High-frequency current sensor NiCuZn soft magnetic ferrite material for partial discharge monitoring and preparation method thereof
The invention discloses a high-frequency current sensor NiCuZn soft magnetic ferrite material for partial discharge monitoring and a preparation method thereof, the magnetic ferrite raw material comprises main components and auxiliary components, the main components comprise 49.3 to 51.2% of Fe2O3, 33.1 to 36.4% of ZnO, 13.6 to 14.2% of NiO and the balance of CuO, and the auxiliary components comprise 0.01 to 0.6% of CaCO3, 0.01 to 0.4% of Nb2O5 and 0.01 to 0.5% of Bi2O3. The invention provides a high-frequency current sensor NiCuZn soft magnetic ferrite material for partial discharge monitoring, which can stably work at 0-100 DEG C, and the transmission impedance value at 0.3-100MHz is greater than 5mV/mA.
本发明公开了一种局部放电监测用高频电流传感器NiCuZn软磁铁氧体材料及制备方法，其中磁铁氧体原料组分包括主成分和辅助成分，按摩尔分数计，主成分Fe2O3为49.3～51.2％，ZnO为33.1～36.4％，NiO为13.6～14.2％，余量为CuO，辅助成分CaCO3、Nb2O5和Bi2O3分别为0.01～0.6％、0.01～0.4％和0.01～0.5％。本发明提供一种局部放电监测用高频电流传感器NiCuZn软磁铁氧体材料，可以在0～100℃下稳定工作，在0.3～100MHz下的传输阻抗值均大于5mV/mA。
High-frequency current sensor NiCuZn soft magnetic ferrite material for partial discharge monitoring and preparation method thereof
The invention discloses a high-frequency current sensor NiCuZn soft magnetic ferrite material for partial discharge monitoring and a preparation method thereof, the magnetic ferrite raw material comprises main components and auxiliary components, the main components comprise 49.3 to 51.2% of Fe2O3, 33.1 to 36.4% of ZnO, 13.6 to 14.2% of NiO and the balance of CuO, and the auxiliary components comprise 0.01 to 0.6% of CaCO3, 0.01 to 0.4% of Nb2O5 and 0.01 to 0.5% of Bi2O3. The invention provides a high-frequency current sensor NiCuZn soft magnetic ferrite material for partial discharge monitoring, which can stably work at 0-100 DEG C, and the transmission impedance value at 0.3-100MHz is greater than 5mV/mA.
本发明公开了一种局部放电监测用高频电流传感器NiCuZn软磁铁氧体材料及制备方法，其中磁铁氧体原料组分包括主成分和辅助成分，按摩尔分数计，主成分Fe2O3为49.3～51.2％，ZnO为33.1～36.4％，NiO为13.6～14.2％，余量为CuO，辅助成分CaCO3、Nb2O5和Bi2O3分别为0.01～0.6％、0.01～0.4％和0.01～0.5％。本发明提供一种局部放电监测用高频电流传感器NiCuZn软磁铁氧体材料，可以在0～100℃下稳定工作，在0.3～100MHz下的传输阻抗值均大于5mV/mA。
High-frequency current sensor NiCuZn soft magnetic ferrite material for partial discharge monitoring and preparation method thereof
一种局部放电监测用高频电流传感器NiCuZn软磁铁氧体材料及其制备方法
WANG YANG (Autor:in) / YANG CHANGLONG (Autor:in) / ZHENG YANG (Autor:in) / KONG QINGJIANG (Autor:in) / BAI HAN (Autor:in) / LIU YING (Autor:in) / ZHANG DONGXUE (Autor:in) / MU BO (Autor:in) / LI XIAOBIN (Autor:in) / SUN SHOUDAO (Autor:in)
07.03.2023
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2023
NiCuZn soft magnetic ferrite material and preparing method thereof
| Europäisches Patentamt | 2015
NiCuZn ferrite material and preparation method thereof
| Europäisches Patentamt | 2015