Permeability study of cracked concrete
Cracks in concrete generally interconnect flow paths and increase concrete permeability. The increase in concrete permeability due to the progression of cracks allows more water or aggressive chemical ions to penetrate into the concrete, facilitating deterioration. The present work studies the relationship between crack characteristics and concrete permeability. In this study, feedback controlled splitting tests are introduced to generate crack width-controlled concrete specimens. Sequential crack pattems with different crack widths are viewed under a microscope. The permeability of cracked concrete is evaluated by water permeability tests. The preliminary results indicate that crack openings generally accelerate water flow rate in concrete. When a specimen is loaded to have a crack opening displacement smaller than 50 microns prior to unloading, the crack opening has little effect on concrete permeability. When the crack opening displacement increases from 50 microns to about 200 microns, concrete permeability increases rapidly. After the crack opening displacement reaches 200 microns, the rate of water permeability increases steadily. The present research may provide insight into developing design criteria for a durable concrete and in predicting service life of a concrete structure.
Permeability study of cracked concrete
Cracks in concrete generally interconnect flow paths and increase concrete permeability. The increase in concrete permeability due to the progression of cracks allows more water or aggressive chemical ions to penetrate into the concrete, facilitating deterioration. The present work studies the relationship between crack characteristics and concrete permeability. In this study, feedback controlled splitting tests are introduced to generate crack width-controlled concrete specimens. Sequential crack pattems with different crack widths are viewed under a microscope. The permeability of cracked concrete is evaluated by water permeability tests. The preliminary results indicate that crack openings generally accelerate water flow rate in concrete. When a specimen is loaded to have a crack opening displacement smaller than 50 microns prior to unloading, the crack opening has little effect on concrete permeability. When the crack opening displacement increases from 50 microns to about 200 microns, concrete permeability increases rapidly. After the crack opening displacement reaches 200 microns, the rate of water permeability increases steadily. The present research may provide insight into developing design criteria for a durable concrete and in predicting service life of a concrete structure.
Permeability study of cracked concrete
Permeabilitätsmessungen an rißbehaftetem Beton
Wang, K. (author) / Jansen, D.C. (author) / Shah, P. (author) / Karr, A.F. (author)
Cement and Concrete Research ; 27 ; 381-393
1997
13 Seiten, 9 Bilder, 1 Tabelle, 7 Quellen
Article (Journal)
English
Permeability Study of Cracked Concrete
| Online Contents | 1997
Permeability Study of Cracked Concrete
| British Library Online Contents | 1997
Permeability, of cracked concrete
| British Library Online Contents | 1999
Permeability of cracked concrete
| Springer Verlag | 1999
Permeability of cracked concrete
| Online Contents | 1999