Lightweight high-strength composite material and preparation method thereof
The invention provides a lightweight high-strength composite material and a preparation method thereof. The lightweight high-strength composite material is prepared from the following raw materials in parts by weight: 20-30 parts of magnesium oxide, 2-5 parts of floating beads, 0.09-0.15 part of citric acid, 4.5-11.5 parts of magnesium sulfate and 7-10 parts of water. The preparation method comprises the following steps: uniformly mixing magnesium oxide and floating beads to obtain a mixture A, and dissolving citric acid and magnesium sulfate in water at 40-50 DEG C to obtain a solution B; adding the mixture A into the solution B, stirring for 1 min at a low speed of 140 rpm, then stirring for 2-3 min at a high speed of 200 rpm or above, and finally curing at 20-30 DEG C. The prepared light high-strength composite material is small in volume weight and has high breaking strength and compressive strength.
本发明提出了一种轻质高强复合材料及其制备方法，所述轻质高强复合材料由以下重量份的原料制备：氧化镁20‑30份、漂珠2‑5份、柠檬酸0.09‑0.15份、硫酸镁4.5‑11.5份和水7‑10份；所述制备方法将氧化镁和漂珠混匀，得到混合物A，将柠檬酸和硫酸镁在40‑50℃溶解于水中，得到溶液B；将混合物A加入到溶液B中，先140rpm低速搅拌1min，然后再200rpm以上高速搅拌2‑3min，最后在20‑30℃的条件下进行养护。本发明制备的轻质高强复合材料容重小，而且具有较高的抗折强度和抗压强度。
Lightweight high-strength composite material and preparation method thereof
The invention provides a lightweight high-strength composite material and a preparation method thereof. The lightweight high-strength composite material is prepared from the following raw materials in parts by weight: 20-30 parts of magnesium oxide, 2-5 parts of floating beads, 0.09-0.15 part of citric acid, 4.5-11.5 parts of magnesium sulfate and 7-10 parts of water. The preparation method comprises the following steps: uniformly mixing magnesium oxide and floating beads to obtain a mixture A, and dissolving citric acid and magnesium sulfate in water at 40-50 DEG C to obtain a solution B; adding the mixture A into the solution B, stirring for 1 min at a low speed of 140 rpm, then stirring for 2-3 min at a high speed of 200 rpm or above, and finally curing at 20-30 DEG C. The prepared light high-strength composite material is small in volume weight and has high breaking strength and compressive strength.
本发明提出了一种轻质高强复合材料及其制备方法，所述轻质高强复合材料由以下重量份的原料制备：氧化镁20‑30份、漂珠2‑5份、柠檬酸0.09‑0.15份、硫酸镁4.5‑11.5份和水7‑10份；所述制备方法将氧化镁和漂珠混匀，得到混合物A，将柠檬酸和硫酸镁在40‑50℃溶解于水中，得到溶液B；将混合物A加入到溶液B中，先140rpm低速搅拌1min，然后再200rpm以上高速搅拌2‑3min，最后在20‑30℃的条件下进行养护。本发明制备的轻质高强复合材料容重小，而且具有较高的抗折强度和抗压强度。
Lightweight high-strength composite material and preparation method thereof
一种轻质高强复合材料及其制备方法
CUI JIANXIN (Autor:in) / SONG JINGHUI (Autor:in) / LI HONGWEI (Autor:in) / WANG YUJIE (Autor:in) / WANG HUIJIE (Autor:in) / ZHANG SHENGWEI (Autor:in) / ZHANG WENTAO (Autor:in) / HAO MEI (Autor:in) / CUI ZIQI (Autor:in) / MA LI (Autor:in)
27.09.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Lightweight high-strength composite material and preparation method thereof
| Europäisches Patentamt | 2023
Lightweight high-strength composite lightweight wallboard and preparation method thereof
| Europäisches Patentamt | 2023
Lightweight high-strength composite material electric pole and preparation method thereof
| Europäisches Patentamt | 2024
Lightweight high-strength geopolymer-based composite material and preparation method thereof
| Europäisches Patentamt | 2024
High-strength lightweight building material and preparation method thereof
| Europäisches Patentamt | 2015