Lap-joint corrosion of precoated materials for building applications
The adoption of designs involving the use of lap joints is becoming increasingly common in the building industry. However, precoated steel sheets assembled by lap joints are prone to suffer durability problems associated with this type of joint, such as the premature deterioration of protective coatings (metallic, organic) and accelerated metallic corrosion of the base steel by moisture retention in the lap. The literature reveals a lack of knowledge about the corrosion mechanisms and primary factors involved in this issue. The main objective of this work is to study lap-joint corrosion in relation with two zinc-based coatings used in the building industry: 55%Al-Zn and hot-dip galvanised (HDG), unpainted and painted, and before and after atmospheric exposure or accelerated ageing (salt fog and Prohesion tests). The proposed corrosion mechanisms are based on results obtained by visual observation and by scanning electron microscopy (SEM) associated with X-ray energy dispersive spectrometry (EDS). Complementary X-ray diffraction (XRD) has also been used. With the unpainted precoated steel sheets, localised attack of the metallic coating is observed in the lapped area. In the case of the metallic+organic coatings, attack is initiated in the lapped area and advances towards the non-lapped area.
Lap-joint corrosion of precoated materials for building applications
The adoption of designs involving the use of lap joints is becoming increasingly common in the building industry. However, precoated steel sheets assembled by lap joints are prone to suffer durability problems associated with this type of joint, such as the premature deterioration of protective coatings (metallic, organic) and accelerated metallic corrosion of the base steel by moisture retention in the lap. The literature reveals a lack of knowledge about the corrosion mechanisms and primary factors involved in this issue. The main objective of this work is to study lap-joint corrosion in relation with two zinc-based coatings used in the building industry: 55%Al-Zn and hot-dip galvanised (HDG), unpainted and painted, and before and after atmospheric exposure or accelerated ageing (salt fog and Prohesion tests). The proposed corrosion mechanisms are based on results obtained by visual observation and by scanning electron microscopy (SEM) associated with X-ray energy dispersive spectrometry (EDS). Complementary X-ray diffraction (XRD) has also been used. With the unpainted precoated steel sheets, localised attack of the metallic coating is observed in the lapped area. In the case of the metallic+organic coatings, attack is initiated in the lapped area and advances towards the non-lapped area.
Lap-joint corrosion of precoated materials for building applications
Chico, Belen (author) / De la Fuente, Daniel (author) / Almeida, Elisabete (author) / Morcillo, Manuel (author) / Gonzalez, Jose Antonio (author) / Otero, Eduardo (author)
Surface and Coatings Technology ; 190 ; 65-74
2005
10 Seiten, 25 Quellen
Article (Journal)
English
Lap-joint testing of precoated steel materials
| Tema Archive | 2003
Trends in corrosion–resistant precoated steel sheets for automotive applications
| British Library Online Contents | 1986
Precoated Steel Sheets for Construction Materials
| British Library Online Contents | 2001
Utilization of precoated materials for road surfacing
| Engineering Index Backfile | 1949