Zirconia powder having black color laminate pattern ceramic sintered body using the powder and method for manufacturing the same
The present invention relates to a zirconia powder having black color enabling manufacture of sintered ceramic bodies with various colors, a sintered laminate pattern ceramic body using the same, and a manufacturing method thereof. More specifically, the zirconia powder is manufactured by mixing, drying, primary sintering, pulverization, molding, and secondary sintering of a powder in which 92.6 wt% of yttria-stabilized zirconia having a white color, 1.6 wt% of silicon dioxide, 2.8 wt% of aluminum oxide, and 3 wt% of a binder, or 72.6 wt% of zirconia having a white color, 1.6% by weight of silicon, 2.8% by weight of aluminum oxide, 3% by weight of a binder, and 20% by weight of black pigment.
본 발명은 블랙색상을 갖는 지르코니아 파우더와 그 파우더를 이용한 라미네이트 패턴 세라믹 소결체 및 그 제조방법에 관한 것으로, 더욱 자세하게는 화이트색상을 갖는 이트리아 안정화 지르코니아(zirconia) 92.6중량%, 이산화규소(JPEGpat00049.jpg48) 1.6중량%, 산화알루미늄(JPEGpat00050.jpg410) 2.8중량%, 바인더 3중량% 또는 화이트색상을 갖는 지르코니아 72.6중량%, 이산화규소(JPEGpat00051.jpg48) 1.6중량%, 산화알루미늄(JPEGpat00052.jpg410) 2.8중량%, 바인더 3중량%, 흑색 색상을 갖는 안료 20중량%으로 혼합한 파우더를 혼합, 건조, 제1차소결, 분쇄, 성형, 제2차소결을 통해, 화이트 또는 블랙색상을 갖는 지르코니아 파우더를 이용한 라미네이트 패턴 세라믹 소결체를 제조함으로써, 최적의 혼합조건과 최적의 제조조건을 통해, 다양한 색상을 갖는 세라믹 소결체 제조가 가능함은 물론, 밀도, 강도, 열팽창계수, 크랙이 발생하지 않고 치밀한 조직을 갖는 세라믹 소결체를 얻을 수 있는 유용한 발명이다.
Zirconia powder having black color laminate pattern ceramic sintered body using the powder and method for manufacturing the same
The present invention relates to a zirconia powder having black color enabling manufacture of sintered ceramic bodies with various colors, a sintered laminate pattern ceramic body using the same, and a manufacturing method thereof. More specifically, the zirconia powder is manufactured by mixing, drying, primary sintering, pulverization, molding, and secondary sintering of a powder in which 92.6 wt% of yttria-stabilized zirconia having a white color, 1.6 wt% of silicon dioxide, 2.8 wt% of aluminum oxide, and 3 wt% of a binder, or 72.6 wt% of zirconia having a white color, 1.6% by weight of silicon, 2.8% by weight of aluminum oxide, 3% by weight of a binder, and 20% by weight of black pigment.
본 발명은 블랙색상을 갖는 지르코니아 파우더와 그 파우더를 이용한 라미네이트 패턴 세라믹 소결체 및 그 제조방법에 관한 것으로, 더욱 자세하게는 화이트색상을 갖는 이트리아 안정화 지르코니아(zirconia) 92.6중량%, 이산화규소(JPEGpat00049.jpg48) 1.6중량%, 산화알루미늄(JPEGpat00050.jpg410) 2.8중량%, 바인더 3중량% 또는 화이트색상을 갖는 지르코니아 72.6중량%, 이산화규소(JPEGpat00051.jpg48) 1.6중량%, 산화알루미늄(JPEGpat00052.jpg410) 2.8중량%, 바인더 3중량%, 흑색 색상을 갖는 안료 20중량%으로 혼합한 파우더를 혼합, 건조, 제1차소결, 분쇄, 성형, 제2차소결을 통해, 화이트 또는 블랙색상을 갖는 지르코니아 파우더를 이용한 라미네이트 패턴 세라믹 소결체를 제조함으로써, 최적의 혼합조건과 최적의 제조조건을 통해, 다양한 색상을 갖는 세라믹 소결체 제조가 가능함은 물론, 밀도, 강도, 열팽창계수, 크랙이 발생하지 않고 치밀한 조직을 갖는 세라믹 소결체를 얻을 수 있는 유용한 발명이다.
Zirconia powder having black color laminate pattern ceramic sintered body using the powder and method for manufacturing the same
블랙색상을 갖는 지르코니아 파우더와 그 파우더를 이용한 라미네이트 패턴 세라믹 소결체 및 그 제조방법
PARK MIN WOO (Autor:in)
16.09.2021
Patent
Elektronische Ressource
Koreanisch
Europäisches Patentamt | 2021
Europäisches Patentamt | 2021
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2022