Electro-assisted regeneration of ion exchange resins
Abstract Electro-assisted regeneration (EAR) for the mixed bed of strongly acidic cation and weakly basic anion exchange resins with the Al(OH)3 suspension in a three-compartment cell was investigated. The desalination experiments were carried out to evaluate the characteristic of the regenerated mixed resins. Experimental results showed that the efficiency of resin regeneration was strictly dependent on the voltage, regeneration time, and feed regenerant flow rate. The amount of the effluent reached 50 times the volume of the resins bed, and the conductivity was less than 1.0 μs/cm. Compared to the conventional ER, the total effluent volume of EAR was about 1000 mL more than that of ER under the same conditions, and the outlet conductivity was significantly lower. The desalination and regeneration reaction mechanisms of the mixed resins indicated the regeneration efficiency of resin with Al(OH)3 as the regenerant was much higher than that with H2O.
Electro-assisted regeneration of ion exchange resins
Abstract Electro-assisted regeneration (EAR) for the mixed bed of strongly acidic cation and weakly basic anion exchange resins with the Al(OH)3 suspension in a three-compartment cell was investigated. The desalination experiments were carried out to evaluate the characteristic of the regenerated mixed resins. Experimental results showed that the efficiency of resin regeneration was strictly dependent on the voltage, regeneration time, and feed regenerant flow rate. The amount of the effluent reached 50 times the volume of the resins bed, and the conductivity was less than 1.0 μs/cm. Compared to the conventional ER, the total effluent volume of EAR was about 1000 mL more than that of ER under the same conditions, and the outlet conductivity was significantly lower. The desalination and regeneration reaction mechanisms of the mixed resins indicated the regeneration efficiency of resin with Al(OH)3 as the regenerant was much higher than that with H2O.
Electro-assisted regeneration of ion exchange resins
Liu, Zhigang (author) / Wang, Ying (author) / Li, Yansheng (author) / Chang, Hui (author)
2008-12-01
5 pages
Article (Journal)
Electronic Resource
English
Electro-Regeneration Mechanism of Ion-Exchange Resins in Electrodeionization
| British Library Online Contents | 2004
| American Chemical Society | 2024
| British Library Conference Proceedings | 2014
| Wiley | 1945
| Tema Archive | 1975