Failure Investigation of a Cage Suspension Gear Chain used in Coal Mines
Abstract This investigation is primarily aimed to examine the probable causes of in-service failure of cage suspension gear chain used in coal mines. Preliminary visual examination, dimensional measurement, chemical analysis, magnetic particle inspection and estimation of mechanical properties are necessary supplement to this investigation. Optical microscopic analysis along with scanning electron microscopy examinations are carried out to understand the metallurgical reasons for failure. The visual examination and magnetic particle investigations reveal presence of fissure cracks at weld joint for both un-failed and failed end link chain. The average hardness value has been found to increase gradually with the distance from the weld interface. The macro and microstructural examinations of the samples prepared from both failed and un-failed specimens depict presence of continuous as well as aligned linear inclusions randomly distributed along with decarburized layer at weld interface/fusion zone. Fractographic examination shows flat fracture covering major portion of cross-section, which is surrounded by a narrow annular metallic fracture surface having a texture different from that of the remaining surface. Fracture mechanics principles have been used to study the fatigue crack growth rate in both weld region and base region of the un-failed gear chain material. Detailed stress analyses are also carried out to evaluate the stress generated along the chain periphery. Finally, it is concluded that presence of serious weld defect due to use of improper welding parameters/procedure caused failure of the end links of the investigated chain link.
Failure Investigation of a Cage Suspension Gear Chain used in Coal Mines
Abstract This investigation is primarily aimed to examine the probable causes of in-service failure of cage suspension gear chain used in coal mines. Preliminary visual examination, dimensional measurement, chemical analysis, magnetic particle inspection and estimation of mechanical properties are necessary supplement to this investigation. Optical microscopic analysis along with scanning electron microscopy examinations are carried out to understand the metallurgical reasons for failure. The visual examination and magnetic particle investigations reveal presence of fissure cracks at weld joint for both un-failed and failed end link chain. The average hardness value has been found to increase gradually with the distance from the weld interface. The macro and microstructural examinations of the samples prepared from both failed and un-failed specimens depict presence of continuous as well as aligned linear inclusions randomly distributed along with decarburized layer at weld interface/fusion zone. Fractographic examination shows flat fracture covering major portion of cross-section, which is surrounded by a narrow annular metallic fracture surface having a texture different from that of the remaining surface. Fracture mechanics principles have been used to study the fatigue crack growth rate in both weld region and base region of the un-failed gear chain material. Detailed stress analyses are also carried out to evaluate the stress generated along the chain periphery. Finally, it is concluded that presence of serious weld defect due to use of improper welding parameters/procedure caused failure of the end links of the investigated chain link.
Failure Investigation of a Cage Suspension Gear Chain used in Coal Mines
Ghosh, Debashis (Autor:in) / Dutta, Shamik (Autor:in) / Shukla, Awdhesh Kumar (Autor:in) / Roy, Himadri (Autor:in)
Journal of The Institution of Engineers (India): Series D ; 97 ; 255-262
09.09.2015
8 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Investigation of the Failure of Roofs in Coal Mines
| NTIS | 1973
Ground Failure Investigation Over Abandoned Coal Mines: A Case Study
| British Library Conference Proceedings | 1988
WELDING EQUIPMENT USED FOR WELDING REINFORCEMENT CAGE FOR SUSPENSION BRIDGE
| Europäisches Patentamt | 2019
Resume of roof support methods used in coal mines
| Engineering Index Backfile | 1963