Corrosion Resistant Alloys for Reinforced Concrete, April 2009
Deterioration of concrete bridges because of reinforcing steel corrosion has been recognized for 4-plus decades as a major technical and economic challenge for the United States. As an option for addressing this problem, renewed interest has focused on corrosion resistant reinforcements, stainless steels in particular. The present research study was performed jointly by Florida Atlantic University and the Florida Department of Transportation to evaluate reinforcements of this type. These included solid stainless steels 3Cr12 (UNS-S41003), 2101LDX (ASTM A955-98), 2304 (UNS-S31803), 2205 (UNS 31803), two 316L (UNS S31603) alloys, two 316 stainless steel clad black bar products, and ASTM A1035 commonly known as MMFX 2. Black bar (ASTM A615) reinforcement provided a baseline for comparison purposes. Results from short-term tests and preliminary results from long-term exposure of reinforced concrete slabs were presented in the first interim report for this project. This second interim report provides longer-term data and analyses of chloride exposures that involved four different types of reinforced concrete specimens, two of which were intended to simulate northern bridge decks exposed to deicing salts and the remaining two to marine substructure elements. Three different concrete mix designs were employed, and specimen types included combinations with a (1) simulated concrete crack, (2) bent top bar, (3) corrosion resistant upper bar(s) and black steel lower bars, and (4) intentional clad defects such that the carbon steel substrate was exposed. Cyclic wet-dry ponding with a sodium chloride (NaCl) solution was employed in the case of specimens intended to simulate northern bridge decks, and continuous partial submergence in either a NaCl solution or at a coastal marine site in Florida was used for specimens intended to represent a coastal bridge substructure. The exposures were for periods in excess of 4 years. The candidate alloys were ranked according to performance, and an analysis is reported that projects performance in actual concrete structures.
Corrosion Resistant Alloys for Reinforced Concrete, April 2009
Deterioration of concrete bridges because of reinforcing steel corrosion has been recognized for 4-plus decades as a major technical and economic challenge for the United States. As an option for addressing this problem, renewed interest has focused on corrosion resistant reinforcements, stainless steels in particular. The present research study was performed jointly by Florida Atlantic University and the Florida Department of Transportation to evaluate reinforcements of this type. These included solid stainless steels 3Cr12 (UNS-S41003), 2101LDX (ASTM A955-98), 2304 (UNS-S31803), 2205 (UNS 31803), two 316L (UNS S31603) alloys, two 316 stainless steel clad black bar products, and ASTM A1035 commonly known as MMFX 2. Black bar (ASTM A615) reinforcement provided a baseline for comparison purposes. Results from short-term tests and preliminary results from long-term exposure of reinforced concrete slabs were presented in the first interim report for this project. This second interim report provides longer-term data and analyses of chloride exposures that involved four different types of reinforced concrete specimens, two of which were intended to simulate northern bridge decks exposed to deicing salts and the remaining two to marine substructure elements. Three different concrete mix designs were employed, and specimen types included combinations with a (1) simulated concrete crack, (2) bent top bar, (3) corrosion resistant upper bar(s) and black steel lower bars, and (4) intentional clad defects such that the carbon steel substrate was exposed. Cyclic wet-dry ponding with a sodium chloride (NaCl) solution was employed in the case of specimens intended to simulate northern bridge decks, and continuous partial submergence in either a NaCl solution or at a coastal marine site in Florida was used for specimens intended to represent a coastal bridge substructure. The exposures were for periods in excess of 4 years. The candidate alloys were ranked according to performance, and an analysis is reported that projects performance in actual concrete structures.
Corrosion Resistant Alloys for Reinforced Concrete, April 2009
W. H. Hartt (author) / R. G. Powers (author) / F. P. Marino (author) / M. Paredes (author) / R. Simmons (author)
2009
150 pages
Report
No indication
English
Highway Engineering , Corrosion & Corrosion Inhibition , Coatings, Colorants, & Finishes , Reinforced concrete , Bridges , Corrosion resistance , Alloys , Corrosion protection , Corrosion testing , Corrosion inhibitors , Bridge structures , Chlorides , Durability , High performance reinforcement , Stainless steel , 5-year program , MMFX-2 steel , Federal Highway Administration(FHWA)
Corrosion Resistant Alloys for Reinforced Concrete
| NTIS | 2007
Manufacturing of corrosion-resistant concrete and reinforced concrete pipes
| British Library Online Contents | 2008
Construction method of corrosion-resistant reinforced concrete structure
| European Patent Office | 2024
6th April 2009 L’Aquila earthquake, Italy: reinforced concrete building performance
| British Library Online Contents | 2011