Corrosion Resistance of MgO-ZrO2 Brick and MgO-Cr2O3 Brick Compared by Rotating Slag Attacking Method
An environment-friendly material MgO-ZrO2 brick which is hoped to substitute for MgO-Cr2O3 brick was investigated. The using effects of MgO-ZrO2 brick and MgO-Cr2O3 brick were compared by rotating slag attacking method whose environment is similar to the environment in RH degasser. It indicates that the corrosion resistance performance of MgO-ZrO2 brick is better than that of MgO-Cr2O3 brick. Due to the effect of molten steel, slag and oxygen, Fe being oxidized to FeO or Fe2O3 at high temperature 1900K will produce volume expansion which results in MgO-Cr2O3 brick being cracked. At the same time, Cr2O3 will be decomposed to CrO3 gas, which will be evaporated seriously by the airflow and lead to MgO-Cr2O3 brick structural loosen and deterioration, ultimately. While the activity of oxygen dissolved molten steel is extremely low and ZrO2 is stable in the rotary kiln at 1900K. Furthermore, ZrO2 will react rapidly with CaO and its product CaZrO3 will form dense layer to prevent MgO-ZrO2 brick from being corroded. Therefore, trial production of MgO-ZrO2 brick applied for RH degasser is recommended.
Corrosion Resistance of MgO-ZrO2 Brick and MgO-Cr2O3 Brick Compared by Rotating Slag Attacking Method
An environment-friendly material MgO-ZrO2 brick which is hoped to substitute for MgO-Cr2O3 brick was investigated. The using effects of MgO-ZrO2 brick and MgO-Cr2O3 brick were compared by rotating slag attacking method whose environment is similar to the environment in RH degasser. It indicates that the corrosion resistance performance of MgO-ZrO2 brick is better than that of MgO-Cr2O3 brick. Due to the effect of molten steel, slag and oxygen, Fe being oxidized to FeO or Fe2O3 at high temperature 1900K will produce volume expansion which results in MgO-Cr2O3 brick being cracked. At the same time, Cr2O3 will be decomposed to CrO3 gas, which will be evaporated seriously by the airflow and lead to MgO-Cr2O3 brick structural loosen and deterioration, ultimately. While the activity of oxygen dissolved molten steel is extremely low and ZrO2 is stable in the rotary kiln at 1900K. Furthermore, ZrO2 will react rapidly with CaO and its product CaZrO3 will form dense layer to prevent MgO-ZrO2 brick from being corroded. Therefore, trial production of MgO-ZrO2 brick applied for RH degasser is recommended.
Corrosion Resistance of MgO-ZrO2 Brick and MgO-Cr2O3 Brick Compared by Rotating Slag Attacking Method
Chen, Song-lin (author) / Yuan, Lin (author) / Feng, Zhong-Qi (author) / Liu, Xi-Jun (author) / Sun, Jia-lin (author) / Pan, Bo (author) / Wang, Jian-dong (author)
2012
5 Seiten
Conference paper
English
Ladle brick with high slag corrosion resistance and preparation method thereof
| European Patent Office | 2020
| Trans Tech Publications | 2015
Slag line brick, preparation method thereof and application of slag line brick in steel ladle
| European Patent Office | 2024
Sintered brick prepared from manganese slag and preparation method of sintered brick
| European Patent Office | 2016