUMINATE MODIFIÉ, SON PROCÉDÉ DE PRÉPARATION ET SON UTILISATION
一种改性铝酸盐水泥及其制备方法和应用
WANG YULI (author) / SUN GUOWEN (author) / LIU XIAOXING (author) / YANG LEI (author) / LUO SHUQIONG (author)
2024-07-04
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Modified aluminate cement and preparation method thereof
| European Patent Office | 2021
Iron aluminate cement clinker, preparation method thereof and iron aluminate cement
| European Patent Office | 2024
Modified aluminate cement as well as preparation method and application thereof
| European Patent Office | 2024