GYPSUM AND MANUFACTURING METHOD THEREFOR, CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR, AND FOUNDATION IMPROVEMENT MATERIAL
To provide a manufacturing method of gypsum constituting a cement composition together with cement clinker by adding to the cement clinker, useful for sufficiently suppressing elution of hexavalent chromium from a cured body of the cement composition even when chromium content in the cement clinker is relatively high.SOLUTION: The manufacturing method of gypsum is a method for manufacturing gypsum via a gas liquid contact process of a gas containing sulfur dioxide and a slurry containing at least calcium sulfide and calcium hydroxide, in which amount of the calcium hydroxide contained in the slurry is 0.2 to 10 pts.mass based on 100 pts.mass of amount of the calcium sulfide contained in the slurry, and the gypsum has percentage content of the sulfur dioxide quantified according to a method described in JIS R9101-1995 of 0.5 to 15 mass%.SELECTED DRAWING: Figure 1
【課題】セメントクリンカーに添加され、セメントクリンカーとともにセメント組成物を構成する石膏の製造方法であって、セメントクリンカーのクロム含有量が比較的高くても、セメント組成物の硬化体から六価クロムの溶出を十分に抑制するのに有用な石膏の製造方法を提供する。【解決手段】本発明に係る石膏の製造方法は、二酸化硫黄を含有するガスと、硫酸カルシウム及び水酸化カルシウムを少なくとも含むスラリーとの気液接触工程を経て石膏を製造する方法であり、スラリーに含まれる硫酸カルシウムの量を１００質量部とすると、スラリーに含まれる水酸化カルシウムの量が０．２〜１０質量部であり、石膏はＪＩＳ Ｒ９１０１−１９９５に記載の方法に準拠して定量される二酸化硫黄の含有率が０．５〜１５質量％である。【選択図】図１
GYPSUM AND MANUFACTURING METHOD THEREFOR, CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR, AND FOUNDATION IMPROVEMENT MATERIAL
To provide a manufacturing method of gypsum constituting a cement composition together with cement clinker by adding to the cement clinker, useful for sufficiently suppressing elution of hexavalent chromium from a cured body of the cement composition even when chromium content in the cement clinker is relatively high.SOLUTION: The manufacturing method of gypsum is a method for manufacturing gypsum via a gas liquid contact process of a gas containing sulfur dioxide and a slurry containing at least calcium sulfide and calcium hydroxide, in which amount of the calcium hydroxide contained in the slurry is 0.2 to 10 pts.mass based on 100 pts.mass of amount of the calcium sulfide contained in the slurry, and the gypsum has percentage content of the sulfur dioxide quantified according to a method described in JIS R9101-1995 of 0.5 to 15 mass%.SELECTED DRAWING: Figure 1
【課題】セメントクリンカーに添加され、セメントクリンカーとともにセメント組成物を構成する石膏の製造方法であって、セメントクリンカーのクロム含有量が比較的高くても、セメント組成物の硬化体から六価クロムの溶出を十分に抑制するのに有用な石膏の製造方法を提供する。【解決手段】本発明に係る石膏の製造方法は、二酸化硫黄を含有するガスと、硫酸カルシウム及び水酸化カルシウムを少なくとも含むスラリーとの気液接触工程を経て石膏を製造する方法であり、スラリーに含まれる硫酸カルシウムの量を１００質量部とすると、スラリーに含まれる水酸化カルシウムの量が０．２〜１０質量部であり、石膏はＪＩＳ Ｒ９１０１−１９９５に記載の方法に準拠して定量される二酸化硫黄の含有率が０．５〜１５質量％である。【選択図】図１
GYPSUM AND MANUFACTURING METHOD THEREFOR, CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR, AND FOUNDATION IMPROVEMENT MATERIAL
石膏及びその製造方法、セメント組成物及びその製造方法、ならびに地盤改良材
ITO TAKAYASU (Autor:in) / NAKAMOTO KAZUHIKO (Autor:in) / MATSUMOTO MASAHIRO (Autor:in) / SAKAI TETSUHIRO (Autor:in)
24.01.2019
Patent
Elektronische Ressource
Japanisch
IPC:
C01F
COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
,
Verbindungen der Metalle Beryllium, Magnesium, Aluminium, Calcium, Strontium, Barium, Radium, Thorium oder der Seltenen Erden
/
C04B
Kalk
,
LIME
/
C09K
Materialien für Anwendungen, soweit nicht anderweitig vorgesehen
,
MATERIALS FOR APPLICATIONS NOT OTHERWISE PROVIDED FOR
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR AND SOIL IMPROVEMENT METHOD
| Europäisches Patentamt | 2018
COMPOSITION, MANUFACTURING METHOD THEREFOR, AND CEMENT MANUFACTURING METHOD
| Europäisches Patentamt | 2024