CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR AND SOIL IMPROVEMENT METHOD
PROBLEM TO BE SOLVED: To provide a cement composition capable of sufficiently effectively using wastes and industrial by-products as a part of raw materials and having improved slurry viscosity while using environmental load reduction clinker which can effectively reduce COgeneration amount during manufacturing processes.SOLUTION: The cement composition contains cement clinker, gypsum, a pulverization auxiliary agent, a dispersant. The cement clinker has hydraulic modulus (HM) of 1.75 to 2.20, silica modulus (SM) of 1.30 or more and less than 2.50, iron modulus (IM) of 2.0 to 10.0, CA amount of 12 mass% or more, CAF amount of 5 to 11 mass%, which are calculated by Bogue equation. Content of the pulverization auxiliary agent is 1 pts.mass or less based on total 100 pts.mass of the cement clinker and the gypsum.SELECTED DRAWING: Figure 1
【課題】原料の一部として廃棄物や産業副産物を十分に有効利用できるとともに製造過程におけるＣＯ２発生量を十分に低減できる環境負荷低減クリンカーを使用しながら、スラリー粘性の改善されたセメント組成物を提供する。【解決手段】本発明に係るセメント組成物は、セメントクリンカーと、石膏と、粉砕助剤と、分散剤とを含む。セメントクリンカーは水硬率（ＨＭ）が１．７５〜２．２０、ケイ酸率（ＳＭ）が１．３０以上２．５０未満、鉄率（ＩＭ）が２．０〜１０．０であり且つボーグ式にて算定されるＣ３Ａ量が１２質量％以上、Ｃ４ＡＦ量が５〜１１質量％である。粉砕助剤の含有量は、セメントクリンカーと石膏との合計１００質量部に対して１質量部以下である。【選択図】図１
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR AND SOIL IMPROVEMENT METHOD
PROBLEM TO BE SOLVED: To provide a cement composition capable of sufficiently effectively using wastes and industrial by-products as a part of raw materials and having improved slurry viscosity while using environmental load reduction clinker which can effectively reduce COgeneration amount during manufacturing processes.SOLUTION: The cement composition contains cement clinker, gypsum, a pulverization auxiliary agent, a dispersant. The cement clinker has hydraulic modulus (HM) of 1.75 to 2.20, silica modulus (SM) of 1.30 or more and less than 2.50, iron modulus (IM) of 2.0 to 10.0, CA amount of 12 mass% or more, CAF amount of 5 to 11 mass%, which are calculated by Bogue equation. Content of the pulverization auxiliary agent is 1 pts.mass or less based on total 100 pts.mass of the cement clinker and the gypsum.SELECTED DRAWING: Figure 1
【課題】原料の一部として廃棄物や産業副産物を十分に有効利用できるとともに製造過程におけるＣＯ２発生量を十分に低減できる環境負荷低減クリンカーを使用しながら、スラリー粘性の改善されたセメント組成物を提供する。【解決手段】本発明に係るセメント組成物は、セメントクリンカーと、石膏と、粉砕助剤と、分散剤とを含む。セメントクリンカーは水硬率（ＨＭ）が１．７５〜２．２０、ケイ酸率（ＳＭ）が１．３０以上２．５０未満、鉄率（ＩＭ）が２．０〜１０．０であり且つボーグ式にて算定されるＣ３Ａ量が１２質量％以上、Ｃ４ＡＦ量が５〜１１質量％である。粉砕助剤の含有量は、セメントクリンカーと石膏との合計１００質量部に対して１質量部以下である。【選択図】図１
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR AND SOIL IMPROVEMENT METHOD
セメント組成物及びその製造方法、並びに地盤改良方法
ITO TAKAYASU (Autor:in) / SASAKI REI (Autor:in)
05.07.2018
Patent
Elektronische Ressource
Japanisch