MULTIFUNCTIONAL ADMIXTURE FOR CONCRETE
PROBLEM TO BE SOLVED: To provide a multifunctional admixture for concrete which can solve simultaneously and sufficiently the following four problems in preparation of concrete having a small unit cement content, especially in preparation of concrete having a small cement content using blast furnace cement: 1) temporal retention of fluidity after preparation is not good; 2) material separation due to sedimentation of aggregates occurs easily and a generation rate of bleeding water is high; 3) strength enhancement at medium- to long-term material age is small; and 4) a number of voids are generated on the surface of an obtained hardened body by vibration compaction when filling the concrete after preparation, resulting in poor appearance.SOLUTION: The multifunctional admixture comprises the following four components A to D, in a specific ratio: a component A is a specific water-soluble vinyl copolymer; a component B is an alkali metal salt of a specific acrylic acid homopolymer; a component C is selected from sucrose, trehalose, lactose, and maltose; and a component D is a specific aliphatic polyether.
【課題】単位セメント量の少ないコンクリートの調製において、特に高炉セメントを用いた単位セメント量の少ないコンクリートの調製において、１）調製後の経時的な流動保持性がよくない、２）骨材の沈降による材料分離が起こり易く、ブリーディング水の発生量が多い、３）中長期材齢の強度増進性が小さい、４）調製後のコンクリートを充填する際の振動締め固めによって、得られる硬化体の表面にボイドが数多く発生し、外観がよくない、以上の四つの課題を同時に且つ充分に解決することができるコンクリート用多機能混和剤を提供する。【解決手段】Ａ成分として特定の水溶性ビニル共重合体、Ｂ成分として特定のアクリル酸単独重合体のアルカリ金属塩、Ｃ成分としてスクロース、トレハロース、ラクトース及びマルトースから選ばれるもの、Ｄ成分として特定の脂肪族ポリエーテル、以上のＡ〜Ｄの四成分を特定割合で含有して成るものを多機能混和剤として用いた。【選択図】なし
MULTIFUNCTIONAL ADMIXTURE FOR CONCRETE
PROBLEM TO BE SOLVED: To provide a multifunctional admixture for concrete which can solve simultaneously and sufficiently the following four problems in preparation of concrete having a small unit cement content, especially in preparation of concrete having a small cement content using blast furnace cement: 1) temporal retention of fluidity after preparation is not good; 2) material separation due to sedimentation of aggregates occurs easily and a generation rate of bleeding water is high; 3) strength enhancement at medium- to long-term material age is small; and 4) a number of voids are generated on the surface of an obtained hardened body by vibration compaction when filling the concrete after preparation, resulting in poor appearance.SOLUTION: The multifunctional admixture comprises the following four components A to D, in a specific ratio: a component A is a specific water-soluble vinyl copolymer; a component B is an alkali metal salt of a specific acrylic acid homopolymer; a component C is selected from sucrose, trehalose, lactose, and maltose; and a component D is a specific aliphatic polyether.
【課題】単位セメント量の少ないコンクリートの調製において、特に高炉セメントを用いた単位セメント量の少ないコンクリートの調製において、１）調製後の経時的な流動保持性がよくない、２）骨材の沈降による材料分離が起こり易く、ブリーディング水の発生量が多い、３）中長期材齢の強度増進性が小さい、４）調製後のコンクリートを充填する際の振動締め固めによって、得られる硬化体の表面にボイドが数多く発生し、外観がよくない、以上の四つの課題を同時に且つ充分に解決することができるコンクリート用多機能混和剤を提供する。【解決手段】Ａ成分として特定の水溶性ビニル共重合体、Ｂ成分として特定のアクリル酸単独重合体のアルカリ金属塩、Ｃ成分としてスクロース、トレハロース、ラクトース及びマルトースから選ばれるもの、Ｄ成分として特定の脂肪族ポリエーテル、以上のＡ〜Ｄの四成分を特定割合で含有して成るものを多機能混和剤として用いた。【選択図】なし
MULTIFUNCTIONAL ADMIXTURE FOR CONCRETE
コンクリート用多機能混和剤
KINOSHITA MITSUO (Autor:in) / SAITO KAZUHIDE (Autor:in) / TOKUHASHI KAZUKI (Autor:in)
22.10.2015
Patent
Elektronische Ressource
Japanisch
Multifunctional polycarboxylic acid concrete admixture and preparation method thereof
| Europäisches Patentamt | 2021
Calcium nitrate - A multifunctional admixture for high performance concrete
| British Library Conference Proceedings | 1999