Methyl sodium silicate modified C35 impervious concrete and preparation method thereof
The invention discloses methyl sodium silicate modified C35 impervious concrete and a preparation method thereof. The impervious concrete is prepared from the following raw materials in parts by mass: 180 to 200 parts of cement, 70 to 90 parts of slag powder, 60 to 80 parts of fly ash, 8 to 20 parts of methyl sodium silicate solution, 800 parts of artificial sand, 1054 parts of gravel, 1.5 to 2.0 parts of water reducing agent and 160 to 175 parts of water. According to the preparation method provided by the invention, by adding the sodium methyl silicate solution, the anti-seepage performance of the concrete can be improved, and the effects of small amount and high efficiency are achieved.
本发明公开了一种甲基硅酸钠改性的C35抗渗混凝土及其制备方法，该抗渗混凝土由以下质量份数的原料组成：水泥180‑200份，矿渣粉70‑90份，粉煤灰60‑80份，甲基硅酸钠溶液8‑20份，人工砂800份，碎石1054份，减水剂1.5‑2.0份，水160‑175份。本发明提供的制备方法通过添加甲基硅酸钠溶液，能够提升混凝土的防渗性能，且具有少量高效的作用。
Methyl sodium silicate modified C35 impervious concrete and preparation method thereof
The invention discloses methyl sodium silicate modified C35 impervious concrete and a preparation method thereof. The impervious concrete is prepared from the following raw materials in parts by mass: 180 to 200 parts of cement, 70 to 90 parts of slag powder, 60 to 80 parts of fly ash, 8 to 20 parts of methyl sodium silicate solution, 800 parts of artificial sand, 1054 parts of gravel, 1.5 to 2.0 parts of water reducing agent and 160 to 175 parts of water. According to the preparation method provided by the invention, by adding the sodium methyl silicate solution, the anti-seepage performance of the concrete can be improved, and the effects of small amount and high efficiency are achieved.
本发明公开了一种甲基硅酸钠改性的C35抗渗混凝土及其制备方法，该抗渗混凝土由以下质量份数的原料组成：水泥180‑200份，矿渣粉70‑90份，粉煤灰60‑80份，甲基硅酸钠溶液8‑20份，人工砂800份，碎石1054份，减水剂1.5‑2.0份，水160‑175份。本发明提供的制备方法通过添加甲基硅酸钠溶液，能够提升混凝土的防渗性能，且具有少量高效的作用。
Methyl sodium silicate modified C35 impervious concrete and preparation method thereof
一种甲基硅酸钠改性的C35抗渗混凝土及其制备方法
RAN XINYI (Autor:in) / LI PEIPENG (Autor:in) / ZENG PINMO (Autor:in) / ZHOU AOBO (Autor:in)
29.11.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Waterproof impervious concrete and preparation method thereof
| Europäisches Patentamt | 2021
Waterproof impervious concrete and preparation method thereof
| Europäisches Patentamt | 2024
Corrosion-resistant impervious concrete and preparation method thereof
| Europäisches Patentamt | 2021