Influence of naphthalene sulphonated and polycarboxylate acid-based superplasticizer on the mechanical properties and hydration behavior of ternary binder: A comparative study
Highlights The effects of BNS and PCS on the performance of OPC-CAC-C S binder were comparative studied. The compressive strength of ternary binder was little affected by BNS, but reduced by PCS. The size of ettringite crystals was decreased due to the adsorption of PCS.
Abstract The effect of two superplasticizers, naphthalene sulphonatedsuperplasticizer (BNS) and polycarboxylate acid-based (PCS), on the setting time, fluidity and compressive strength of ordinary Portland cement - calcium aluminate cement - gypsum (OPC-CAC-CSH) ternary binder and C3A-C3S-CSH system was studied. In order to explore the influence of BNS and PCS on the ternary binder, the hydration products and microstructure were analyzed by XRD, TG and SEM. Results show that the effect of BNS on the fluidity of OPC-CAC-CSH was better than PCS. BNS prolonged the setting time of OPC-CAC-CSH, but PCS had little effect on it. The compressive strength of OPC-CAC-CSH was slightly promoted with the increase of BNS content, while that was gradually reduced with the increase of PCS content. Moreover, the morphology and size of ettringite crystals were changed after adding PCS.
Influence of naphthalene sulphonated and polycarboxylate acid-based superplasticizer on the mechanical properties and hydration behavior of ternary binder: A comparative study
Highlights The effects of BNS and PCS on the performance of OPC-CAC-C S binder were comparative studied. The compressive strength of ternary binder was little affected by BNS, but reduced by PCS. The size of ettringite crystals was decreased due to the adsorption of PCS.
Abstract The effect of two superplasticizers, naphthalene sulphonatedsuperplasticizer (BNS) and polycarboxylate acid-based (PCS), on the setting time, fluidity and compressive strength of ordinary Portland cement - calcium aluminate cement - gypsum (OPC-CAC-CSH) ternary binder and C3A-C3S-CSH system was studied. In order to explore the influence of BNS and PCS on the ternary binder, the hydration products and microstructure were analyzed by XRD, TG and SEM. Results show that the effect of BNS on the fluidity of OPC-CAC-CSH was better than PCS. BNS prolonged the setting time of OPC-CAC-CSH, but PCS had little effect on it. The compressive strength of OPC-CAC-CSH was slightly promoted with the increase of BNS content, while that was gradually reduced with the increase of PCS content. Moreover, the morphology and size of ettringite crystals were changed after adding PCS.
Influence of naphthalene sulphonated and polycarboxylate acid-based superplasticizer on the mechanical properties and hydration behavior of ternary binder: A comparative study
Niu, Mengdie (author) / Li, Guoxin (author) / Li, Qiqi (author) / Zhang, Ge (author)
2021-10-22
Article (Journal)
Electronic Resource
English
Influence of Polycarboxylate Superplasticizer on Cement Hydration Products
| British Library Conference Proceedings | 2014
Influence of Polycarboxylate Superplasticizer on Cement Hydration Products
| Trans Tech Publications | 2014
| European Patent Office | 2021