METHOD OF PRODUCING TRANSPARENT CERAMIC OF YTTRIUM ALUMINIUM GARNET
FIELD: chemistry.SUBSTANCE: invention relates to method of producing transparent ceramic yttrium aluminium garnet (YAG), including doped with ions of rare-earth metals (Nd, Tm, Yb, Ho, Er), which can be used as active laser medium, or luminescence materials and scintillators (during doping by ions of Ce, Pr, Tb, Eu, Sm). In method of sol-gel method is obtained xerogel powders of approximate composition [YAlO(OH)(CHCOO)(NO)]·nHO, which is ground in planetary mill and sieved through sieve with mesh size of 100 mqm. Powder xerogel, passed through sieve, is placed in mold and compacted at pressure of 200 MPa. Obtained compact is heated at rate of 0.06 K/min to 600 °C, then at rate of 5 K/min to 1,200 °C in oxygen-containing atmosphere and kept at this temperature for 0.5 hours. Then compact is placed in vacuum furnace, heated at rate of 10 K/min to 1,800 °C and kept at this temperature for 4 hours. Obtained sample is annealed in air at 1,300 °C for 1 hour, then ground and polished at surfaces. Obtaining transparent ceramic yttrium aluminium garnet with transmission at wavelength of 1,064 nm 83.6 %, replacement of pure nano powder yttrium oxide with nano powder yttrium oxide doped with ions of rare-earth metals (Nd, Tm, Yb, Ho, Er, Ce, Pr, Sm, Eu, Tb) in amount of up to 10 mol%, obtained is ceramic YAG doped with ions of rare-earth elements and suitable for use as laser or scintillation material.EFFECT: technical result of invention consists in simplification of technology of ceramic YAG.1 cl, 2 ex
Изобретение относится к способу получения прозрачной керамики алюмоиттриевого граната (ИАГ), в том числе легированной ионами редкоземельных металлов (Nd, Yb, Tm, Но, Er), которая может быть использована в качестве активной лазерной среды, либо люминофоров и сцинтилляторов (при легировании ионами Ce, Pr, Tb, Eu, Sm). В способе золь-гель методом получают порошки ксерогеля примерного состава [YAlO(ОН)(СНСОО)(NO)]·nHO, которые подвергают размолу в планетарной мельнице и просеивают через сито с размером ячейки 100 мкм. Порошок ксерогеля, прошедшего через сито, помещают в пресс-форму и компактируют при давлении 200 МПа. Полученный компакт нагревают со скоростью 0,06 К/мин до 600°C, затем со скоростью 5 К/мин до 1200°C в кислородсодержащей атмосфере и выдерживают при этой температуре 0,5 часа. Затем компакт помещают в вакуумную печь, где нагревают со скоростью 10 К/мин до 1800°C и выдерживают при этой температуре 4 часа. Полученный образец отжигают на воздухе при температуре 1300°C 1 час, затем шлифуют и полируют поверхности. Получают прозрачную керамику алюмоиттриевого граната, имеющую пропускание на длине волны 1064 нм 83,6%, заменой чистого нанопорошка оксида иттрия нанопорошком оксида иттрия, легированного ионами редкоземельных металлов (Nd, Yb, Tm, Но, Er, Ce, Pr, Tb, Eu, Sm) в количестве до 10 мол.%, получают керамику ИАГ, легированную ионами редкоземельных элементов и пригодную для использования в качестве лазерного или сцинтилляционного материала. Технический результат от использования изобретения заключается в упрощении технологии керамики ИАГ. 2 пр.
METHOD OF PRODUCING TRANSPARENT CERAMIC OF YTTRIUM ALUMINIUM GARNET
FIELD: chemistry.SUBSTANCE: invention relates to method of producing transparent ceramic yttrium aluminium garnet (YAG), including doped with ions of rare-earth metals (Nd, Tm, Yb, Ho, Er), which can be used as active laser medium, or luminescence materials and scintillators (during doping by ions of Ce, Pr, Tb, Eu, Sm). In method of sol-gel method is obtained xerogel powders of approximate composition [YAlO(OH)(CHCOO)(NO)]·nHO, which is ground in planetary mill and sieved through sieve with mesh size of 100 mqm. Powder xerogel, passed through sieve, is placed in mold and compacted at pressure of 200 MPa. Obtained compact is heated at rate of 0.06 K/min to 600 °C, then at rate of 5 K/min to 1,200 °C in oxygen-containing atmosphere and kept at this temperature for 0.5 hours. Then compact is placed in vacuum furnace, heated at rate of 10 K/min to 1,800 °C and kept at this temperature for 4 hours. Obtained sample is annealed in air at 1,300 °C for 1 hour, then ground and polished at surfaces. Obtaining transparent ceramic yttrium aluminium garnet with transmission at wavelength of 1,064 nm 83.6 %, replacement of pure nano powder yttrium oxide with nano powder yttrium oxide doped with ions of rare-earth metals (Nd, Tm, Yb, Ho, Er, Ce, Pr, Sm, Eu, Tb) in amount of up to 10 mol%, obtained is ceramic YAG doped with ions of rare-earth elements and suitable for use as laser or scintillation material.EFFECT: technical result of invention consists in simplification of technology of ceramic YAG.1 cl, 2 ex
Изобретение относится к способу получения прозрачной керамики алюмоиттриевого граната (ИАГ), в том числе легированной ионами редкоземельных металлов (Nd, Yb, Tm, Но, Er), которая может быть использована в качестве активной лазерной среды, либо люминофоров и сцинтилляторов (при легировании ионами Ce, Pr, Tb, Eu, Sm). В способе золь-гель методом получают порошки ксерогеля примерного состава [YAlO(ОН)(СНСОО)(NO)]·nHO, которые подвергают размолу в планетарной мельнице и просеивают через сито с размером ячейки 100 мкм. Порошок ксерогеля, прошедшего через сито, помещают в пресс-форму и компактируют при давлении 200 МПа. Полученный компакт нагревают со скоростью 0,06 К/мин до 600°C, затем со скоростью 5 К/мин до 1200°C в кислородсодержащей атмосфере и выдерживают при этой температуре 0,5 часа. Затем компакт помещают в вакуумную печь, где нагревают со скоростью 10 К/мин до 1800°C и выдерживают при этой температуре 4 часа. Полученный образец отжигают на воздухе при температуре 1300°C 1 час, затем шлифуют и полируют поверхности. Получают прозрачную керамику алюмоиттриевого граната, имеющую пропускание на длине волны 1064 нм 83,6%, заменой чистого нанопорошка оксида иттрия нанопорошком оксида иттрия, легированного ионами редкоземельных металлов (Nd, Yb, Tm, Но, Er, Ce, Pr, Tb, Eu, Sm) в количестве до 10 мол.%, получают керамику ИАГ, легированную ионами редкоземельных элементов и пригодную для использования в качестве лазерного или сцинтилляционного материала. Технический результат от использования изобретения заключается в упрощении технологии керамики ИАГ. 2 пр.
METHOD OF PRODUCING TRANSPARENT CERAMIC OF YTTRIUM ALUMINIUM GARNET
СПОСОБ ПОЛУЧЕНИЯ ПРОЗРАЧНОЙ КЕРАМИКИ АЛЮМОИТТРИЕВОГО ГРАНАТА
BALABANOV STANISLAV SERGEEVICH (Autor:in) / GAVRISHCHUK EVGENIJ MIKHAJLOVICH (Autor:in) / DROBOTENKO VIKTOR VASILEVICH (Autor:in) / PALASHOV OLEG VALENTINOVICH (Autor:in) / PERMIN DMITRIJ ALEKSEEVICH (Autor:in) / ROSTOKINA ELENA EVGENEVNA (Autor:in)
20.05.2016
Patent
Elektronische Ressource
Russisch
Method for preparing yttrium aluminium garnet transparent ceramic
| Europäisches Patentamt | 2015
METHOD FOR PRODUCING ALLOYED YTTRIUM ALUMINIUM GARNET
| Europäisches Patentamt | 2017
METHOD FOR PRODUCING A NANOPOWDER OF YTTRIUM ALUMINIUM GARNET
| Europäisches Patentamt | 2021
Preparation method of fine-grain transparent yttrium aluminum garnet-based ceramic material
| Europäisches Patentamt | 2024
METHOD FOR PRODUCING PARAMAGNETIC GARNET-TYPE TRANSPARENT CERAMIC
| Europäisches Patentamt | 2023