SINTERED COMPACT OF SILICON CARBIDE AND PRODUCING METHOD THEREOF
PROBLEM TO BE SOLVED: To provide a sintered compact of silicon carbide and a producing method thereof in which suppression of generation frequency of crack etc. due to baking shrinkage in a formed product is achieved.SOLUTION: There is provided a producing method of a ceramic sintered compact in which, by precipitating a part of ingredient powder with elutriation subjected to slurry obtained from supplementation of distribution agent and solvent to ceramic ingredient powder, supernatant of the slurry is recovered, then a formed product is produced by forming a cake of the ingredient powder in the supernatant, and the formed product is subjected to calcination. Due to the elutriation, y% or more of ingredient powder among ingredient powder having a larger diameter than criterion particle diameter to be x% as accumulation in early stage particle diameter distribution is removed. The elutriation is carried out so that 2 dimensional plot (x, y) is positioned in first specified region S1 or second specified region S2.
【課題】成形体の焼成収縮に由来するクラック等の発生頻度抑制が図られている炭化珪素質焼結体及びその製造方法の提供。【解決手段】セラミックス原料粉末に対して分散剤及び溶媒が添加されて得られたスラリーに対するエルトリエーションによって原料粉末の一部を沈降させることにより、前記スラリーの上澄みを回収し、前記上澄みに含まれている原料粉末を成形することにより成形体を作製し、前記成形体を焼成することにより焼結体を作製するセラミックス焼結体の製造方法。前記エルトリエーションによって、初期粒径分布において累積ｘ％となる基準粒径より大径の原料粉末のうち、ｙ％以上の原料粉末が除去され、２次元プロット（ｘ、ｙ）が、第１指定領域Ｓ１又は第２指定領域Ｓ２に含まれるようにエルトリエーションが実施される。【選択図】図３
SINTERED COMPACT OF SILICON CARBIDE AND PRODUCING METHOD THEREOF
PROBLEM TO BE SOLVED: To provide a sintered compact of silicon carbide and a producing method thereof in which suppression of generation frequency of crack etc. due to baking shrinkage in a formed product is achieved.SOLUTION: There is provided a producing method of a ceramic sintered compact in which, by precipitating a part of ingredient powder with elutriation subjected to slurry obtained from supplementation of distribution agent and solvent to ceramic ingredient powder, supernatant of the slurry is recovered, then a formed product is produced by forming a cake of the ingredient powder in the supernatant, and the formed product is subjected to calcination. Due to the elutriation, y% or more of ingredient powder among ingredient powder having a larger diameter than criterion particle diameter to be x% as accumulation in early stage particle diameter distribution is removed. The elutriation is carried out so that 2 dimensional plot (x, y) is positioned in first specified region S1 or second specified region S2.
【課題】成形体の焼成収縮に由来するクラック等の発生頻度抑制が図られている炭化珪素質焼結体及びその製造方法の提供。【解決手段】セラミックス原料粉末に対して分散剤及び溶媒が添加されて得られたスラリーに対するエルトリエーションによって原料粉末の一部を沈降させることにより、前記スラリーの上澄みを回収し、前記上澄みに含まれている原料粉末を成形することにより成形体を作製し、前記成形体を焼成することにより焼結体を作製するセラミックス焼結体の製造方法。前記エルトリエーションによって、初期粒径分布において累積ｘ％となる基準粒径より大径の原料粉末のうち、ｙ％以上の原料粉末が除去され、２次元プロット（ｘ、ｙ）が、第１指定領域Ｓ１又は第２指定領域Ｓ２に含まれるようにエルトリエーションが実施される。【選択図】図３
SINTERED COMPACT OF SILICON CARBIDE AND PRODUCING METHOD THEREOF
炭化珪素質焼結体およびその製造方法
NAKAMURA HIROAKI (Autor:in) / ASANO TOMOYUKI (Autor:in)
09.07.2015
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2024
METHOD FOR PRODUCING SILICON CARBIDE SINTERED COMPACT
| Europäisches Patentamt | 2015
| Europäisches Patentamt | 2015
REACTIVE SINTERED SILICON CARBIDE SINTERED COMPACT AND METHOD FOR PRODUCING THE SAME
| Europäisches Patentamt | 2022