METHOD FOR FIRING CEMENT CLINKER AND FIRING DEVICE
PROBLEM TO BE SOLVED: To increase the content of SOin a cement clinker while maintaining the stable driving of a cement firing device.SOLUTION: Provided is a method for firing a cement clinker where, when gypsum is blown from the aisle of a cement kiln via a blowing nozzle, the average blowing position of the gypsum is controlled to the region of 1,300°C or higher to lower than 1,400°C of the cement kiln. In the case the firing temperature is 1,300 to 1,400°C, a large part of the SOin the gypsum enters into a solid solution in the clinker, and, in the case the firing temperature is 1,450°C, there hardly occurs a change in the content of the SOin the clinker before and after the firing, and a large part of the SOin the gypsum volatiles. By controlling the blowing speed in the blowing nozzle, the average blowing position of the gypsum can reach the above-mentioned region, and after the crushing or granulation of the fine grains, the blowing can be performed in such a manner that the average blowing position of the gypsum reaches the above-mentioned region via the blowing nozzle.SELECTED DRAWING: Figure 1
【課題】セメント焼成装置の安定運転を維持しながら、セメントクリンカのＳＯ3含有率を高める。【解決手段】セメントキルンの窯前から吹き込みノズルを介して石膏を吹き込むにあたり、該石膏の平均吹き込み位置を該セメントキルンの１３００℃以上１４００℃未満の領域とするセメントクリンカの焼成方法。焼成温度が１３００℃〜１４００℃の場合には、石膏中のＳＯ3の大部分がクリンカへ固溶し、焼成温度が１４５０℃の場合には、焼成前後でクリンカのＳＯ3含有率にあまり変化がなく、石膏中のＳＯ3の大部分が揮発してしまう。吹き込みノズルにおける吹き込み速度を調整することで石膏の平均吹き込み位置を前記領域にすることができ、細粒を粉砕又は造粒した後、吹き込みノズルを介して石膏の平均吹き込み位置が前記領域になるように吹き込むことができる。【選択図】図１
METHOD FOR FIRING CEMENT CLINKER AND FIRING DEVICE
PROBLEM TO BE SOLVED: To increase the content of SOin a cement clinker while maintaining the stable driving of a cement firing device.SOLUTION: Provided is a method for firing a cement clinker where, when gypsum is blown from the aisle of a cement kiln via a blowing nozzle, the average blowing position of the gypsum is controlled to the region of 1,300°C or higher to lower than 1,400°C of the cement kiln. In the case the firing temperature is 1,300 to 1,400°C, a large part of the SOin the gypsum enters into a solid solution in the clinker, and, in the case the firing temperature is 1,450°C, there hardly occurs a change in the content of the SOin the clinker before and after the firing, and a large part of the SOin the gypsum volatiles. By controlling the blowing speed in the blowing nozzle, the average blowing position of the gypsum can reach the above-mentioned region, and after the crushing or granulation of the fine grains, the blowing can be performed in such a manner that the average blowing position of the gypsum reaches the above-mentioned region via the blowing nozzle.SELECTED DRAWING: Figure 1
【課題】セメント焼成装置の安定運転を維持しながら、セメントクリンカのＳＯ3含有率を高める。【解決手段】セメントキルンの窯前から吹き込みノズルを介して石膏を吹き込むにあたり、該石膏の平均吹き込み位置を該セメントキルンの１３００℃以上１４００℃未満の領域とするセメントクリンカの焼成方法。焼成温度が１３００℃〜１４００℃の場合には、石膏中のＳＯ3の大部分がクリンカへ固溶し、焼成温度が１４５０℃の場合には、焼成前後でクリンカのＳＯ3含有率にあまり変化がなく、石膏中のＳＯ3の大部分が揮発してしまう。吹き込みノズルにおける吹き込み速度を調整することで石膏の平均吹き込み位置を前記領域にすることができ、細粒を粉砕又は造粒した後、吹き込みノズルを介して石膏の平均吹き込み位置が前記領域になるように吹き込むことができる。【選択図】図１
METHOD FOR FIRING CEMENT CLINKER AND FIRING DEVICE
セメントクリンカの焼成方法及び焼成装置
NIIJIMA SHUN (Autor:in) / YOSHIKAWA TOMOHISA (Autor:in)
10.08.2017
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
CEMENT FIRING APPARATUS AND METHOD FOR CEMENT CLINKER BURNING
| Europäisches Patentamt | 2018
CEMENT RAW MATERIAL FIRING DEVICE AND MANUFACTURING METHOD OF CEMENT CLINKER
| Europäisches Patentamt | 2021
Electric heating cement clinker firing system and method
| Europäisches Patentamt | 2022
| Engineering Index Backfile | 1944