Nickel-iron slag-based shield tunnel backfill grouting material and preparation method thereof
The invention relates to a nickel-iron slag-based shield tunnel wall post-grouting material which comprises the following components in parts by mass: 30-50 parts of blast furnace nickel-iron slag, 20-50 parts of fly ash, 5-20 parts of boric sludge, 0.5-3 parts of an activating agent, 5-20 parts of a blender, 80-110 parts of an exciting agent solution, 100-150 parts of recycled fine aggregate and 3-5 parts of an additive, and the water-binder ratio of the nickel-iron slag-based shield tunnel wall post-grouting material is 0.45-0.8. The preparation method comprises the following steps: weighing the materials in parts by weight; preparing blast furnace ferronickel slag powder; manufacturing recycled fine aggregate sand; preparing an exciting agent solution; making gel material neat paste; and adding the recycled fine aggregate, a blender and an additive to obtain the nickel-iron slag-based shield tunnel backfill grouting material. The cement single-liquid grouting material is low in energy consumption, energy-saving, environment-friendly, low in production cost and high in production efficiency, has the characteristics of high strength, good coagulability, good fluidity and the like, can replace a traditional cement single-liquid grouting material, can effectively reduce the use of Portland cement, and is beneficial to reutilization of solid waste resources.
本发明涉及一种镍铁渣基盾构隧道壁后注浆材料,按质量份数计,组分如下:高炉镍铁渣30~50份,粉煤灰20~50份,硼泥5~20份,活化剂0.5~3份,调和剂5~20份,激发剂溶液80~110份,再生细骨料100~150份,外加剂3~5份,镍铁渣基盾构隧道壁后注浆材料的水胶比为0.45~0.8。制备方法:按照重量份数称取材料;制作高炉镍铁渣粉;制作再生细骨料砂;制作激发剂溶液;制作胶凝材料净浆;加入再生细骨料、调和剂、外加剂得到镍铁渣基盾构隧道壁后注浆材料。本发明低耗能、节能环保、生产成本低、生产效率高,同时具有强度高、凝结性好、流动性好等特点,可替代传统水泥单液注浆材料,可有效减少硅酸盐水泥的使用,有利于固废资源再利用。
Nickel-iron slag-based shield tunnel backfill grouting material and preparation method thereof
The invention relates to a nickel-iron slag-based shield tunnel wall post-grouting material which comprises the following components in parts by mass: 30-50 parts of blast furnace nickel-iron slag, 20-50 parts of fly ash, 5-20 parts of boric sludge, 0.5-3 parts of an activating agent, 5-20 parts of a blender, 80-110 parts of an exciting agent solution, 100-150 parts of recycled fine aggregate and 3-5 parts of an additive, and the water-binder ratio of the nickel-iron slag-based shield tunnel wall post-grouting material is 0.45-0.8. The preparation method comprises the following steps: weighing the materials in parts by weight; preparing blast furnace ferronickel slag powder; manufacturing recycled fine aggregate sand; preparing an exciting agent solution; making gel material neat paste; and adding the recycled fine aggregate, a blender and an additive to obtain the nickel-iron slag-based shield tunnel backfill grouting material. The cement single-liquid grouting material is low in energy consumption, energy-saving, environment-friendly, low in production cost and high in production efficiency, has the characteristics of high strength, good coagulability, good fluidity and the like, can replace a traditional cement single-liquid grouting material, can effectively reduce the use of Portland cement, and is beneficial to reutilization of solid waste resources.
本发明涉及一种镍铁渣基盾构隧道壁后注浆材料,按质量份数计,组分如下:高炉镍铁渣30~50份,粉煤灰20~50份,硼泥5~20份,活化剂0.5~3份,调和剂5~20份,激发剂溶液80~110份,再生细骨料100~150份,外加剂3~5份,镍铁渣基盾构隧道壁后注浆材料的水胶比为0.45~0.8。制备方法:按照重量份数称取材料;制作高炉镍铁渣粉;制作再生细骨料砂;制作激发剂溶液;制作胶凝材料净浆;加入再生细骨料、调和剂、外加剂得到镍铁渣基盾构隧道壁后注浆材料。本发明低耗能、节能环保、生产成本低、生产效率高,同时具有强度高、凝结性好、流动性好等特点,可替代传统水泥单液注浆材料,可有效减少硅酸盐水泥的使用,有利于固废资源再利用。
Nickel-iron slag-based shield tunnel backfill grouting material and preparation method thereof
一种镍铁渣基盾构隧道壁后注浆材料及其制备方法
LIU JIANPING (author) / SONG GE (author) / GE XIAOWEI (author) / LIU KAIXIN (author) / TIAN YULIN (author) / LIU BING (author) / WANG YING (author) / XU XIAOCHUAN (author) / YU JINGMIN (author)
2024-05-07
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Slag-based shield tunnel backfill grouting material and preparation method thereof
European Patent Office | 2024
|European Patent Office | 2024
|Shield tunnel timed condensation backfill grouting material formula and grouting process
European Patent Office | 2022
|Shield backfill grouting slurry and preparation method thereof
European Patent Office | 2024
|Shield backfill grouting slurry and preparation method thereof
European Patent Office | 2021
|