Erosion-resistant castable for garbage incinerator and preparation method of erosion-resistant castable
The invention provides an erosion-resistant castable for a garbage incinerator and a preparation method of the erosion-resistant castable, and relates to the technical field of castable. The erosion-resistant castable for the garbage incinerator comprises the following raw materials in parts by weight: 25-40 parts of mullite, 8-15 parts of silicon carbide, 3-10 parts of modified fibers, 3-10 parts of modified silica powder, 3-8 parts of pure calcium aluminate cement and 0.1-0.5 part of a water reducing agent. The preparation method of the erosion-resistant castable for the garbage incinerator, provided by the invention, is simple in process, and the obtained castable has excellent wear resistance and erosion resistance.
本发明提供一种垃圾焚烧炉用耐侵蚀浇注料及其制备方法，涉及浇注料技术领域。一种垃圾焚烧炉用耐侵蚀浇注料，包括以下重量份的原料：莫来石25‑40份、碳化硅8‑15份、改性纤维3‑10份、改性硅微粉3‑10份、纯铝酸钙水泥3‑8份、减水剂0.1‑0.5份。本发明提出的一种垃圾焚烧炉用耐侵蚀浇注料制备方法工艺简单，得到的浇注料具有优良的耐磨耐侵蚀性能。
Erosion-resistant castable for garbage incinerator and preparation method of erosion-resistant castable
The invention provides an erosion-resistant castable for a garbage incinerator and a preparation method of the erosion-resistant castable, and relates to the technical field of castable. The erosion-resistant castable for the garbage incinerator comprises the following raw materials in parts by weight: 25-40 parts of mullite, 8-15 parts of silicon carbide, 3-10 parts of modified fibers, 3-10 parts of modified silica powder, 3-8 parts of pure calcium aluminate cement and 0.1-0.5 part of a water reducing agent. The preparation method of the erosion-resistant castable for the garbage incinerator, provided by the invention, is simple in process, and the obtained castable has excellent wear resistance and erosion resistance.
本发明提供一种垃圾焚烧炉用耐侵蚀浇注料及其制备方法，涉及浇注料技术领域。一种垃圾焚烧炉用耐侵蚀浇注料，包括以下重量份的原料：莫来石25‑40份、碳化硅8‑15份、改性纤维3‑10份、改性硅微粉3‑10份、纯铝酸钙水泥3‑8份、减水剂0.1‑0.5份。本发明提出的一种垃圾焚烧炉用耐侵蚀浇注料制备方法工艺简单，得到的浇注料具有优良的耐磨耐侵蚀性能。
Erosion-resistant castable for garbage incinerator and preparation method of erosion-resistant castable
一种垃圾焚烧炉用耐侵蚀浇注料及其制备方法
ZHANG SHAN (Autor:in) / DONG SHUNJIE (Autor:in) / ZHANG LIN (Autor:in) / BAO LI (Autor:in)
14.05.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2022
Castable for high-temperature garbage incinerator and preparation method of castable
| Europäisches Patentamt | 2015
Alkali-resistant, wear-resistant and erosion-resistant castable and preparation method thereof
| Europäisches Patentamt | 2024
High-strength, chemical-erosion-resistant, wear-resistant and fire-resistant castable
| Europäisches Patentamt | 2024