The invention relates to a 50% natural, renewable and impermeable compound that is widely used in industry and combines natural, physical, mechanical and thermal properties. Said compound is characterised in that when it solidifies, it withstands temperatures between 300°C and 405°C, becoming water-resistant. The compound is obtained by combining the blend of 8 parts of powdered coconut shell (endocarp) with 2 parts of expanded perlite (of rhyolite mineral) that is also powered and 80% epoxy resin in relation to the amount of coconut shell powder to be used, until achieving a lump-free moistened powder. This powder is then poured into the desired matrix and a carbon fibre fabric layer is added in the lower portion and another layer is added in the upper portion of the compound. It is pressed at a maximum of 1000 kg of pressure with levelling sensors and at a temperature of 110°C, to then cool and obtain the desired part by means of chiller equipment. When this compound solidifies by means of compression and moulding, it enables the manufacture, via thermal action and according to its intended use, of cabinets for electrical devices or, for example, boards for interiors, mirror frames, etc., in the automotive industry.

Compuesto 50 % natural, renovable e impermeable, de amplio uso industrial, que combina propiedades naturales, físicas, mecánicas y térmicas, que se caracteriza porque al solidificarse soporta temperaturas entre los 300° C y 405°C, resultando resistente al agua. El compuesto se obtiene combinando la mezcla de cascara de coco (endocarpio) en estado de polvo en 8 partes, con perlitas expandidas (de mineral riolita) también en estado de polvo en 2 partes y resina epoxica en un 80% en relación a la cantidad de polvo de cascara de coco a utilizar, hasta lograr un polvo humectado sin grumos, el cual se vuelca en la matriz deseada y se agrega una capa de tela de fibra de carbono en la parte inferior y otra capa en la parte superior del compuesto y se prensa a maximo 1000 kg de presión con sensores de nivelación y a una temperatura de 110°C, para luego mediante equipo chiller enfríar y obtener la pieza deseada. Este compuesto a través de acción térmica, al solidificarse mediante compresión y moldeado, permite fabricar de acuerdo con el uso que se le quiera dar, gabinetes para artefactos eléctricos, o por ejemplo en la industria automotriz para fabricar tableros de interiores, armazón de espejos, entre otros.

L'invention concerne un composé 50 % naturel, renouvelable et imperméable, largement utilisé dans l'industrie, qui combine des propriétés naturelles, physiques, mécaniques et thermiques, qui est caractérisé en ce que lorsqu'il se solidifie, il supporte des températures comprises entre 300 °C et 405 °C, étant ainsi résistant à l'eau. Le composé est obtenu par combinaison du mélange de coque de coco (endocarpe) à l'état de poussière en 8 parties, avec des perlites expansées (du minéral rhyolite) également à l'état de poussière en 2 parties et de résine époxyde dans une quantité de 80 % par rapport à la quantité de poudre de coque de coco à utiliser, jusqu'à obtenir une poudre humectée sans grumeaux, laquelle est versée dans la matrice souhaitée et on ajoute une couche de toile en fibre de carbone dans la partie inférieure ainsi qu'une autre couche dans la partie supérieure du composé et on presse au maximum à 1000 kg de pression avec des capteurs de nivellement et à une température de 110 °C, pour ensuite, au moyen d'un équipement refroidisseur, refroidir et obtenir la pièce souhaitée. Ce composé, par l'intermédiaire d'une action thermique, en étant solidifié par compression et moulage, permet de fabriquer conformément à l'utilisation que l'on souhaite en faire, des armoires pour équipements électriques, ou par exemple dans l'industrie automobile de fabriquer des panneaux intérieurs, une armature de rétroviseurs, entres autres.