MULTIFUNCTIONAL ADMIXTURE FOR CONCRETE
PROBLEM TO BE SOLVED: To provide a multifunctional admixture for a concrete capable of solving simultaneously and at a satisfactorily low cost, three problems: 1) a concrete prepared using a Portland blast furnace cement containing a blast furnace slag fine powder has a low fluidity retention (slump retention) with time after being prepared; 2) a hardened body obtained by hardening a concrete prepared using a Portland blast furnace cement containing a large amount of a blast furnace slag fine powder has a low compression strength; and 3) when a concrete prepared using a Portland blast furnace cement containing a large amount of a blast furnace slag fine powder is subjected to a thermal history by which the temperature of the concrete is elevated by heat-generation thereof in a process in which the concrete is hardened through a hydration reaction thereof, compression strength is deteriorated.SOLUTION: The multifunctional admixture for a concrete is prepared by blending a specified water-soluble vinyl copolymer, a specified water-soluble dextrin compound, and a specified hydroquinone in a specified blending ratio.
【課題】１）高炉スラグ微粉末を含有する高炉セメントを用いて調製したコンクリートは、調製後の経時的な流動保持性（スランプ保持性）が低い、２）高炉スラグ微粉末を多く含有する高炉セメントを用いて調製したコンクリートは、得られる硬化体の圧縮強度が低い、３）高炉スラグ微粉末を多く含有する高炉セメントを用いて調製したコンクリートは、調製したコンクリートが水和反応により硬化する過程で発熱により温度上昇する熱履歴を受けると、得られるコンクリート硬化体の圧縮強度が低下する、以上の１）〜３）の三つの課題を同時に且つ充分に低コストで解決できるコンクリート用多機能混和剤を提供する。【解決手段】コンクリート用多機能混和剤として、特定の水溶性ビニル共重合体、特定の水溶性デキストリン化合物及び特定のハイドロキノン類を特定割合で含有して成るものを用いた。【選択図】なし
MULTIFUNCTIONAL ADMIXTURE FOR CONCRETE
PROBLEM TO BE SOLVED: To provide a multifunctional admixture for a concrete capable of solving simultaneously and at a satisfactorily low cost, three problems: 1) a concrete prepared using a Portland blast furnace cement containing a blast furnace slag fine powder has a low fluidity retention (slump retention) with time after being prepared; 2) a hardened body obtained by hardening a concrete prepared using a Portland blast furnace cement containing a large amount of a blast furnace slag fine powder has a low compression strength; and 3) when a concrete prepared using a Portland blast furnace cement containing a large amount of a blast furnace slag fine powder is subjected to a thermal history by which the temperature of the concrete is elevated by heat-generation thereof in a process in which the concrete is hardened through a hydration reaction thereof, compression strength is deteriorated.SOLUTION: The multifunctional admixture for a concrete is prepared by blending a specified water-soluble vinyl copolymer, a specified water-soluble dextrin compound, and a specified hydroquinone in a specified blending ratio.
【課題】１）高炉スラグ微粉末を含有する高炉セメントを用いて調製したコンクリートは、調製後の経時的な流動保持性（スランプ保持性）が低い、２）高炉スラグ微粉末を多く含有する高炉セメントを用いて調製したコンクリートは、得られる硬化体の圧縮強度が低い、３）高炉スラグ微粉末を多く含有する高炉セメントを用いて調製したコンクリートは、調製したコンクリートが水和反応により硬化する過程で発熱により温度上昇する熱履歴を受けると、得られるコンクリート硬化体の圧縮強度が低下する、以上の１）〜３）の三つの課題を同時に且つ充分に低コストで解決できるコンクリート用多機能混和剤を提供する。【解決手段】コンクリート用多機能混和剤として、特定の水溶性ビニル共重合体、特定の水溶性デキストリン化合物及び特定のハイドロキノン類を特定割合で含有して成るものを用いた。【選択図】なし
MULTIFUNCTIONAL ADMIXTURE FOR CONCRETE
コンクリート用多機能混和剤
KINOSHITA MITSUO (Autor:in) / KURODA MOE (Autor:in)
20.08.2015
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
/
C08K
Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe
,
USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
/
C08L
COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
,
Massen auf Basis makromolekularer Verbindungen
Multifunctional polycarboxylic acid concrete admixture and preparation method thereof
| Europäisches Patentamt | 2021
Calcium nitrate - A multifunctional admixture for high performance concrete
| British Library Conference Proceedings | 1999