Environment-friendly durable autoclaved aerated concrete material and preparation method thereof
The invention provides an environment-friendly durable autoclaved aerated concrete material and a preparation method thereof, and belongs to the technical field of novel building materials. The environment-friendly durable autoclaved aerated concrete material is prepared from the following substances in parts by mass: 45 to 70 parts of fly ash, 3 to 12 parts of gypsum, 10 to 20 parts of solid waste slurry, 5 to 10 parts of cement, 6 to 15 parts of lime, 0.1 to 0.5 part of aluminum powder paste, 0.1 to 0.5 part of photosensitive catalytic material and 0.1 to 0.5 part of ceramic fiber. According to the environment-friendly durable autoclaved aerated concrete material disclosed by the invention, the service life of the autoclaved aerated concrete material is prolonged by utilizing the characteristics of long-term stability of the photosensitive catalytic material and high hardness and high wear resistance of the ceramic fibers.
本申请提供了一种环保耐用蒸压加气混凝土材料及其制备方法，属于新型建筑材料技术领域。环保耐用蒸压加气混凝土材料按照质量份数包括如下物质：粉煤灰45‑70份、石膏3‑12份、固废浆料10‑20份、水泥5‑10份、石灰6‑15份、铝粉膏0.1‑0.5份、光敏催化材料0.1‑0.5份、陶瓷纤维0.1‑0.5份。本申请的环保耐用蒸压加气混凝土材料，利用光敏催化材料的长期稳定性和陶瓷纤维的高硬度、高耐磨性特点，提高蒸压加气混凝土材料的使用寿命。
Environment-friendly durable autoclaved aerated concrete material and preparation method thereof
The invention provides an environment-friendly durable autoclaved aerated concrete material and a preparation method thereof, and belongs to the technical field of novel building materials. The environment-friendly durable autoclaved aerated concrete material is prepared from the following substances in parts by mass: 45 to 70 parts of fly ash, 3 to 12 parts of gypsum, 10 to 20 parts of solid waste slurry, 5 to 10 parts of cement, 6 to 15 parts of lime, 0.1 to 0.5 part of aluminum powder paste, 0.1 to 0.5 part of photosensitive catalytic material and 0.1 to 0.5 part of ceramic fiber. According to the environment-friendly durable autoclaved aerated concrete material disclosed by the invention, the service life of the autoclaved aerated concrete material is prolonged by utilizing the characteristics of long-term stability of the photosensitive catalytic material and high hardness and high wear resistance of the ceramic fibers.
本申请提供了一种环保耐用蒸压加气混凝土材料及其制备方法，属于新型建筑材料技术领域。环保耐用蒸压加气混凝土材料按照质量份数包括如下物质：粉煤灰45‑70份、石膏3‑12份、固废浆料10‑20份、水泥5‑10份、石灰6‑15份、铝粉膏0.1‑0.5份、光敏催化材料0.1‑0.5份、陶瓷纤维0.1‑0.5份。本申请的环保耐用蒸压加气混凝土材料，利用光敏催化材料的长期稳定性和陶瓷纤维的高硬度、高耐磨性特点，提高蒸压加气混凝土材料的使用寿命。
Environment-friendly durable autoclaved aerated concrete material and preparation method thereof
环保耐用蒸压加气混凝土材料及其制备方法
ZHANG XIAOMENG (Autor:in) / LIU YUTING (Autor:in) / TIAN YE (Autor:in) / CAO JUN (Autor:in) / CHEN GANG (Autor:in) / ZHAO JINGYU (Autor:in) / TIAN ZIYANG (Autor:in) / ZHAO XINGLAN (Autor:in) / YANG SIQING (Autor:in) / LI ZHONGHUI (Autor:in)
18.06.2024
Patent
Elektronische Ressource
Chinesisch
Environment-friendly autoclaved aerated concrete block and preparation method thereof
| Europäisches Patentamt | 2016
Environment-friendly autoclaved aerated concrete block and preparation method thereof
| Europäisches Patentamt | 2022
Autoclaved aerated concrete, autoclaved aerated concrete slab and preparation method thereof
| Europäisches Patentamt | 2020
Novel solid waste environment-friendly autoclaved aerated concrete and preparation method thereof
| Europäisches Patentamt | 2021
Autoclaved aerated concrete material and preparation method thereof
| Europäisches Patentamt | 2024