PREPARATION METHOD FOR ALKALINE SOLUTION-TREATED CERAMSITE LIGHT CONCRETE BLOCK
A preparation method for an alkaline solution-treated ceramsite light concrete block, comprising the following preparation raw materials in percentage by weight: 21-31% of cement, 10-17% of water, 0-8% of ceramsite, 7-35% of coarse aggregate, and 35-37% of fine aggregate. Before mixing, the ceramsite is soaked in a sodium hydroxide or calcium hydroxide alkaline solution for 8-12 hours at normal temperature to etch the surface of the ceramsite, so that the surface is roughened, the adhesion between the ceramsite and mortar is increased, and the strength of the ceramsite concrete block is improved. The prepared ceramsite concrete block has the advantages such as low apparent density, high strength, and excellent thermal insulation performance.
L'invention concerne un procédé de préparation d'un bloc de béton léger de céramsite traité en solution alcaline, comprenant les matières premières de préparation suivantes, en pourcentage en poids : de 21à 31 % de ciment, de 10 à 17 % d'eau, de 0 à 8 % de céramsite, de 7 à 35 % d'agrégat grossier, et de 35 à 37 % d'agrégat fin. Avant mélange, le céramsite est immergé dans une solution alcaline d'hydroxyde de sodium ou d'hydroxyde de calcium pendant 8 à 12 heures à une température normale pour graver la surface du céramsite, de sorte que la surface est rugueuse, l'adhérence entre le céramsite et le mortier est accrue, et la résistance du bloc de béton de céramsite est améliorée. Le bloc de béton de céramsite préparé présente les avantages d'une faible densité apparente, d'une résistance élevée et d'excellentes performances d'isolation thermique.
一种碱液处理陶粒轻型混凝土砌块的制备方法，其制备原料包括以下重量百分比组分：21-31％水泥、10-17％水、0-8％陶粒、7-35％粗骨料、35-37％细骨料。在拌合之前，将陶粒在氢氧化钠或氢氧化钙碱溶液常温下浸泡8-12小时来刻蚀陶粒表面，将表面粗糙化，增大陶粒与砂浆的粘结，从而提高陶粒混凝土砌块的强度。所制备的陶粒混凝土砌块具有表观密度轻、强度高、保温隔热性能优异等优点。
PREPARATION METHOD FOR ALKALINE SOLUTION-TREATED CERAMSITE LIGHT CONCRETE BLOCK
A preparation method for an alkaline solution-treated ceramsite light concrete block, comprising the following preparation raw materials in percentage by weight: 21-31% of cement, 10-17% of water, 0-8% of ceramsite, 7-35% of coarse aggregate, and 35-37% of fine aggregate. Before mixing, the ceramsite is soaked in a sodium hydroxide or calcium hydroxide alkaline solution for 8-12 hours at normal temperature to etch the surface of the ceramsite, so that the surface is roughened, the adhesion between the ceramsite and mortar is increased, and the strength of the ceramsite concrete block is improved. The prepared ceramsite concrete block has the advantages such as low apparent density, high strength, and excellent thermal insulation performance.
L'invention concerne un procédé de préparation d'un bloc de béton léger de céramsite traité en solution alcaline, comprenant les matières premières de préparation suivantes, en pourcentage en poids : de 21à 31 % de ciment, de 10 à 17 % d'eau, de 0 à 8 % de céramsite, de 7 à 35 % d'agrégat grossier, et de 35 à 37 % d'agrégat fin. Avant mélange, le céramsite est immergé dans une solution alcaline d'hydroxyde de sodium ou d'hydroxyde de calcium pendant 8 à 12 heures à une température normale pour graver la surface du céramsite, de sorte que la surface est rugueuse, l'adhérence entre le céramsite et le mortier est accrue, et la résistance du bloc de béton de céramsite est améliorée. Le bloc de béton de céramsite préparé présente les avantages d'une faible densité apparente, d'une résistance élevée et d'excellentes performances d'isolation thermique.
一种碱液处理陶粒轻型混凝土砌块的制备方法，其制备原料包括以下重量百分比组分：21-31％水泥、10-17％水、0-8％陶粒、7-35％粗骨料、35-37％细骨料。在拌合之前，将陶粒在氢氧化钠或氢氧化钙碱溶液常温下浸泡8-12小时来刻蚀陶粒表面，将表面粗糙化，增大陶粒与砂浆的粘结，从而提高陶粒混凝土砌块的强度。所制备的陶粒混凝土砌块具有表观密度轻、强度高、保温隔热性能优异等优点。
PREPARATION METHOD FOR ALKALINE SOLUTION-TREATED CERAMSITE LIGHT CONCRETE BLOCK
PROCÉDÉ DE PRÉPARATION D'UN BLOC DE BÉTON LÉGER DE CÉRAMSITE TRAITÉ EN SOLUTION ALCALINE
一种碱液处理陶粒轻型混凝土砌块的制备方法
WANG SHIJUN (Autor:in) / FAN XUEFENG (Autor:in) / FU BINGBIN (Autor:in) / SONG JUN (Autor:in) / YANG DEZHOU (Autor:in) / ZHANG HAIPING (Autor:in) / PING CHANG (Autor:in) / FANG YUZHANG (Autor:in) / AN NING (Autor:in) / MA YANHONG (Autor:in)
05.05.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Preparation method of alkali liquor-treated ceramsite light concrete block
| Europäisches Patentamt | 2021
Preparation method of alkali-solution-treated ceramsite lightweight concrete building block
| Europäisches Patentamt | 2021
Ceramsite Foam Concrete Insulation Block
| Trans Tech Publications | 2015
Surface-treated ceramsite for concrete and preparation method thereof
| Europäisches Patentamt | 2022