DIELECTRIC CERAMIC COMPOSITION AND CERAMIC ELECTRONIC COMPONENT COMPRISING THE SAME
PROBLEM TO BE SOLVED: To provide a dielectric ceramic composition that has a high insulation resistance and has a capacity temperature characteristic satisfying the X9R characteristic of the EIA standard.SOLUTION: The dielectric ceramic composition is provided that contains as a main component, barium calcium titanate represented by a composition formula BaCaTiO(x is 0.05 or more and 0.1 or less) and as an accessory component, an oxide of Y and an oxide of Yb. In the dielectric ceramic composition, the content of the Y oxide is 0.5 to 2 mol in terms of YOwith respect to 100 mol of barium calcium titanate, the content of the oxide of Yb is 0.5 to 2 mol in terms of YbOwith respect to 100 mol of barium calcium titanate, and the average particle size is 0.3 μm or more. Further, a dielectric magnetic composition is provided that is identical to the above dielectric magnetic composition except that dielectric magnetic composition is preferably a core-shell structure.SELECTED DRAWING: None
【課題】絶縁抵抗が高く、かつ容量温度特性がＥＩＡ規格のＸ９Ｒ特性を満たす誘電体磁器組成物の提供。【解決手段】主成分として組成式Ｂａ（１−ｘ）ＣａｘＴｉＯ３（ｘは０．０５以上０．１以下である）で表されるチタン酸バリウムカルシウムを含み、副成分としてＹの酸化物、およびＹｂの酸化物を含む誘電体磁器組成物であって、前記Ｙの酸化物の含有量は、チタン酸バリウムカルシウム１００ｍｏｌに対して、Ｙ２Ｏ３換算で０．５〜２ｍｏｌであり、前記Ｙｂの酸化物の含有量は、チタン酸バリウムカルシウム１００ｍｏｌに対して、Ｙｂ２Ｏ３換算で０．５〜２ｍｏｌであり、平均粒径が０．３μｍ以上である、誘電体磁器組成物。更にコア−シェル構造であることが好ましい誘電体磁気組成物。【選択図】なし
DIELECTRIC CERAMIC COMPOSITION AND CERAMIC ELECTRONIC COMPONENT COMPRISING THE SAME
PROBLEM TO BE SOLVED: To provide a dielectric ceramic composition that has a high insulation resistance and has a capacity temperature characteristic satisfying the X9R characteristic of the EIA standard.SOLUTION: The dielectric ceramic composition is provided that contains as a main component, barium calcium titanate represented by a composition formula BaCaTiO(x is 0.05 or more and 0.1 or less) and as an accessory component, an oxide of Y and an oxide of Yb. In the dielectric ceramic composition, the content of the Y oxide is 0.5 to 2 mol in terms of YOwith respect to 100 mol of barium calcium titanate, the content of the oxide of Yb is 0.5 to 2 mol in terms of YbOwith respect to 100 mol of barium calcium titanate, and the average particle size is 0.3 μm or more. Further, a dielectric magnetic composition is provided that is identical to the above dielectric magnetic composition except that dielectric magnetic composition is preferably a core-shell structure.SELECTED DRAWING: None
【課題】絶縁抵抗が高く、かつ容量温度特性がＥＩＡ規格のＸ９Ｒ特性を満たす誘電体磁器組成物の提供。【解決手段】主成分として組成式Ｂａ（１−ｘ）ＣａｘＴｉＯ３（ｘは０．０５以上０．１以下である）で表されるチタン酸バリウムカルシウムを含み、副成分としてＹの酸化物、およびＹｂの酸化物を含む誘電体磁器組成物であって、前記Ｙの酸化物の含有量は、チタン酸バリウムカルシウム１００ｍｏｌに対して、Ｙ２Ｏ３換算で０．５〜２ｍｏｌであり、前記Ｙｂの酸化物の含有量は、チタン酸バリウムカルシウム１００ｍｏｌに対して、Ｙｂ２Ｏ３換算で０．５〜２ｍｏｌであり、平均粒径が０．３μｍ以上である、誘電体磁器組成物。更にコア−シェル構造であることが好ましい誘電体磁気組成物。【選択図】なし
DIELECTRIC CERAMIC COMPOSITION AND CERAMIC ELECTRONIC COMPONENT COMPRISING THE SAME
誘電体磁器組成物およびそれを含むセラミック電子部品
YAMAGUCHI KEN (Autor:in) / SHIMIZU MASAYOSHI (Autor:in) / HATAKE KOTARO (Autor:in)
29.06.2017
Patent
Elektronische Ressource
Japanisch
Dielectric Composition and Ceramic Electronic Component Comprising the Same
Europäisches Patentamt | 2015
Dielectric Composition and Ceramic Electronic Component Comprising the Same
Europäisches Patentamt | 2020
Dielectric Composition and Ceramic Electronic Component Comprising the Same
Europäisches Patentamt | 2016
Dielectric Composition and Ceramic Electronic Component Comprising the Same
| Europäisches Patentamt | 2019
CERAMIC ELECTRONIC COMPONENT AND DIELECTRIC CERAMIC COMPOSITION
Europäisches Patentamt | 2018