THE MANUFACTURING METHOD OF HIGH PURITY ALUMINA CERAMIC BALLS USING WASTE ALUMINUM DROSS
The present invention relates to a method for manufacturing a high-purity alumina ceramic ball with waste aluminum dross. More specifically, the method includes: a first step of recovering aluminum hydroxide from the waste aluminum dross; a second step of grinding and sintering the recovered aluminum hydroxide to prepare aluminum powder; a third step of mixing the aluminum powder, an inorganic binder, an organic binder, and a solvent to prepare ceramic granules and producing a ceramic ball through a refining process; a fourth step of drying the produced ceramic ball; a fifth step of calcining the dried ceramic ball at 800 to 1000°C; and a sixth step of firing the heat-treated ceramic ball at 1500 to 1700°C. The present invention can effectively recover the aluminum metal from the waste aluminum dross to prepare the high-purity alumina and manufacture the high-purity alumina ceramic ball by using the same. The present invention can minimize the amount of the dross by recycling the waste aluminum dross and reduce the industrial waste treatment cost and protect the environment accordingly. The present invention can also reduce the ceramic ball manufacturing costs and manufacture the high-purity alumina ceramic ball which is eco-friendly and economical.
본 발명은 알루미늄 폐드로스를 이용한 고순도 알루미나 세라믹볼의 제조방법에 관한 것으로, 보다 구체적으로는 알루미늄 폐드로스로부터 수산화알루미늄을 회수하는 제1단계; 상기 회수된 수산화알루미늄을 분쇄한 후, 소결하여 알루미나 파우더를 제조하는 제2단계; 상기 알루미나 파우더와, 무기바인더, 유기바인더 및 수용제를 혼합하여 세라믹스 과립체를 제조하고 정환하여 세라믹볼을 제조하는 제3단계; 상기 제조된 세라믹볼을 건조시키는 제4단계; 상기 건조된 세라믹볼을 800~1000℃에서 하소하는 제5단계; 및 상기 열처리된 세라믹볼을 1500~1700℃에서 소성하는 제6단계를 포함하는 것을 특징으로 하는, 알루미늄 폐드로스를 이용한 고순도 알루미나 세라믹볼의 제조방법이 제공된다. 본 발명에 따르면, 폐기되는 알루미늄 드로스로부터 알루미늄 금속을 효과적으로 회수하여 고순도 알루미나를 제조하고 이를 이용하여 고순도 알루미나 세라믹볼을 제조할 수 있게 되어, 폐기되는 알루미늄 드로스를 재활용함에 따라 드로스 최소화로 인한 산업폐기물 처리비용의 저감 및 환경보호효과를 얻을 수 있게 될 뿐만 아니라, 세라믹볼의 제조원가를 절감하여 친환경적이고 경제적으로 고부가가치를 갖는 고순도 알루미나 세라믹볼을 제조할 수 있게 된다.
THE MANUFACTURING METHOD OF HIGH PURITY ALUMINA CERAMIC BALLS USING WASTE ALUMINUM DROSS
The present invention relates to a method for manufacturing a high-purity alumina ceramic ball with waste aluminum dross. More specifically, the method includes: a first step of recovering aluminum hydroxide from the waste aluminum dross; a second step of grinding and sintering the recovered aluminum hydroxide to prepare aluminum powder; a third step of mixing the aluminum powder, an inorganic binder, an organic binder, and a solvent to prepare ceramic granules and producing a ceramic ball through a refining process; a fourth step of drying the produced ceramic ball; a fifth step of calcining the dried ceramic ball at 800 to 1000°C; and a sixth step of firing the heat-treated ceramic ball at 1500 to 1700°C. The present invention can effectively recover the aluminum metal from the waste aluminum dross to prepare the high-purity alumina and manufacture the high-purity alumina ceramic ball by using the same. The present invention can minimize the amount of the dross by recycling the waste aluminum dross and reduce the industrial waste treatment cost and protect the environment accordingly. The present invention can also reduce the ceramic ball manufacturing costs and manufacture the high-purity alumina ceramic ball which is eco-friendly and economical.
본 발명은 알루미늄 폐드로스를 이용한 고순도 알루미나 세라믹볼의 제조방법에 관한 것으로, 보다 구체적으로는 알루미늄 폐드로스로부터 수산화알루미늄을 회수하는 제1단계; 상기 회수된 수산화알루미늄을 분쇄한 후, 소결하여 알루미나 파우더를 제조하는 제2단계; 상기 알루미나 파우더와, 무기바인더, 유기바인더 및 수용제를 혼합하여 세라믹스 과립체를 제조하고 정환하여 세라믹볼을 제조하는 제3단계; 상기 제조된 세라믹볼을 건조시키는 제4단계; 상기 건조된 세라믹볼을 800~1000℃에서 하소하는 제5단계; 및 상기 열처리된 세라믹볼을 1500~1700℃에서 소성하는 제6단계를 포함하는 것을 특징으로 하는, 알루미늄 폐드로스를 이용한 고순도 알루미나 세라믹볼의 제조방법이 제공된다. 본 발명에 따르면, 폐기되는 알루미늄 드로스로부터 알루미늄 금속을 효과적으로 회수하여 고순도 알루미나를 제조하고 이를 이용하여 고순도 알루미나 세라믹볼을 제조할 수 있게 되어, 폐기되는 알루미늄 드로스를 재활용함에 따라 드로스 최소화로 인한 산업폐기물 처리비용의 저감 및 환경보호효과를 얻을 수 있게 될 뿐만 아니라, 세라믹볼의 제조원가를 절감하여 친환경적이고 경제적으로 고부가가치를 갖는 고순도 알루미나 세라믹볼을 제조할 수 있게 된다.
THE MANUFACTURING METHOD OF HIGH PURITY ALUMINA CERAMIC BALLS USING WASTE ALUMINUM DROSS
알루미늄 폐드로스를 이용한 고순도 알루미나 세라믹볼의 제조방법
KIM BYUNG GOOK (Autor:in) / KANG SUNG JIN (Autor:in) / PARK CHI KYUN (Autor:in)
25.06.2015
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
Europäisches Patentamt | 2021
| Europäisches Patentamt | 2020
Aluminum dross brick preparation method based on aluminum dross brick preparation device
| Europäisches Patentamt | 2021
High-purity alumina corundum ceramic metallization method
| Europäisches Patentamt | 2021
Insulation material containing waste perlite and aluminum dross and manufacturing process thereof
| Europäisches Patentamt | 2024