Preparation method of building engineering waste mud curing agent
The invention relates to a preparation method of a construction engineering waste mud curing agent. The construction engineering waste mud curing agent comprises the following components in parts by weight: 3-4 parts of mineral powder and 1-2 parts of P.O42.5 ordinary Portland cement. The preparation method comprises the following steps: fully stirring and mixing 3-4 parts of mineral powder and 1-2 parts of P.O42.5 ordinary Portland cement in a stirring barrel, then pouring the mixture into a stirring tank, meanwhile, pouring recycled waste slurry and soil crushed by a soil crushing device into the stirring tank, and fully stirring in the stirring tank to obtain a mixture; the construction engineering waste mud curing agent can be prepared. Compared with other curing agents, the building engineering waste mud curing agent prepared by the preparation method has the characteristics of simple raw materials, low cost, simple proportioning, simple operation and wide application range.
本发明涉及一种建筑工程废弃泥浆固化剂的制备方法，所述建筑工程废弃泥浆固化剂包括以下重量份的组分：3～4份矿粉、1～2份P.O42.5普通硅酸盐水泥；制备方法包括以下步骤：将3～4份矿粉以及1～2份P.O42.5普通硅酸盐水泥在搅拌桶中进行充分搅拌混合，然后倒入拌和池，同时向搅拌池内倒入回收的废弃泥浆以及通过土体粉碎装置粉碎的土，通过拌和池进行充分搅拌，即可制备得到建筑工程废弃泥浆固化剂。该制备方法制备得到的建筑工程废弃泥浆固化剂相较于其它固化剂，具有原料简单、成本低廉、配比简单、操作简单且应用面广的特点。
Preparation method of building engineering waste mud curing agent
The invention relates to a preparation method of a construction engineering waste mud curing agent. The construction engineering waste mud curing agent comprises the following components in parts by weight: 3-4 parts of mineral powder and 1-2 parts of P.O42.5 ordinary Portland cement. The preparation method comprises the following steps: fully stirring and mixing 3-4 parts of mineral powder and 1-2 parts of P.O42.5 ordinary Portland cement in a stirring barrel, then pouring the mixture into a stirring tank, meanwhile, pouring recycled waste slurry and soil crushed by a soil crushing device into the stirring tank, and fully stirring in the stirring tank to obtain a mixture; the construction engineering waste mud curing agent can be prepared. Compared with other curing agents, the building engineering waste mud curing agent prepared by the preparation method has the characteristics of simple raw materials, low cost, simple proportioning, simple operation and wide application range.
本发明涉及一种建筑工程废弃泥浆固化剂的制备方法，所述建筑工程废弃泥浆固化剂包括以下重量份的组分：3～4份矿粉、1～2份P.O42.5普通硅酸盐水泥；制备方法包括以下步骤：将3～4份矿粉以及1～2份P.O42.5普通硅酸盐水泥在搅拌桶中进行充分搅拌混合，然后倒入拌和池，同时向搅拌池内倒入回收的废弃泥浆以及通过土体粉碎装置粉碎的土，通过拌和池进行充分搅拌，即可制备得到建筑工程废弃泥浆固化剂。该制备方法制备得到的建筑工程废弃泥浆固化剂相较于其它固化剂，具有原料简单、成本低廉、配比简单、操作简单且应用面广的特点。
Preparation method of building engineering waste mud curing agent
一种建筑工程废弃泥浆固化剂的制备方法
ZHOU YANG (author) / WU XIAOQIANG (author) / ZHOU MING (author)
2023-06-30
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2024
| European Patent Office | 2023
Curing agent and curing method for phosphogypsum waste residues
| European Patent Office | 2020
| European Patent Office | 2024