METHOD FOR OBTAINING A WEAR-RESISTANT COMPOSITE MATERIAL BASED ON SILICON CARBIDE
FIELD: composite materials.SUBSTANCE: invention relates to the field of obtaining superhard composite materials and can be used in the manufacture of abrasive tools. For the manufacture of a workpiece with a diamond-containing phase, a diamond-lonsdaleite abrasive in the amount of 30-50, wt. %, is used as a diamond-containing phase with a particle size of 30-250 mcm, and to obtain a silicon carbide base, a mixture of green silicon carbide powders with a particle size of 5-9, 26-30, 38-42 mcm in the ratio (0.5-1.5) : (6-8) : (11-13). Then the workpiece is heat-treated and impregnated with silicon melt at 1550 ± 50°C for 1 hour in the backfill of crushed silicon wafers.EFFECT: resulting wear-resistant composite material based on silicon carbide is characterized by a Young’s modulus of 520-620 GPa, wear resistance of 47-58.5⋅10-15and the thickness of the graphitized layer on the particles of the diamond-containing component of 12-15 mcm.1 cl, 1 tbl, 7 ex
Изобретение относится к области получения сверхтвердых композиционных материалов и может быть использовано при изготовлении абразивного инструмента. Для изготовления заготовки с алмазосодержащей фазой в качестве алмазосодержащей фазы используют алмаз-лонсдейлитовый абразив в количестве 30-50 мас. % с размером частиц 30-250 мкм, а для получения основы карбида кремния - смесь порошков карбида кремния зеленого с размером частиц 5-9, 26-30, 38-42 мкм в соотношении (0,5-1,5) : (6-8) : (11-13). Затем заготовку термообрабатывают и пропитывают расплавом кремния при 1550±50оС в течение 1 ч в засыпке измельчённых кремниевых пластин. Полученный износостойкий композиционный материал на основе карбида кремния характеризуется модулем Юнга 520-620 ГПа, износостойкостью - 47-58,5⋅10-15м3и толщиной графитированного слоя на частицах алмазосодержащей составляющей 12-15 мкм. 1 табл., 7 пр.
METHOD FOR OBTAINING A WEAR-RESISTANT COMPOSITE MATERIAL BASED ON SILICON CARBIDE
FIELD: composite materials.SUBSTANCE: invention relates to the field of obtaining superhard composite materials and can be used in the manufacture of abrasive tools. For the manufacture of a workpiece with a diamond-containing phase, a diamond-lonsdaleite abrasive in the amount of 30-50, wt. %, is used as a diamond-containing phase with a particle size of 30-250 mcm, and to obtain a silicon carbide base, a mixture of green silicon carbide powders with a particle size of 5-9, 26-30, 38-42 mcm in the ratio (0.5-1.5) : (6-8) : (11-13). Then the workpiece is heat-treated and impregnated with silicon melt at 1550 ± 50°C for 1 hour in the backfill of crushed silicon wafers.EFFECT: resulting wear-resistant composite material based on silicon carbide is characterized by a Young’s modulus of 520-620 GPa, wear resistance of 47-58.5⋅10-15and the thickness of the graphitized layer on the particles of the diamond-containing component of 12-15 mcm.1 cl, 1 tbl, 7 ex
Изобретение относится к области получения сверхтвердых композиционных материалов и может быть использовано при изготовлении абразивного инструмента. Для изготовления заготовки с алмазосодержащей фазой в качестве алмазосодержащей фазы используют алмаз-лонсдейлитовый абразив в количестве 30-50 мас. % с размером частиц 30-250 мкм, а для получения основы карбида кремния - смесь порошков карбида кремния зеленого с размером частиц 5-9, 26-30, 38-42 мкм в соотношении (0,5-1,5) : (6-8) : (11-13). Затем заготовку термообрабатывают и пропитывают расплавом кремния при 1550±50оС в течение 1 ч в засыпке измельчённых кремниевых пластин. Полученный износостойкий композиционный материал на основе карбида кремния характеризуется модулем Юнга 520-620 ГПа, износостойкостью - 47-58,5⋅10-15м3и толщиной графитированного слоя на частицах алмазосодержащей составляющей 12-15 мкм. 1 табл., 7 пр.
METHOD FOR OBTAINING A WEAR-RESISTANT COMPOSITE MATERIAL BASED ON SILICON CARBIDE
СПОСОБ ПОЛУЧЕНИЯ ИЗНОСОСТОЙКОГО КОМПОЗИЦИОННОГО МАТЕРИАЛА НА ОСНОВЕ КАРБИДА КРЕМНИЯ
DYACHKOVA LARISA NIKOLAEVNA (Autor:in) / VITYAZ PETR ALEKSANDROVICH (Autor:in) / OSIPOV VLADIMIR ANATOLEVICH (Autor:in) / ILYUSHCHENKO ALEKSANDR FEDOROVICH (Autor:in)
18.11.2021
Patent
Elektronische Ressource
Russisch
| Europäisches Patentamt | 2024
Fire-resistant and wear-resistant silicon carbide material with microporous structure
| Europäisches Patentamt | 2020
Wear-resistant silicon carbide ceramic-based compound material and preparation method thereof
| Europäisches Patentamt | 2015