Characteristics of steel slag under different cooling conditions
Four types of steel slags, a ladle slag, a BOF (basic oxygen furnace) slag and two different EAF (electric arc furnace) slags, were characterized and modified by semi-rapid cooling in crucibles and rapid cooling by water granulation. The aim of this work was to investigate the effect of different cooling conditions on the properties of glassy slags with respect to their leaching and volume stability. Optical microscopy, X-ray diffraction, scanning electron microscope and a standard test leaching (prEN 12457-2/3) have been used for the investigation. The results show that the disintegrated ladle slag was made volume stable by water granulation, which consisted of 98 % glass. However EAF slag 1, EAF slag 2 and the BOF slag formed 17 %, 1 % and 1 % glass, respectively. The leaching test showed that the glass-containing matrix did not prevent leaching of minor elements from the modified slags. The solubility of chromium, molybdenum and vanadium varied in the different modifications, probably due to their presence in different minerals and their different distributions.
Characteristics of steel slag under different cooling conditions
Four types of steel slags, a ladle slag, a BOF (basic oxygen furnace) slag and two different EAF (electric arc furnace) slags, were characterized and modified by semi-rapid cooling in crucibles and rapid cooling by water granulation. The aim of this work was to investigate the effect of different cooling conditions on the properties of glassy slags with respect to their leaching and volume stability. Optical microscopy, X-ray diffraction, scanning electron microscope and a standard test leaching (prEN 12457-2/3) have been used for the investigation. The results show that the disintegrated ladle slag was made volume stable by water granulation, which consisted of 98 % glass. However EAF slag 1, EAF slag 2 and the BOF slag formed 17 %, 1 % and 1 % glass, respectively. The leaching test showed that the glass-containing matrix did not prevent leaching of minor elements from the modified slags. The solubility of chromium, molybdenum and vanadium varied in the different modifications, probably due to their presence in different minerals and their different distributions.
Characteristics of steel slag under different cooling conditions
Die Charakterisierung von Schlacken aus der Stahlherstellung unter verschiedenen Abkühlungsbedingungen
Tossavainen, M. (Autor:in) / Engstrom, F. (Autor:in) / Yang, Q. (Autor:in) / Menad, N. (Autor:in) / Lidstrom Larsson, M. (Autor:in) / Bjorkman, B. (Autor:in)
Waste Management ; 27 ; 1335-1344
2007
10 Seiten, 8 Bilder, 3 Tabellen, 19 Quellen
Aufsatz (Zeitschrift)
Englisch
Hydration Properties of Steel Slag under Different Curing Temperatures
| British Library Conference Proceedings | 2014
| Engineering Index Backfile | 1968
STEEL SLAG GRAIN, STEEL SLAG, AND METHOD FOR PRODUCING STEEL SLAG GRAIN
| Europäisches Patentamt | 2016