High-density zirconia corundum brick for hazardous waste disposal rotary kiln
The invention discloses a high-density zirconia corundum brick for a hazardous waste disposal rotary kiln, and belongs to the field of refractory materials. The zirconia corundum brick comprises the following components in percentage by weight: 1-20% of zirconia with the particle size less than or equal to 3mm, 5-15% of alumina micro powder with a particle size less than or equal to 0.004mm, 1-5% of a binding agent and the balance of corundum with the particle size less than or equal to 8mm. The zirconia corundum brick is prepared by mixing the raw materials according to the ratio, preparing a pug in a mixing mill, carrying out molding under the pressure of more than or equal to 400 tons, and sintering a green brick in a tunnel kiln or a shuttle kiln at 1500-1800 DEG C after molding. The high-density zirconia corundum brick has the advantages that the high-density zirconia corundum brick is suitable for various specifications of rotary kilns for hazardous waste disposal, the service life of the product can reach more than 6 months, and the high-density zirconia corundum brick plays a very positive role in improving the operation rate of the rotary kilns for hazardous waste disposal.
一种危险废物处置回转窑用高致密锆刚玉砖，属于耐火材料领域。锆刚玉砖按重量百分比各组份为：粒径≤3mm的氧化锆：1～20％；粒径≤0.004mm氧化铝微粉：5～15％；结合剂：1～5％，余量为粒径≤8mm的刚玉；将上述原料配比混合，于混炼机中制成泥料，在≥400吨的压力下成型，成型后砖坯于1500～1800℃的隧道窑或者梭式窑内烧成。优点在于，适用于各种规格危险废弃物处置用回转窑，产品使用寿命可达到6个月以上，对提高危险废弃物处置用回转窑运转率起到了非常积极的作用。
High-density zirconia corundum brick for hazardous waste disposal rotary kiln
The invention discloses a high-density zirconia corundum brick for a hazardous waste disposal rotary kiln, and belongs to the field of refractory materials. The zirconia corundum brick comprises the following components in percentage by weight: 1-20% of zirconia with the particle size less than or equal to 3mm, 5-15% of alumina micro powder with a particle size less than or equal to 0.004mm, 1-5% of a binding agent and the balance of corundum with the particle size less than or equal to 8mm. The zirconia corundum brick is prepared by mixing the raw materials according to the ratio, preparing a pug in a mixing mill, carrying out molding under the pressure of more than or equal to 400 tons, and sintering a green brick in a tunnel kiln or a shuttle kiln at 1500-1800 DEG C after molding. The high-density zirconia corundum brick has the advantages that the high-density zirconia corundum brick is suitable for various specifications of rotary kilns for hazardous waste disposal, the service life of the product can reach more than 6 months, and the high-density zirconia corundum brick plays a very positive role in improving the operation rate of the rotary kilns for hazardous waste disposal.
一种危险废物处置回转窑用高致密锆刚玉砖，属于耐火材料领域。锆刚玉砖按重量百分比各组份为：粒径≤3mm的氧化锆：1～20％；粒径≤0.004mm氧化铝微粉：5～15％；结合剂：1～5％，余量为粒径≤8mm的刚玉；将上述原料配比混合，于混炼机中制成泥料，在≥400吨的压力下成型，成型后砖坯于1500～1800℃的隧道窑或者梭式窑内烧成。优点在于，适用于各种规格危险废弃物处置用回转窑，产品使用寿命可达到6个月以上，对提高危险废弃物处置用回转窑运转率起到了非常积极的作用。
High-density zirconia corundum brick for hazardous waste disposal rotary kiln
一种危险废物处置回转窑用高致密锆刚玉砖
XIA WENBIN (Autor:in) / GAO CHANGHE (Autor:in) / ZHAN HUASHENG (Autor:in) / MA SHULONG (Autor:in) / WEI YINGFENG (Autor:in) / CAI BINLI (Autor:in)
04.05.2021
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
High-density chrome corundum brick for hazardous waste disposal rotary kiln
| Europäisches Patentamt | 2021
High-density corundum mullite brick for hazardous waste disposal rotary kiln
| Europäisches Patentamt | 2021
High-density chromium-zirconium-corundum brick for hazardous waste disposal rotary kiln
| Europäisches Patentamt | 2021
Corundum brick for hazardous waste rotary kiln and preparation method thereof
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2021