Effect of Sb addition on the tensile deformation behavior of lead-free Sn–3.5Ag solder alloy
Highlights ► Addition of 1.5% Sb to the Sn–3.5Ag alloy improved both strength and ductility. ► The enhanced strength was due to the solid solution hardening of Sb in Sn matrix. ► The improved ductility was due to higher SRS caused by structural refinement. ► The strength decreased and the ductility increased with increasing test temperature. ► The effect of temperature and strain rate was more pronounced for Sn–Ag–Sb.
Abstract Tensile deformation behavior of Sn–3.5Ag and Sn–3.5Ag–1.5Sb alloys was investigated at temperatures ranging from 298 to 400K, and strain rates ranging from 5×10−4 to 1×10−2 s−1. After melting and casting, the samples were rolled to sheets, from which tensile specimens were punched and pulled to fracture in uniaxial tension tests. Scanning electron microscopy (SEM) was used to study the microstructure and fracture surface of the samples. Addition of 1.5% Sb into the binary alloy resulted in an increase in both ultimate tensile strength (UTS) and ductility. The enhanced strength was attributed to the solid solution hardening effects of Sb in the Sn matrix. The improved ductility was, however, caused by the structural refinement which results in the higher strain rate hardening of the Sb-containing alloy. This was manifested by the higher strain rate sensitivity (SRS) indices (m) of 0.14–0.27, as compared to 0.11–0.20 found for the Sn–3.5Ag alloy.
Effect of Sb addition on the tensile deformation behavior of lead-free Sn–3.5Ag solder alloy
Highlights ► Addition of 1.5% Sb to the Sn–3.5Ag alloy improved both strength and ductility. ► The enhanced strength was due to the solid solution hardening of Sb in Sn matrix. ► The improved ductility was due to higher SRS caused by structural refinement. ► The strength decreased and the ductility increased with increasing test temperature. ► The effect of temperature and strain rate was more pronounced for Sn–Ag–Sb.
Abstract Tensile deformation behavior of Sn–3.5Ag and Sn–3.5Ag–1.5Sb alloys was investigated at temperatures ranging from 298 to 400K, and strain rates ranging from 5×10−4 to 1×10−2 s−1. After melting and casting, the samples were rolled to sheets, from which tensile specimens were punched and pulled to fracture in uniaxial tension tests. Scanning electron microscopy (SEM) was used to study the microstructure and fracture surface of the samples. Addition of 1.5% Sb into the binary alloy resulted in an increase in both ultimate tensile strength (UTS) and ductility. The enhanced strength was attributed to the solid solution hardening effects of Sb in the Sn matrix. The improved ductility was, however, caused by the structural refinement which results in the higher strain rate hardening of the Sb-containing alloy. This was manifested by the higher strain rate sensitivity (SRS) indices (m) of 0.14–0.27, as compared to 0.11–0.20 found for the Sn–3.5Ag alloy.
Effect of Sb addition on the tensile deformation behavior of lead-free Sn–3.5Ag solder alloy
Mahmudi, R. (author) / Mahin-Shirazi, S. (author)
2011-05-29
6 pages
Article (Journal)
Electronic Resource
English
Effect of Sb addition on the tensile deformation behavior of lead-free Sn-3.5Ag solder alloy
| British Library Online Contents | 2011
Fatigue crack growth behavior of 96.5Sn-3.5Ag lead-free solder
| British Library Online Contents | 2001
Tensile Properties of Sn-3.5Ag and Sn-3.5Ag-0.75Cu Lead-free Solders
| British Library Online Contents | 2002
Indentation creep of lead-free Sn–3.5Ag solder alloy: Effects of cooling rate and Zn/Sb addition
| British Library Online Contents | 2013
| British Library Online Contents | 2009