CALCIUM BENTONITE WET PROCESS SLURRY FOR LINERBOARD
A method for making a wet slurry containing calcium bentonite filler for a linerboard making process can include mixing calcium bentonite ore with water to form an initial slurry; screening the initial slurry to remove aggregates having a particle size of greater than 250 microns; milling the initial slurry until a d50 particle size of the slurry is 10 microns or less and a weight percent of particles having a particle size of 45 microns is less than 5 wt% based on the total weight of the slurry; and screening the milled slurry to remove particles having a particle size greater than 44 microns to thereby produce a final slurry.
L'invention concerne un procédé de fabrication d'une pâte humide contenant une charge de bentonite de calcium pour un procédé de fabrication de carton doublure, qui peut comprendre : le mélange d'un minerai de bentonite de calcium avec de l'eau pour former une pâte initiale; le criblage de la pâte initiale pour éliminer les agrégats dont la granulométrie est supérieure à 250 microns; le broyage de la pâte initiale jusqu'à ce que la granulométrie D50 soit inférieure ou égale à 10 microns et que le pourcentage en poids des particules ayant une granulométrie de 45 microns soit inférieur à 5 % en poids par rapport au poids total de la pâte; et le criblage de la pâte broyée pour éliminer les particules dont la taille est supérieure à 44 microns, afin de produire une pâte finale.
CALCIUM BENTONITE WET PROCESS SLURRY FOR LINERBOARD
A method for making a wet slurry containing calcium bentonite filler for a linerboard making process can include mixing calcium bentonite ore with water to form an initial slurry; screening the initial slurry to remove aggregates having a particle size of greater than 250 microns; milling the initial slurry until a d50 particle size of the slurry is 10 microns or less and a weight percent of particles having a particle size of 45 microns is less than 5 wt% based on the total weight of the slurry; and screening the milled slurry to remove particles having a particle size greater than 44 microns to thereby produce a final slurry.
L'invention concerne un procédé de fabrication d'une pâte humide contenant une charge de bentonite de calcium pour un procédé de fabrication de carton doublure, qui peut comprendre : le mélange d'un minerai de bentonite de calcium avec de l'eau pour former une pâte initiale; le criblage de la pâte initiale pour éliminer les agrégats dont la granulométrie est supérieure à 250 microns; le broyage de la pâte initiale jusqu'à ce que la granulométrie D50 soit inférieure ou égale à 10 microns et que le pourcentage en poids des particules ayant une granulométrie de 45 microns soit inférieur à 5 % en poids par rapport au poids total de la pâte; et le criblage de la pâte broyée pour éliminer les particules dont la taille est supérieure à 44 microns, afin de produire une pâte finale.
CALCIUM BENTONITE WET PROCESS SLURRY FOR LINERBOARD
PÂTE DE BENTONITE DE CALCIUM PAR PROCÉDÉ HUMIDE POUR CARTON DOUBLURE
HOCKMAN JOHN (author) / LAAKSO ARI-PEKKA (author) / EISENHOUR DON (author)
2024-09-06
Patent
Electronic Resource
English
| Elsevier | 1984
PROCESS FOR CONVERTING CALCIUM BENTONITE TO SODIUM BENTONITE
| European Patent Office | 2017
Calcium Bentonite and Fly Ash in Slurry Wall Construction Materials
| British Library Conference Proceedings | 1994
Cement-Bentonite Slurry Systems
| British Library Conference Proceedings | 2012