MANUFACTURING METHOD OF POROUS CONCRETE
PROBLEM TO BE SOLVED: To provide a manufacturing method of porous concrete capable of efficiently being manufactured by using concrete debris.SOLUTION: At first concrete debris having particle size of 60 mm or less is generated by pulverizing the concrete debris (Step S1). Next, the concrete debris having particle size of 60 mm or less is mixed with cement, an admixture and water by using a mixer (Step S2). High early strength Portland cement is used as the cement of mortar, tap water is used as the water and polycarboxylic acid ether-based high performance AE water-reducing agent is used as the admixture. The high performance AE water-reducing agent is used at c (weight of cement)×0.7%. Then fresh concrete obtained by mixing is compacted (Step S3).SELECTED DRAWING: Figure 1
【課題】コンクリートガラを用いて効率よく製造することができる多孔質コンクリートの製造方法を提供する。【解決手段】まず、コンクリートガラを粉砕して粒度６０ｍｍ以下のコンクリートガラを生成する（ステップＳ１）。次に、粒度６０ｍｍ以下のコンクリートガラを、セメントと混和材料と水と、混練機を用いて混練する（ステップＳ２）。ここで、モルタルのセメントとして早強ポルトランドセメントを用い、水として水道水を用い、混和材料として、ポリカルボン酸エーテル系の高性能ＡＥ減水剤を用いる。ここで、高性能ＡＥ減水剤は、ｃ（セメントの重量）×０．７％で用いる。次に、混練して得たフレッシュコンクリートを締固める（ステップＳ３）。【選択図】図１
MANUFACTURING METHOD OF POROUS CONCRETE
PROBLEM TO BE SOLVED: To provide a manufacturing method of porous concrete capable of efficiently being manufactured by using concrete debris.SOLUTION: At first concrete debris having particle size of 60 mm or less is generated by pulverizing the concrete debris (Step S1). Next, the concrete debris having particle size of 60 mm or less is mixed with cement, an admixture and water by using a mixer (Step S2). High early strength Portland cement is used as the cement of mortar, tap water is used as the water and polycarboxylic acid ether-based high performance AE water-reducing agent is used as the admixture. The high performance AE water-reducing agent is used at c (weight of cement)×0.7%. Then fresh concrete obtained by mixing is compacted (Step S3).SELECTED DRAWING: Figure 1
【課題】コンクリートガラを用いて効率よく製造することができる多孔質コンクリートの製造方法を提供する。【解決手段】まず、コンクリートガラを粉砕して粒度６０ｍｍ以下のコンクリートガラを生成する（ステップＳ１）。次に、粒度６０ｍｍ以下のコンクリートガラを、セメントと混和材料と水と、混練機を用いて混練する（ステップＳ２）。ここで、モルタルのセメントとして早強ポルトランドセメントを用い、水として水道水を用い、混和材料として、ポリカルボン酸エーテル系の高性能ＡＥ減水剤を用いる。ここで、高性能ＡＥ減水剤は、ｃ（セメントの重量）×０．７％で用いる。次に、混練して得たフレッシュコンクリートを締固める（ステップＳ３）。【選択図】図１
MANUFACTURING METHOD OF POROUS CONCRETE
多孔質コンクリートの製造方法
SATO RITSU (author) / SAWADA MITSUNARI (author) / MIZUKAMI AKIRA (author) / ONAKA MASAHIDE (author)
2017-10-12
Patent
Electronic Resource
Japanese